A kind of glazing oil and its preparation method

A technology of varnish and parts by weight, applied in the direction of coating, etc., can solve the problem of uneven surface thickness, etc., and achieve the effects of enhancing leveling, improving stability, and improving surface hydrophobicity

Active Publication Date: 2021-04-20
杭州创先彩印包装有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the first object of the present invention is to provide a varnish and a preparation method thereof, which solves the problem of uneven thickness of the varnish on the surface of printing products, and has the effect of improving the leveling of the varnish. advantage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glazing oil and its preparation method
  • A kind of glazing oil and its preparation method
  • A kind of glazing oil and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Embodiment 1: a kind of varnish, including the components shown in Table 1 in parts by weight.

[0052] The above-mentioned high-strength impermeable concrete is prepared through the following steps:

[0053] S1, take the emulsifier and water in corresponding parts by weight, heat in a water bath to 80° C. to dissolve, and stir at high speed to obtain an emulsified solution. Take corresponding parts by weight of methyl methacrylate, butyl acrylate, acrylic acid, acrylonitrile and hydroxyethyl acrylate, mix them uniformly, add them into the emulsified solution, and mix them uniformly to obtain a seed emulsion.

[0054] S2, taking corresponding parts by weight of polyvinyl alcohol powder and initiator and mixing to obtain an additive liquid. Take 20% of the seed emulsion, add 1 / 3 of the additive solution, mix evenly to obtain a reaction solution, and control the reaction temperature at 80°C. After the reaction solution turns blue, add the remaining seed emulsion and the...

Embodiment 2-7

[0057]Embodiment 2-7: a kind of glazing oil, the only difference from embodiment 1 is that the parts by weight of some components are different; the components and parts by weight are shown in Table 1.

[0058] Components and their corresponding parts by weight in table 1. embodiment 1-7

[0059]

Embodiment 8-9

[0060] Embodiment 8-9: A kind of glazing oil, the only difference from Embodiment 1 is that polyethylene glycol monomethyl ether methacrylate with relative molecular weights of 1000 and 1200 are selected.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glazing oil and a preparation method thereof, and relates to the technical field of printing; the glazing oil comprises the following components in parts by weight: comonomer: 1105-1578 parts; water: 1108-1568 parts; emulsifier: 80‑138 parts; sodium hydroxide: 104‑151 parts; initiator: 94‑121 parts. Among them, comonomers include methyl methacrylate, butyl acrylate, acrylic acid, acrylonitrile, and hydroxyethyl acrylate; emulsifiers include polyethylene glycol monomethyl ether methacrylate and / or p-styrenesulfonic acid sodium. The glazing oil is prepared through the following steps: S1, take the copolymerization unit, sodium hydroxide, emulsifier and water of the corresponding parts by weight, heat and dissolve, and mix uniformly to obtain the seed emulsion; S2, take the initiator of the corresponding parts by weight Add it into the seed emulsion and mix evenly to obtain an emulsion polymer. The invention has the advantage of improving the leveling property of the glazing oil.

Description

technical field [0001] The invention relates to the technical field of printing, in particular to a varnish and a preparation method thereof. Background technique [0002] Glazing oil refers to a liquid that is coated on the surface of printed matter to increase gloss, abrasion resistance and water resistance. Varnishes include water-based varnishes, oil-based varnishes, UV varnishes, and alcohol-soluble varnishes. At present, water-based varnish is the most widely used in China, because it has very good environmental protection performance. [0003] The Chinese patent with the authorized announcement number CN104845500B and the authorized announcement date on March 1, 2017 discloses a printing varnish, which is composed of the following raw materials: water-soluble acrylic epoxy resin, mussel mucin, Calcium acetate, acrylates, solvents, and functional additives are specifically prepared through the following steps: add acrylates to the water-soluble acrylic epoxy resin in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D151/08C09D133/20C08F283/06C08F220/14C08F220/18C08F220/06C08F220/20C08F220/46C08F212/14
CPCC09D133/20C09D151/08C08F220/14C08F283/065C08F220/1804C08F220/06C08F220/20C08F220/46C08F212/14
Inventor 颜丽英
Owner 杭州创先彩印包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com