Fiber reinforced composite material Grade-A fireproof heat-insulating board and production process thereof

A technology of fire-proof insulation board and composite materials, which is applied in the field of board processing, can solve the problems that cannot fully meet the integration of building fire-proof insulation, etc., and achieve the effects of eliminating fire hazards, long service life, and superior weather resistance

Inactive Publication Date: 2018-10-30
四川涵杰新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The A-class fireproof materials used in buildings such as rock wool, foamed cement, and foamed concrete have certain defects. With the development of the construction market, they will not be able to fully meet the requirements of building fireproofing and thermal insulation integration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber reinforced composite material Grade-A fireproof heat-insulating board and production process thereof
  • Fiber reinforced composite material Grade-A fireproof heat-insulating board and production process thereof
  • Fiber reinforced composite material Grade-A fireproof heat-insulating board and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A fiber-reinforced composite A-class fireproof insulation board is composed of the following materials in weight ratio per cubic meter,

[0029] Polystyrene particles 10kg / m 3 , cement 180kg / m 3 , polypropylene fiber 0.66kg / m 3 , plant fiber 0.66kg / m 3 , hydroxypropyl methylcellulose 1.3kg / m 3 , Recycled fine powder 13kg / m 3 , Recycling particles 5kg / m 3 And foaming agent 0.16kg / m 3 .

[0030] The invention also discloses a production process of fiber-reinforced composite material A-class fireproof insulation board, which includes the following steps:

[0031] Step 1. Lay plastic film on the support formwork, and the laid plastic film must be kept flat and free of holes and leaks;

[0032] Step 2. Lay glass fiber mesh cloth on the upper surface of the plastic film, and the laid glass fiber mesh cloth must be kept flat and uniform;

[0033] Step 3, mix polyphenylene particles, cement, polypropylene fiber, plant fiber, hydroxypropyl methylcellulose, recycled fine...

Embodiment 2

[0039] A fiber-reinforced composite A-class fireproof insulation board is composed of the following materials in weight ratio per cubic meter,

[0040] Polystyrene particles 10kg / m 3 , cement 180kg / m 3 , polypropylene fiber 0.66kg / m 3 , plant fiber 0.66kg / m 3 , hydroxypropyl methylcellulose 1.3kg / m 3 , Recycled fine powder 13kg / m 3 , Recycling particles 5kg / m 3 , foaming agent 0.16kg / m 3 And early strength agent 5kg / m 3 -6kg / m 3 .

[0041] The invention also discloses a production process of fiber-reinforced composite material A-class fireproof insulation board, which includes the following steps:

[0042] Step 1. Lay plastic film on the support formwork, and the laid plastic film must be kept flat and free of holes and leaks;

[0043] Step 2. Lay glass fiber mesh cloth on the upper surface of the plastic film, and the laid glass fiber mesh cloth must be kept flat and uniform;

[0044] Step 3, mix polyphenylene particles, cement, polypropylene fiber, plant fiber, hy...

Embodiment 3

[0050] A fiber-reinforced composite A-class fireproof insulation board is composed of the following materials in weight ratio per cubic meter,

[0051] Polystyrene particles 10kg / m 3 , cement 180kg / m 3 , polypropylene fiber 0.66kg / m 3 , plant fiber 0.66kg / m 3 , hydroxypropyl methylcellulose 1.3kg / m 3 , Recycled fine powder 13kg / m 3 , Recycling particles 5kg / m 3 , foaming agent 0.16kg / m 3 and retarder 5kg / m 3-6kg / m 3 .

[0052] The invention also discloses a production process of fiber-reinforced composite material A-class fireproof insulation board, which includes the following steps:

[0053] Step 1. Lay plastic film on the support formwork, and the laid plastic film must be kept flat and free of holes and leaks;

[0054] Step 2. Lay glass fiber mesh cloth on the upper surface of the plastic film, and the laid glass fiber mesh cloth must be kept flat and uniform;

[0055] Step 3, mix polyphenylene particles, cement, polypropylene fiber, plant fiber, hydroxypropyl m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fiber reinforced composite material Grade-A fireproof heat-insulating board which is composed of, by weight ratio per cubic meter, 10kg / m3 of polyphenyl granule, 180kg / m3 ofcement, 0.66kg / m3 of polypropylene fiber, 0.66kg / m3 of plant fiber, 1.3kg / m3 of hydroxypropyl methyl cellulose, 13kg / m3 of regenerated material fine powder, 5kg / m3 of regenerated material granule and0.16kg / m3 of foamer. The invention further discloses a production process of the fiber reinforced composite material Grade-A fireproof heat-insulating board.

Description

technical field [0001] The invention belongs to the field of plate processing, and in particular relates to a fiber-reinforced composite material A-level fireproof heat preservation board and a production process thereof. Background technique [0002] With the continuous development of the real estate industry, energy saving has gradually attracted the attention of enterprises and consumers. Improving the thermal insulation performance of building envelope is an important means to realize building energy saving, and improving the thermal insulation performance of building walls is an important part of improving the overall thermal insulation performance of building envelope. Due to the remarkable effect of external thermal insulation technology of external walls, it has gradually become the mainstream technology of external thermal insulation. [0003] To develop external thermal insulation technology, we should vigorously develop and popularize new external wall thermal in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/08C04B16/06C04B18/24B28B1/52B28B3/00B28B11/24B28B11/12C04B111/28
CPCB28B1/525B28B3/00B28B11/12B28B11/24C04B16/0633C04B18/24C04B28/00C04B38/08C04B2111/00612C04B2111/285C04B2201/10C04B2201/20C04B2201/32C04B2201/50C04B16/08C04B24/383C04B14/02C04B2103/42C04B38/0074C04B2103/12C04B2103/22Y02W30/91
Inventor 母敏王培志廖明均
Owner 四川涵杰新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com