Preparation method of platinum nano cage and application to catalyst

A gold nanocage and gold nanoparticle technology, which is applied in the field of synthesis of nanomaterials, can solve the problems of reduced catalytic activity and poor stability of platinum-based nanomaterials, and achieve the effects of easy implementation, easy scale-up, and cost reduction

Active Publication Date: 2019-01-25
JIAXING UNIV
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the embodiments of the present invention is to provide a method for preparing platinum-gold nanocages to solve the problems of poor stability and reduced catalytic activity of existing platinum-based nanomaterials in the process of being used as catalysts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of platinum nano cage and application to catalyst
  • Preparation method of platinum nano cage and application to catalyst
  • Preparation method of platinum nano cage and application to catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of preparation method of platinum-gold nanocage, described preparation method comprises the steps:

[0045] a. Preparation of gold nanoseed solution: Add 7.5mL 0.5mol / L cetyltrimethylammonium bromide and 87.5μL 0.02mol / L tetrahydrate chloroauric acid tetrahydrate solution in a 50mL round bottom flask, under vigorous stirring Add 0.6 mL of 0.01 mol / L sodium borohydride solution in an ice bath, and then continue stirring at 25°C for 3 hours to obtain a 3-5 nm gold nanometer seed solution. The reaction involved in step a is 8HAuCl 4 ·3H 2 O+3NaBH 4 =8Au+3NaB(OH) 4 +12H 2 O+32HCl

[0046] b. Preparation of cut-angle octahedral gold nanoparticles solution:

[0047] b1. Dilute the gold nano-seed solution obtained in step a 100 times with water to obtain a diluted gold nano-seed solution, add 12mL 0.016mol / L hexadecyltrimethylammonium bromide solution in a round bottom flask, 25 μL 0.02mol / L chloroauric acid tetrahydrate solution, 25 μL 0.0388mol / L sodium citrat...

Embodiment 2

[0062] A thin-film catalyst, described thin-film catalyst is prepared from the cut-angle octahedral platinum-gold nanocage solution that utilizes embodiment 1 to obtain, and its preparation process is as follows:

[0063] Take 2 μL of cut-angle octahedral platinum-gold nanocage solution and drop it on the surface of the conductive material of the glassy carbon plate, volatilize in an oven at 70 degrees Celsius for 10 minutes, repeat this step to obtain a three-dimensional ordered cut-angle octahedral platinum-gold nanocage film with a thickness of 7 μm Catalysts such as Figure 4 As shown, what is shown is the scanning electron microscope image of the obtained angular-cut octahedral platinum-gold nanocage thin film catalyst, and the lower right corner is a structural schematic diagram. porous structure.

Embodiment 3

[0065] The angle-cut octahedral platinum-gold nanocage film catalyst obtained in Example 2 is pretreated by cyclic voltammetry scanning, the voltage range is 0.6 to 1.0 volts, and the electrolyte is 0.1mol / L sulfuric acid, until the cyclic voltammetry can be obtained until repeated.

[0066] Before testing the methanol oxidation performance of the catalyst, the electrolyte (0.1 mol / L sulfuric acid and 1 mol / L methanol) was blown with nitrogen to remove dissolved oxygen for 10 minutes.

[0067] The cleaved octahedral platinum-gold nanocage thin film catalyst, the platinum-coated cleaved octahedral gold nanoparticle catalyst and the 10% Pt / C E-TEK catalyst with the same specific surface area were applied to the catalytic oxidation of methanol. Cyclic voltammetry was compared as Figure 5 Shown are the comparison diagrams of cyclic voltammetry polarization curves of the three catalysts in 0.1mol / L sulfuric acid and 1mol / L methanol solutions, s1, s2, s3 respectively represent the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention discloses a method of preparing platinum nano cage, relates to the technical field of synthesis technology field of nano materials, and the preparation method includesthe following steps: a. preparation of gold nano particle seed solution; b. preparation of angular octahedral gold nanoparticle solution; c. preparation of platinum-coated angle-cutting octahedral gold nanoparticle solution; d. the octahedral gold nano particles are etched to obtain the octahedral platinum nano cage solution. The preparation method comprises the following steps prepare corner-cutting octahedron gold nanoparticles by using the solution phase gradual growth method; selectively growing platinum on the corners of the corner-cutting octahedron by using the solution phase method; and selectively etching most gold to generate the corner-cutting octahedron platinum nano cage; the cut-angle octahedral platinum nano cage with a plurality of edges and corners is mixed with platinum nano cage is self-assembled into an orderly arranged porous film which has long-term stability and higher specific surface area and important application potential in the field of catalysis.

Description

technical field [0001] The invention relates to the technical field of synthesis of nanomaterials, in particular to a preparation method of a platinum-gold nanocage and its application in catalysts. Background technique [0002] Platinum catalyst is a general term for catalysts made of metal platinum as the main active component. It is mainly used for ammonia oxidation, reforming of petroleum hydrocarbons, oxidation and hydrogenation of unsaturated compounds, removal of carbon monoxide and nitrogen oxides in gases, etc. Process is a kind of catalyst often used in chemical, petroleum and chemical reaction processes. It has high catalytic activity, strong selectivity, convenient catalyst production, and low usage. Component compounding, etc., to optimize catalytic performance. [0003] But because platinum is a rare metal, the price is relatively expensive. Therefore, in the application of industrial catalysis, special attention should be paid to improving the utilization ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/16B22F1/00C22C1/08B82Y30/00B82Y40/00B01J23/52
CPCC22C1/08B82Y30/00B82Y40/00B01J23/52B22F9/16B22F2009/165B22F1/07
Inventor 张立秋陈振煌刘立春
Owner JIAXING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka