Fly ash colorful brick and preparation method

A technology of fly ash and colored bricks, which is applied to pavement, buildings, roads and other directions paved with prefabricated blocks to achieve the effects of increasing productivity, alleviating environmental pollution, and saving time

Inactive Publication Date: 2017-08-18
肥西县碧涛建材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the defects in the prior art, the object of the present invention is to provide a fly ash colored brick, which solves the problem of fly ash resource utilization, and the preparation method of the provided fly ash colored brick reduces the production cycle and does not require sintering , does not require heat energy, saves time, improves productivity, reduces costs, and more importantly, it can alleviate the problem of environmental pollution caused by fly ash

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The fly ash colored brick provided in this embodiment comprises the following components in parts by weight: 51 parts of fly ash, 8 parts of calcium sulfate, 17 parts of gypsum, 1.05 parts of water glass, and 23 parts of pigment , 5 parts of adhesive and 20 parts of water.

[0028] The adhesive comprises the following components in parts by weight: 25 parts of attapulgite clay, 13 parts of phosphogypsum and 15 parts of ferrous sulfate.

[0029] According to another aspect of the present invention, provide described fly ash colored brick preparation method, described method comprises the steps:

[0030] (1) Material treatment: fly ash is the undersize material after thermal stewing and magnetic separation, with a particle size of 7mm;

[0031] (2) Forming: Weigh the materials according to the ratio of the raw materials of the fly ash colored bricks, mix them evenly with a mixer, load them into the brick pressing mold, and press them into shape with a brick pressing mach...

Embodiment 2

[0035] The fly ash colored brick provided in this embodiment comprises the following components in parts by weight: 35 parts of fly ash, 14 parts of calcium sulfate, 6 parts of gypsum, 3.04 parts of water glass, and 15 parts of pigment , 19 parts of adhesive and 7 parts of water.

[0036] The adhesive comprises the following components in parts by weight: 12 parts of attapulgite clay, 25 parts of phosphogypsum and 7 parts of ferrous sulfate.

[0037] According to another aspect of the present invention, provide described fly ash colored brick preparation method, described method comprises the steps:

[0038] (1) Material treatment: fly ash is the undersieve after thermal stewing and magnetic separation, with a particle size of 4mm;

[0039] (2) Forming: Weigh the materials according to the ratio of the raw materials of the fly ash colored bricks, mix them evenly with a mixer, load them into the brick pressing mold, and press them into shape with a brick pressing machine;

[...

Embodiment 3

[0043] The fly ash colored brick provided in this embodiment, the fly ash colored brick includes the following components in parts by weight: the fly ash colored brick includes the following components in parts by weight: 50 parts of fly ash, sulfuric acid 9 parts of calcium, 15 parts of gypsum, 2.05 parts of water glass, 22 parts of pigment, 7 parts of adhesive and 15 parts of water.

[0044] The adhesive comprises the following components in parts by weight: 15 parts of attapulgite clay, 23 parts of phosphogypsum and 9 parts of ferrous sulfate.

[0045] According to another aspect of the present invention, provide described fly ash colored brick preparation method, described method comprises the steps:

[0046] (1) Material treatment: fly ash is the undersieve after thermal stewing and magnetic separation, with a particle size of 4mm;

[0047] (2) Forming: Weigh the materials according to the ratio of the raw materials of the fly ash colored bricks, mix them evenly with a m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building materials and provides a fly ash colorful brick and a preparation method. The fly ash colorful brick comprises, by weight, 35-51 parts of fly ash, 8-14 parts of calcium sulfate, 6-17 parts of gypsum, 1.05-3.04 parts of sodium silicate, 15-23 parts of pigment, 5-19 parts of adhesive and 7-20 parts of water. The fly ash colorful brick solves the problem about fly ash recycling. The provided preparation method of the fly ash colorful brick shortens the production period, sintering and heat energy are not needed, time is saved, the productivity is improved, the cost is reduced, and more importantly, the environment pollution problem caused by fly ash can be relieved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a fly ash colored brick and a preparation method thereof. Background technique [0002] Fly ash is one of the largest industrial wastes in my country. With the development of the power industry, the discharge of fly ash from coal-fired power plants is increasing year by year. If a large amount of fly ash is not treated, it will generate dust and pollute the atmosphere; if it is discharged into the water system, it will cause river silting, and the toxic chemicals in it will also cause harm to human beings and organisms. In addition, fly ash can be used as an admixture for concrete. [0003] my country is a large coal-producing country, and coal is used as the basic fuel for electric power production. my country's energy industry has developed steadily, with an annual growth rate of 7.3% in power generation capacity. The rapid development of the power indu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14E01C5/06C04B111/82
CPCC04B28/143C04B2111/00017C04B2111/0075C04B2111/82E01C5/065C04B18/08C04B14/365C04B22/00C04B14/102C04B22/149C04B2103/54C04B20/0076
Inventor 俞克波
Owner 肥西县碧涛建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com