Rubber nipple silica gel material and preparation method thereof

A technology of silicone and baby bottles, applied in the field of silicone products, can solve the problems of poor ventilation, no water, and small shrinkage.

Inactive Publication Date: 2018-11-16
长沙浩然医疗科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sucking part and venting part of the pacifier are the key points of the whole product. The flow rate of the sucking part and the air intake of the venting part will affect the normal use of the pacifier. If the flow rate is too high, the baby will not be able to swallow the milk, and its ventilating function Poor, the imbalance of air intake, air outlet and flow will make the internal air pressure of the bottle different from the external air pressure, which will easily cause the nipple to be flattened and unable to discharge water, or the baby will suffer from abdominal distension, abdominal pain, hiccups, and spit-up due to excessive air intake. Therefore, its use effect is not ideal
[0003] The Chinese patent document "A Silicone Baby Pacifier and Its Manufacturing Method (Patent No.: CN104672913A)" discloses a silicone baby pacifier and its manufacturing method and its preparation method. Oxane dimethyl silicone oil, hydroxyl silicone oil, dimethyl dimethoxysilane, fumed silica, zirconium phosphate and platinum catalyst, the invention can effectively prevent milk leakage and choking, safe and reliable, with high transparency, No whitening, good physical properties, small shrinkage, good elongation at break, high tensile strength and tear strength, but it has added metal elements such as chromium, and its physical properties and service life need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A silicone material for a feeding bottle nipple, in parts by weight, comprising the following raw materials: 250 parts of siloxane dimethyl silicone oil, 225 parts of hydroxyl silicone oil, 110 parts of dimethyldimethoxysilane, 35 parts of fumed silica, platinum 7.5 parts of catalyst, 30 parts of polylactic acid fiber, 15 parts of dissolving pulp, and 7.5 parts of casein.

[0025] The specific surface area of ​​the fumed silica is 350m 2 / g. The molecular weight of the polylactic acid fiber is 18000.

[0026] The preparation method of the above-mentioned silicone material for a feeding bottle nipple comprises the following steps: 1) Weighing each raw material according to the above parts by weight, adding siloxane dimethyl silicone oil, hydroxyl silicone oil, dimethyldimethoxysilane, Stir fumed silica, platinum catalyst, polylactic acid fiber, casein, and calcium-based bentonite for 3 hours until fully mixed, and heat mix at 160°C for 15 minutes to form a rubber compo...

Embodiment 2

[0028] A silicone material for a feeding bottle nipple, in parts by weight, comprising the following raw materials: 200 parts of siloxane dimethyl silicone oil, 250 parts of hydroxyl silicone oil, 100 parts of dimethyldimethoxysilane, 50 parts of fumed silica, platinum 5 parts of catalyst, 40 parts of polylactic acid fiber, 10 parts of dissolving pulp, and 10 parts of casein.

[0029] The specific surface area of ​​the fumed silica is 300m 2 / g. The molecular weight of the polylactic acid fiber is 20000.

[0030] The preparation method of the above-mentioned silicone material for a feeding bottle nipple comprises the following steps: 1) Weighing each raw material according to the above parts by weight, adding siloxane dimethyl silicone oil, hydroxyl silicone oil, dimethyldimethoxysilane, Fumed silica, platinum catalyst, polylactic acid fiber, casein, and calcium-based bentonite were stirred for 2 hours until fully mixed, and then hot-mixed at 170°C for 10 minutes to form a r...

Embodiment 3

[0032] A silicone material for a feeding bottle nipple, in parts by weight, comprising the following raw materials: 300 parts of siloxane dimethyl silicone oil, 200 parts of hydroxyl silicone oil, 120 parts of dimethyldimethoxysilane, 20 parts of fumed silica, platinum 10 parts of catalyst, 20 parts of polylactic acid fiber, 20 parts of dissolving pulp, 5 parts of casein.

[0033] The specific surface area of ​​the fumed silica is 400m 2 / g. The molecular weight of the polylactic acid fiber is 15000.

[0034] The preparation method of the above-mentioned silicone material for a feeding bottle nipple comprises the following steps: 1) Weighing each raw material according to the above parts by weight, adding siloxane dimethyl silicone oil, hydroxyl silicone oil, dimethyldimethoxysilane, Stir fumed silica, platinum catalyst, polylactic acid fiber, casein, and calcium-based bentonite for 4 hours until fully mixed, and heat mix at 150°C for 20 minutes to form a rubber compound; 2) M...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rubber nipple silica gel material and a preparation method thereof, which belong to the technical field of a silica gel material. The rubber nipple silica gel material comprises the following raw materials: siloxane dimethicone, hydroxyl silicone oil, dimethoxydimethylsilane, gas-phase white carbon black, a platinum catalyst, polylactic acid fiber, casein, and ca bentonite. The preparation method comprises the steps of mixing, injection moulding, and sulfuration and the like. The method employs polylactic acid fiber, casein and ca bentonite as reinforcement, and the service life and physical properties of the rubber nipple silica gel material are increased.

Description

technical field [0001] The invention belongs to the technical field of silica gel products, and in particular relates to a silica gel material for a feeding bottle nipple and a preparation method thereof. Background technique [0002] Natural latex has been used as raw material for infant pacifiers in history. Natural latex is a soft material with a very high elongation at break. It has good elasticity and is easy to return to its original shape after being deformed. The disadvantages of manufactured pacifiers are that they have peculiar smell, are prone to aging, and have a short service life. Therefore, a liquid silicone rubber nipple formed by high-temperature heat vulcanization has appeared. The silicone rubber nipple has the characteristics of no peculiar smell, high temperature resistance, repeated boiling and disinfection, not easy to aging, and long service life. However, the sucking part and venting part of the pacifier are the key points of the whole product. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/04C08L83/06C08L67/04C08L89/00C08K3/34C08K3/36C08K5/5419
CPCC08K2201/006C08L83/04C08L83/06C08L2201/10C08L2205/035C08L2205/16C08L2312/00C08L67/04C08L89/00C08K3/346C08K3/36C08K5/5419
Inventor 不公告发明人
Owner 长沙浩然医疗科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products