Sound-absorption and flame-retardant automobile trim material and preparation method thereof

A technology for automobile interior and sound absorption, applied in the field of automobile interior materials, can solve the problems of insufficient technological content, single function, complicated process, etc., and achieve the effects of thick touch, good flame retardancy, and good sound absorption effect.

Inactive Publication Date: 2019-02-15
JURONG FENGLING TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, automotive interior materials generally have several shortcomings such as insufficient technological content, single function, high price and complicated process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound-absorption and flame-retardant automobile trim material and preparation method thereof
  • Sound-absorption and flame-retardant automobile trim material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A sound-absorbing and flame-retardant automotive interior material. The raw materials include, in parts by weight, 30 parts of polypropylene resin, 5 parts of ABS resin, 3 parts of polymethyl methacrylate, 2 parts of polyester fiber, and 4 parts of degummed jute fiber. 1 part of barium sulfate, 2 parts of polyvinyl alcohol, 1 part of diarsenic trioxide, 2 parts of flame retardant, 3 parts of toughening agent, 1 part of silane coupling agent.

[0017] The flame retardant is a mixture of ammonium polyphosphate, montmorillonite and aluminum hydroxide, and the weight ratio of the three is 3:1:2.

[0018] The toughening agent is polymethyl methacrylate-butadiene-styrene copolymer.

[0019] The barium sulfate is nano barium sulfate with a particle size of 100-300nm.

[0020] The preparation method of the above-mentioned sound-absorbing and flame-retardant automotive interior material comprises the following steps:

[0021] Step 1: Soak the polyester fiber and degummed jute ...

Embodiment 2

[0024] A sound-absorbing and flame-retardant automotive interior material. The raw materials include, in parts by weight, 35 parts of polypropylene resin, 7 parts of ABS resin, 6 parts of polymethyl methacrylate, 3 parts of polyester fiber, and 7 parts of degummed jute fiber. 2 parts of barium sulfate, 4 parts of polyvinyl alcohol, 2 parts of diarsenic trioxide, 4 parts of flame retardant, 5 parts of toughening agent, 2 parts of silane coupling agent.

[0025] The flame retardant is a mixture of ammonium polyphosphate, montmorillonite and aluminum hydroxide, and the weight ratio of the three is 2:2:3.

[0026] The toughening agent is ethylene-methyl acrylate-glycidyl methacrylate copolymer.

[0027] The barium sulfate is nano barium sulfate with a particle size of 100-300nm.

[0028] The preparation method of the above-mentioned sound-absorbing and flame-retardant automotive interior material comprises the following steps:

[0029] Step 1: Soak the polyester fiber and degumm...

Embodiment 3

[0032] A sound-absorbing and flame-retardant automotive interior material, the raw materials include in parts by weight: 40 parts of polypropylene resin, 7 parts of ABS resin, 5 parts of polymethyl methacrylate, 4 parts of polyester fiber, 5 parts of degummed jute fiber, 2 parts of barium sulfate, 3 parts of polyvinyl alcohol, 2 parts of diarsenic trioxide, 4 parts of flame retardant, 4 parts of toughening agent, 2 parts of silane coupling agent.

[0033] The flame retardant is a mixture of ammonium polyphosphate, montmorillonite and aluminum hydroxide, and the weight ratio of the three is 3:1:2.

[0034] The toughening agent is polymethyl methacrylate-butadiene-styrene copolymer.

[0035] The barium sulfate is nano barium sulfate with a particle size of 100-300nm.

[0036] The preparation method of the above-mentioned sound-absorbing and flame-retardant automotive interior material comprises the following steps:

[0037] Step 1: Soak the polyester fiber and degummed jute fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a sound-absorption and flame-retardant automotive trim material and a preparation method thereof. Raw materials of the trim material comprise a polypropylene resin, an ABS resin, polymethyl methacrylate, a polyester fiber, a degummed jute fiber, barium sulfate, polyvinyl alcohol, arsenic trioxide, a flame retardant, a toughening agent and a silane coupling agent. The preparation method comprises the following steps: modifying the polyester fiber and the degummed jute fiber with the silane coupling agent, uniformly mixing the polypropylene resin, the ABS resin, the polymethyl methacrylate, the barium sulfate, the polyvinyl alcohol, the arsenic trioxide, the flame retardant, the toughening agent and the modified fibers by a high mixing machine, carrying out fusion ina screw extruder, and carrying out extrusion to obtain the trim material. The material not only greatly absorbs interior noise to improve the comfort in the automobiles, but also has favorable flame retardance and can improve the safety performance.

Description

technical field [0001] The invention belongs to the technical field of automotive interior materials, in particular to a sound-absorbing and flame-retardant automotive interior material and a preparation method thereof. Background technique [0002] The interior materials consumed by an ordinary family car are about 20-40kg. These decorations are mainly composed of flammable textiles, fiber lining boards, polyurethane foam, artificial leather, hot-melt adhesives and other materials. , and are mainly distributed in more than forty parts such as ceilings, door linings, carpets, seats, seat belts, sound insulation felts, luggage compartment liners, and sealing filter felts. During the transportation of automobiles, due to electrical short circuit, engine failure, traffic accidents and other reasons, it is very easy to cause fire, resulting in property loss and even casualties. However, flammable automotive interior decorations tend to aggravate the degree of fire in accidents....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L55/02C08L33/12C08L29/04C08L67/02C08L1/02C08K3/30C08K3/22C08K3/32C08K3/34C08K5/3492
CPCC08K2003/2227C08K2003/3045C08K2003/323C08K2201/011C08L23/12C08L2201/02C08L2205/035C08L2205/16C08L55/02C08L33/12C08L29/04C08L67/02C08L1/02C08K3/30C08K3/22C08K3/32C08K3/346C08K5/34928
Inventor 夏兴峰
Owner JURONG FENGLING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap