Cold-resistant and crack-resistant PVC resin for door and window plastic steel profiles

A technology of PVC resin and plastic steel for doors and windows, applied in the field of polymer materials, can solve the problems of material toughness and low temperature resistance, poor high temperature resistance, brittle deformation of PVC resin, and the influence of material mechanical strength, etc. Low temperature performance, effect of improving processing characteristics and thermal stability

Inactive Publication Date: 2018-12-28
HEFEI LONGYANG AGRI TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The most important material in plastic-steel doors and windows is polyvinyl chloride, that is, PVC resin; polyvinyl chloride has good processing characteristics and outstanding mechanical properties, but the material's toughness, low temperature resistance, and high temperature resistance are poor. Embrittlement deformation occurs, and the toughness of the material is greatly reduced. In this state, after being impacted, PVC is very easy to crack and lose its suppor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold-resistant and crack-resistant PVC resin for door and window plastic steel profiles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A PVC resin for cold-resistant and crack-resistant door and window plastic-steel profiles. According to the mass parts, the components of the PVC resin include: 100 parts of PVC, 4 parts of ACR processing aid, 18 parts of filler, 6 parts of cold-resistant toughening agent, polyethylene wax 0.5 part, 1 part of composite stabilizer, 0.4 part of ultraviolet absorber, 0.2 part of antioxidant.

[0037] Wherein, the filler is a mixture of titanium dioxide and light calcium carbonate mixed at a ratio of 6:1.

[0038] The composite stabilizer contains calcium zinc stabilizer and di-n-butyltin dilaurate.

[0039] The ultraviolet absorber is ultraviolet absorber RMB; the antioxidant is antioxidant 164.

[0040] The preparation method of the PVC resin that present embodiment provides is:

[0041] According to the parts by mass, PVC, ACR processing aids, fillers, cold-resistant toughening agents, polyethylene wax, composite stabilizers, ultraviolet absorbers, and antioxidants are...

Embodiment 2

[0043] A PVC resin for cold-resistant and crack-resistant door and window plastic-steel profiles. According to the parts by mass, the components of the PVC resin include: 120 parts of PVC, 7 parts of ACR processing aid, 25 parts of filler, 9 parts of cold-resistant toughening agent, polyethylene wax 1.2 parts, 3 parts of composite stabilizer, 0.8 part of ultraviolet absorber, 0.5 part of antioxidant.

[0044] Wherein, the filler is a mixture of titanium dioxide and light calcium carbonate mixed at a ratio of 6:1.

[0045] The composite stabilizer contains calcium zinc stabilizer and di-n-butyltin dilaurate.

[0046] The ultraviolet absorber is ultraviolet absorber UV-9; the antioxidant is antioxidant 1076.

[0047] The preparation method of the PVC resin that present embodiment provides is:

[0048] According to the parts by mass, PVC, ACR processing aids, fillers, cold-resistant toughening agents, polyethylene wax, composite stabilizers, ultraviolet absorbers, and antioxida...

Embodiment 3

[0050] A PVC resin for cold-resistant and crack-resistant door and window plastic-steel profiles. According to the mass parts, the components of the PVC resin include: 110 parts of PVC, 5.5 parts of ACR processing aid, 21 parts of filler, 7 parts of cold-resistant toughening agent, polyethylene wax 0.9 parts, 2.2 parts of composite stabilizers, 0.6 parts of ultraviolet absorbers, and 0.4 parts of antioxidants.

[0051] Wherein, the filler is a mixture of titanium dioxide and light calcium carbonate mixed at a ratio of 6:1.

[0052] The composite stabilizer contains calcium zinc stabilizer and di-n-butyltin dilaurate.

[0053] The ultraviolet absorber is ultraviolet absorber UVP-327; the antioxidant is antioxidant TNP.

[0054] The preparation method of the PVC resin that present embodiment provides is:

[0055] According to the parts by mass, PVC, ACR processing aids, fillers, cold-resistant toughening agents, polyethylene wax, composite stabilizers, ultraviolet absorbers, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of polymer materials, in particular to a cold-resistant and crack-resistant PVC resin for door and window plastic steel profiles. The PVC resin includes PVC, ACR processing aid, filler, cold-resistant toughening agent, polyethylene wax, composite stabilizer, ultraviolet absorber and antioxidant. The cold-resistant toughening agent is a novel material prepared by compounding a plurality of elastomer materials and high-hardness fillers; the filler is a mixture of titanium dioxide and light calcium carbonate; the composite stabilizer contains calcium-zinc stabilizer and di-n-butyltin dilaurate; the ultraviolet absorber is ultraviolet absorber RMB, ultraviolet absorber UV-9 or ultraviolet absorber UVP-327; and the antioxidant is antioxidant 164, antioxidant 1076 or antioxidant TNP. The PVC resin material has good toughness and outstanding low temperature resistance, and is not easily embrittled under low temperature conditions. The cold-resistant and crack-resistant PVC resin is good in impact resistance and does not crack easily.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PVC resin for cold-resistant and crack-resistant door and window plastic-steel profiles. Background technique [0002] Doors and windows are divided into enclosure components or partition components according to their positions, which are important components in the building enclosure structure system. According to the different types of materials, the doors and windows on the market today can be roughly divided into the following categories: wooden doors and windows, steel doors and windows, plastic steel doors and windows, aluminum alloy doors and windows, glass steel doors and windows, stainless steel doors and windows, iron flower doors and windows. With the continuous improvement of people's living standards, the types of doors and windows and their derivative products are still increasing, and the grades are gradually rising, such as heat-insulated broken bridge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L33/04C08L23/06C08K13/02C08K3/22C08K3/26
CPCC08K2003/2241C08K2003/265C08L27/06C08L2201/08C08L2205/03C08L33/04C08L23/06C08K13/02C08K3/22C08K3/26
Inventor 沈涛
Owner HEFEI LONGYANG AGRI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap