X70-grade abrasion-resistant pipeline steel plate for delivery pipeline and manufacture method thereof

A technology for conveying pipelines and manufacturing methods, applied in the field of steel materials, can solve problems such as insufficient wear resistance and insufficient wear resistance, and achieve the effects of increasing wear loss, improving hardenability, and increasing hardness

Inactive Publication Date: 2018-11-27
NANJING IRON & STEEL CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

X series pipeline steel is commonly used for pipelines. This series of pipeline steel can achieve good strength and toughness and excellent welding performance, but it cannot meet the requirements of pipeline transportation slurry in terms of wear resistance
At present, the existing slurry pipelines at home and abroad are still constructed with conventional pipeline steel, but they still use the traditional polygonal ferrite + pearlite structure. Although the strength level meets the requirements of domestic coal transportation pipeline projects, it is not excellent in wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • X70-grade abrasion-resistant pipeline steel plate for delivery pipeline and manufacture method thereof
  • X70-grade abrasion-resistant pipeline steel plate for delivery pipeline and manufacture method thereof
  • X70-grade abrasion-resistant pipeline steel plate for delivery pipeline and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An X70 grade wear-resistant pipeline steel plate for transportation pipelines provided in this embodiment and its manufacturing method, the chemical composition of which is shown in Table 1.

[0027] The invention is smelted in a 120-ton top-bottom double-blown converter, continuously cast into a continuous casting slab with a section of 220mm×1800mm, and carries out controlled rolling and cooling in a 3500mm coil rolling mill production line.

[0028] The thickness of the product is 15.9mm, and the system is designed according to the composition and ratio of raw material preparation → hot metal pretreatment → top and bottom combined blowing converter smelting → LF furnace refining → RH vacuum treatment → slab pouring → walking furnace heating → high pressure water descaling → controlled rolling Controlled cooling → post-rolling treatment,

[0029] Among them, when the walking furnace is heated, the slab heating temperature is 1210°C, and the heating time is 11-14min / cm...

Embodiment 2

[0031] An X70 grade wear-resistant pipeline steel plate for transportation pipelines provided in this example and a manufacturing method thereof are different from Example 1 in that its chemical composition is shown in Table 1.

Embodiment 3

[0033] An X70 grade wear-resistant pipeline steel plate for transportation pipelines provided in this example and a manufacturing method thereof are different from Example 1 in that its chemical composition is shown in Table 1.

[0034] The chemical composition (mass percentage: %) of table 1 embodiment 1~embodiment 3

[0035] Element

C

Si

mn

Cr

Nb

Ti

Mo

Ni

P

S

Example 1

0.069

0.30

1.60

0.23

0.056

0.017

0.25

0.26

0.008

0.0012

Example 2

0.082

0.15

1.51

0.17

0.065

0.011

0.15

0.18

0.008

0.0011

Example 3

0.075

0.28

1.55

0.25

0.061

0.015

0.23

0.25

0.009

0.0011

[0036] The mechanical properties of wear-resistant pipeline steel plates in Examples 1 to 3 are shown in Table 2:

[0037]

[0038] The wear-resistant pipeline steel obtained by the above composition design and manufacturing method is the microstructure of granul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an X70-grade abrasion-resistant pipeline steel plate and a manufacture method thereof, and relates to the field of steel materials. The steel plate is prepared from the following chemical ingredients in percentage by mass: 0.060-0.090 percent of C, 1.30-1.70 percent of Mn, 0.15-0.25 percent of Cr, 0.10-0.35 percent of Si, 0.035-0.070 percent of Nb, 0.010-0.020 percent of Ti, 0.10-0.30 percent of Ni, less than or equal to 0.010 percent of P, less than or equal to 0.002 percent of S and the balance of Fe and inevitable impurities. According to the steel plate, during component designing, the final performance of an abrasion-resistant pipeline steel plate is ensured to meet the requirement for pipeline manufacture, the steel hardness is considered to be improved to reinforce the abrasion resistance on that basis, and the X70-grade abrasion-resistant pipeline steel plate has better abrasion resistance than that of a conventional pipeline steel during slurry erodingand abrading due to component system optimization and microscopic organization with coordinated hardness proportion.

Description

technical field [0001] The invention relates to the technical field of iron and steel materials, in particular to an X70-grade wear-resistant pipeline steel plate for conveying pipelines and a manufacturing method thereof. Background technique [0002] Pipeline transportation has played an important role in gas and liquid transportation projects such as oil and natural gas because of its large transportation volume, strong adaptability, low operating cost, and excellent environmental benefits. Slurry transportation of solid materials such as coal and mineral materials can make full use of the advantages of pipeline transportation to alleviate the difficulty of material transportation. The long-distance and large-volume pipeline transportation of materials in industries such as coal, electric power, metallurgy, petroleum, chemical industry, and building materials requires a large amount of pipeline steel. Since coal powder, mineral concentrate powder, tailings, cement, ash a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/48C22C38/50C22C38/58C21D8/02
CPCC22C38/02C21D8/0226C21D2211/002C21D2211/005C22C38/04C22C38/48C22C38/50C22C38/58
Inventor 姜金星张鹏程武会宾贠强鹏
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products