High-toughness and weather-resistant plastic photovoltaic scaffold

A photovoltaic bracket and weather-resistant technology, applied in the field of high-toughness and weather-resistant plastic photovoltaic brackets, can solve the problems of inconvenient handling and installation, low bearing capacity, easy corrosion, etc., and achieve the effect of excellent comprehensive performance.

Inactive Publication Date: 2019-01-01
江苏德溢利新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the accessories of photovoltaic brackets in the domestic market are mainly divided into two kinds of accessories made of galvanized steel and aluminum alloy. The section steel is heavy, inconvenient to transport and install, and easy to corrode; aluminum alloy brackets are generally used in the solar energy application on the roof of civil buildings. , aluminum alloy has the characteristics of corrosion resistance, light weight, beautiful and durable, but its bearing capacity is low
[0003] At present, people are more inclined to use plastic photovoltaic brackets. The biggest advantage lies in its low production cost and inexhaustible raw material reserves. This photovoltaic bracket can not only be bent, but also transparent in color, and can be fully integrated with windows and blinds without damage. The exterior wall and the appearance of the building, but the existing toughness and weather resistance need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness and weather-resistant plastic photovoltaic scaffold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 2

[0021] The preparation of embodiment 1 titanium dioxide-attapulgite composite

[0022] 1) Disperse attapulgite with a mesh number of 800-1000 into 38 wt% hydrochloric acid solution under ultrasonic conditions, reflux in a water bath at 100°C for 16 hours, filter, wash until neutral and dry to obtain purified attapulgite for later use;

[0023] 2) Stir 100 g of the purified attapulgite evenly, then add 1 L of tetrabutyl titanate, 12 L of ethanol, 10 L of acetylacetone, and 12 L of deionized water, stir and react at room temperature to obtain a sol and then turn it into a gel. The obtained gel is dried, calcined and ground to obtain titanium dioxide modified attapulgite.

[0024] 3) Add 10 g of silicone oil to the obtained titanium dioxide-attapulgite composite by spraying, stir evenly, then add 5 g of silane coupling agent under high-speed stirring at 1500-2000 r / min, and mix evenly.

Embodiment 2

[0025] Example 2 A kind of high-toughness and weather-resistant plastic photovoltaic support

[0026] It consists of the following raw materials in parts by weight: 100 parts of polyvinyl chloride, 2.5 parts of calcium zinc stabilizer, 10 parts of CPE, 3 parts of nitrile rubber, 0.5 part of paraffin wax, 0.4 part of PE wax, 0.4 part of ACR-P551, calcium sulfate whisker 10 parts, 5 parts of titanium dioxide, 10100.5 parts of antioxidant, 0.2 part of UV531, 2 parts of rare earth stabilizer, 15 parts of titanium dioxide-attapulgite composite prepared in Example 1.

Embodiment 3

[0027] Example 3 A kind of high toughness and weather-resistant plastic photovoltaic support

[0028] It consists of the following raw materials in parts by weight: 110 parts of polyvinyl chloride, 3 parts of calcium zinc stabilizer, 12 parts of CPE, 4 parts of nitrile rubber, 0.8 part of paraffin wax, 0.6 part of PE wax, 0.4 part of ACR-P551, calcium sulfate whisker 12 parts, 5 parts of titanium dioxide, 0.5 parts of antioxidant 1010, 0.2 parts of UV531, 2 parts of rare earth stabilizer, 12 parts of titanium dioxide-attapulgite composite prepared in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
volumeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-toughness and weather-resistant plastic photovoltaic scaffold, which comprises the following raw materials by weight: 100-120 parts of polyvinyl chloride, 2-5 parts of acalcium-zinc stabilizer, 10-12 parts of CPE, 2-5 of nitrile butadiene rubber, 0.2-0.8 part of paraffin, 0.2-0.6 part of PE wax, 0.2-0.6 part of ACR-P551, 0.2-0.5 part of an antioxidant 1010, 0.2-0.5part of UV531, 2-4 parts of a rare earth stabilizer, and 10-15 parts of a titanium dioxide-attapulgite complex. According to the present invention, the test results prove that the prepared plastic hassubstantially improved toughness and substantially enhanced weather resistance, and can main long-lasting gloss.

Description

technical field [0001] The invention relates to a high-tough and weather-resistant plastic photovoltaic support. Background technique [0002] At present, the accessories of photovoltaic brackets in the domestic market are mainly divided into two kinds of accessories made of galvanized steel and aluminum alloy. The section steel is heavy, inconvenient to transport and install, and easy to corrode; aluminum alloy brackets are generally used in the solar energy application on the roof of civil buildings. , aluminum alloy has the characteristics of corrosion resistance, light weight, beautiful and durable, but its bearing capacity is low. [0003] At present, people are more inclined to use plastic photovoltaic brackets. The biggest advantage lies in its low production cost and inexhaustible raw material reserves. This photovoltaic bracket can not only be bent, but also transparent in color, and can be fully integrated with windows and blinds without damage. The exterior wall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L9/02C08L23/28C08L23/06C08K13/06C08K9/06C08K9/02C08K3/34
CPCC08K2003/2241C08L27/06C08L2201/08C08L2205/035C08L9/02C08L23/286C08L23/06C08K13/06C08K9/06C08K9/08C08K9/02C08K3/346
Inventor 施新波白凤香陈玉龙
Owner 江苏德溢利新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap