Ceramic body paste based on composite rock mineral

A technology of ceramic mud and minerals, applied in the field of ceramics, can solve the problems of low firing efficiency of ceramic mud, and achieve the effects of good compactness, high firing efficiency and good quality

Inactive Publication Date: 2018-11-23
德阳极光文创设计有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is that the sintering efficiency of ceramic mud of shale minerals is relatively low, and the purpose is to provide ceramic mud based on shale minerals to solve the use problem of ceramic mud of shale minerals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The ceramic mud based on shale minerals of the present invention comprises the following components in parts by weight: 10-16 parts of red clay, 23-36 parts of porcelain sand, 10-17 parts of fine mud, 24-39 parts of porcelain clay, 11-39 parts of quartz 21 parts, purple sand shale 10-18 parts, hematite 14-26 parts, anatase 8-19 parts, kaolinite 13-26 parts, illite 8-19 parts, chlorite 5-16 parts, 4 to 16 parts of calcite.

[0021] Ceramic mud based on shale minerals, including the following components in parts by weight: 12-15 parts of red clay, 28-33 parts of porcelain sand, 13-16 parts of refined mud, 29-34 parts of porcelain clay, and 15-20 parts of quartz , 14-17 parts of purple sand shale, 17-24 parts of hematite, 11-18 parts of anatase, 18-22 parts of kaolinite, 11-17 parts of illite, 9-13 parts of chlorite, and 8 parts of calcite ~14 servings.

[0022] Ceramic mud based on shale minerals, including the following components in parts by weight: 13 parts of red cl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ceramic body paste based on composite rock mineral. The ceramic body paste is prepared from the following components in parts by weight: 10 to 16 parts of red clay, 23 to 26 parts of ceramic grit, 10 to 17 parts of refined clay, 24 to 39 parts of petuntse, 11 to 21 parts of quartz, 10 to 18 parts of red stoneware shale, 14 to 26 parts of hematite, 8 to 10 parts of anatase,13 to 26 parts of kaolinite, 8 to 19 parts of illite, 5 to 16 parts of chlorite, 4 to 16 parts of calcite. The components of the ceramic body paste provided by the invention supplement each other, theprepared finished product is better in compactness.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to ceramic mud based on composite rock minerals. Background technique [0002] Shale is a kind of sedimentary rock with complex composition, but all have thin sheet-like or thin-sheet-like joints. It is mainly a rock formed by clay deposition through pressure and temperature, but it is mixed with quartz, feldspar debris and other chemical substances. Substances can be divided into calcareous shale, iron shale, siliceous shale, carbonaceous shale, black shale, kerogen shale, etc., according to the composition of the mixture, among which iron shale may become iron ore, Oil shale can be used to refine oil, and black shale can be used as an indicator formation for oil. [0003] Shale is formed in a still water environment, and sediment has been deposited for a long time, so it often exists in lakes and river deltas. Shale is also formed in oceanic continental shelves, and shale often contains f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13C04B33/04
CPCC04B33/04C04B33/13C04B33/16C04B2235/3208C04B2235/3232C04B2235/3272
Inventor 赖国全赖国光
Owner 德阳极光文创设计有限公司