Manufacturing method of ceramic brick briquettes

A manufacturing method and technology for ceramic tiles, which are applied in the field of manufacturing ceramic tile mud blanks, can solve the problems of poor wear resistance and poor three-dimensional effect of a printed decorative layer, and achieve strong three-dimensional effect, strong sense of layer transition, and good wear resistance. Effect

Inactive Publication Date: 2018-11-02
湖北兴荣陶瓷有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems that the printed decorative layer formed by conventional inkjet printing is not wear-resistant and has poor three-dimensional effect in the prior art, and proposes a ceramic brick mud and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]This embodiment provides a method for manufacturing a ceramic brick mud adobe and ceramic bricks manufactured using it.

[0035] A kind of manufacture method of ceramic brick adobe, it comprises the steps:

[0036] A, select known base material and lining for ceramic adobe, form adobe through positively punching cloth, the thickness of the lining layer in the body is 1.2mm, and dry the adobe;

[0037] B. Inkjet printing organic permeable color glaze ink on the dried brick adobe; the temperature of the adobe is 45-55°C during inkjet printing;

[0038] C. Inkjet printing organic penetration enhancer ink;

[0039] D. Place the adobe for more than 10 minutes, so that the organic penetration enhancer ink can fully play its role and form a certain depth of penetration enhancement layer (generally more than 0.3mm);

[0040] E. Secondary drying at a temperature of 50°C for 60 minutes to obtain a ceramic brick adobe.

[0041] The above process is described here, the placement ...

Embodiment 2

[0049] A kind of manufacture method of ceramic brick adobe, it comprises the steps:

[0050] A, select known base material and lining for ceramic tiles, and form bricks through positively punching cloth, and the thickness of the lining layer in the green body is 2mm, and the bricks are dried;

[0051] B. Inkjet printing organic permeable color glaze ink on the dried brick adobe; the temperature of the adobe is 45-55°C during inkjet printing;

[0052] C. Combined printing with screen and roller to apply organic penetration enhancer ink; the amount of organic penetration enhancer ink is 80±20 g / m2;

[0053] D. Place the adobe for 30 minutes to make the organic penetration enhancer ink fully play its role and form a certain depth of penetration enhancement layer;

[0054] E. Secondary drying at 120° C. for 20 minutes to obtain a ceramic brick adobe with a penetration layer depth of about 0.9 mm.

[0055] The ink used is the same as the system of Example 1.

[0056] In step A, ...

Embodiment 3

[0061] A kind of manufacture method of ceramic brick adobe, it comprises the steps:

[0062] A, select known base material and lining for ceramic adobe, form adobe through positively hitting the cloth, the thickness of the lining layer in the body is 0.8mm, and dry the adobe;

[0063] B. Inkjet printing organic permeable color glaze ink on the dried brick adobe; the temperature of the adobe is 45-55°C during inkjet printing;

[0064] C. Combined screen and roller printing to apply organic penetration enhancer ink; the amount of organic penetration enhancer ink is 50±10 g / m2;

[0065] D. Place the adobe for 15 minutes to make the organic penetration enhancer ink fully play its role and form a certain depth of penetration enhancement layer;

[0066] E. Secondary drying at 80° C. for 35 minutes to obtain a ceramic brick adobe with a penetration layer depth of about 0.8 mm. The thickness of the permeable layer is basically the same as the thickness of the fabric layer.

[0067]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A manufacturing method of ceramic brick briquettes includes following steps: A, selecting raw materials commonly used for ceramic bricks to make briquettes; B, applying organic permeable colored glazeink; C, applying organic permeation promoter ink; D, drying at 50-200 DEG C for 10-60min to obtain the ceramic brick briquettes. The ceramic brick briquettes are adopted to prepare ceramic bricks, apermeation layer formed by the permeable glaze ink has certain thickness, the permeable glaze ink permeates into a fabric layer to enable decorative patterns to be wear-resistant, and the problem thatprinted decorative layers formed by conventional ink-jet printing do not have three-dimensional layering sense and are not wear-resistant.

Description

technical field [0001] The invention relates to the technical field of manufacturing ceramic products, in particular to a method for manufacturing ceramic brick mud adobe. Background technique [0002] Ceramic inkjet printing technology is a technology widely used in the production of ceramic tiles in recent years. It prints ink on the surface of bricks through nozzles instead of traditional screen printing, roller printing and other decorative methods. Because it is a non-contact printing, It can "print" concave-convex products without physical plate making, simple and rapid plate transfer, personalized production can be realized, and the production repeatability is good, so the scope of use is getting wider and wider. But its disadvantage is that the printed decorative layer is too shallow. At the same time, the ink has poor wear resistance after firing. With the extension of use time, the decorative effect will be greatly reduced. The process of applying transparent glaz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/85
CPCC04B41/85C04B41/50C04B41/4543C04B41/4554
Inventor 张煜琳
Owner 湖北兴荣陶瓷有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com