Carbon fiber composite material plate and ceramic plate welding method

A composite material and carbon fiber technology, which is applied in the field of welding carbon fiber composite material sheets and ceramic sheets, can solve the problems of poor joint strength and large joint stress, and achieve the effect of improving joint strength, realizing metallurgical connection, and increasing the flow of solder.

Active Publication Date: 2018-12-25
济南英维新材料科技合伙企业(有限合伙)
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the shortcomings of conventional brazing materials that are prone to defects, poor joint strength, and large joint stress on the welded joints of ceramics and carbon fiber composite materials, and propose a method for welding carbon fiber composite material plates and ceramic plates. The method includes The following steps: stack the carbon fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] In this embodiment, the reinforced phenolic epoxy composite material T300 / 648 plate and 100*50*2mm silicon oxide ceramic plate with a size specification of 100*50*2mm are used; the specific composition of the AgCuTi solder is Ag70.5Cu27.5Ti2 solder, which comes from Changsha Maxtor Metal Materials Co., Ltd.

[0016] This embodiment includes the following steps:

[0017] S1, machining the silicon oxide ceramic plate and the reinforced phenolic epoxy composite material to obtain the plate to be welded;

[0018] S2, use 400-grit sandpaper to polish the silicon oxide ceramic plate and the reinforced phenolic epoxy composite material plate, and then put them into the acetone solution for ultrasonic cleaning for 10-15 minutes to remove surface oil and other sundries to ensure that the surface is clean;

[0019] S3, adding nano-silicon carbide particles to the AgCuTi solder, the nano-silicon carbide particles are 3%-5% of the weight of the AgCuTi solder, and performing ball m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of dissimilar material connection, and particularly relates to a carbon fiber composite material plate and ceramic plate welding method which includes thesteps: sequentially overlapping a carbon fiber composite material plate, a nano-brazing filler metal and a ceramic plate from top to bottom; performing pressing assembly to form an assembly part; brazing the assembly part under inert gas atmosphere protection of an external magnetic field; performing heat preservation, cooling and heat treatment after welding to finish connection of the carbon fiber composite material plate and the ceramic plate. The nano-brazing filler metal is combined with inert gas protection brazing of the external magnetic field for the first time, texture formation anddefect inhibition in the brazing process are facilitated, and the performance of a connecting joint is obviously improved.

Description

technical field [0001] The invention belongs to the technical field of connection of dissimilar materials, and more specifically relates to a method for welding a carbon fiber composite material plate and a ceramic plate. Background technique [0002] At present, brazing material is mainly used for ceramic connection, and there are no related reports on the connection of ceramics and carbon fiber composite materials. Brazing with conventional filler metals, the joints are prone to defects, the strength is average, and the quality of the joints is relatively poor, and the stress of the joints is relatively large. [0003] Inert gas protective brazing with nano-solder and magnetic field can make the structure of the joint more uniform. In addition, the external magnetic field can suppress the defects in the brazing process and obtain a joint with higher performance. Contents of the invention [0004] The purpose of the present invention is to overcome the shortcomings of co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B37/00
CPCC04B37/00
Inventor 戴军杨莉张尧成姜伟沈赛
Owner 济南英维新材料科技合伙企业(有限合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap