Celeste blue glaze and preparation method thereof

A technology of celadon glaze and calcite, which is applied in the field of ceramic glazes, can solve problems such as the cracking of Jun porcelain, and achieve the effects of increasing opacity, high artistic value, and increasing gloss and transparency

Inactive Publication Date: 2019-03-01
禹州市神后镇永春瓷业有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the formula and process of Jun porcelain with sky blue glaze are difficult to fire into the glaze color of sky blue after rain, and the fired Jun porcelain is easy to burst during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: Azure glaze, comprising the following raw materials in parts by mass:

[0017] Yellow feldspar 48, this medicine 14, calcite 14, quartz 11, talc 5, ashes 0.4.

[0018] The preparation method of azure glaze as above, comprises the following steps:

[0019] S1: Weigh the raw materials according to the proportion, add water to the ball mill for grinding, and pass through the sieve after grinding to obtain the glaze slurry;

[0020] S2: immerse the green body in the glaze slurry by hand;

[0021] S3: Put the green body into the kiln for firing, heat at a rate of 300°C / h for 3 hours in an oxidizing atmosphere, reach 900°C, keep it for 3 hours, then control the heating rate to 55°C / h, reach 1020°C, keep it for 2 hours Control the heating rate to 110°C / h, heat to 1240°C under a reducing atmosphere, keep it for 0.5h, and then cool it naturally.

[0022] The mass ratio of raw materials, balls and water in the ball mill is 1:2:0.8, and the mesh size of the screen...

Embodiment 2

[0023] Embodiment 2: Azure glaze, comprising the following raw materials in parts by mass:

[0024] Yellow feldspar 50, this medicine 15, calcite 15, quartz 13, talc 7, ashes 0.5.

[0025] The preparation method of azure glaze as above, comprises the following steps:

[0026] S1: Weigh the raw materials according to the proportion, add water to the ball mill for grinding, and pass through the sieve after grinding to obtain the glaze slurry;

[0027] S2: immerse the green body in the glaze slurry by hand;

[0028] S3: Put the green body into the kiln for firing, heat at a rate of 300°C / h for 3 hours in an oxidizing atmosphere, reach 900°C, keep it for 3 hours, then control the heating rate to 55°C / h, reach 1020°C, keep it for 2 hours Control the heating rate to 110°C / h, heat to 1240°C under a reducing atmosphere, keep it for 0.5h, and then cool it naturally.

[0029] The mass ratio of raw materials, balls and water in the ball mill is 1:2:0.8, and the mesh size of the screen...

Embodiment 3

[0030] Embodiment 3: Azure glaze, comprising the following raw materials in parts by mass:

[0031] Yellow feldspar 51, this medicine 16, calcite 16, quartz 13, talc 8, ashes 0.6.

[0032] Described azure glaze comprises the raw material of following mass parts:

[0033] The preparation method of azure glaze as above, comprises the following steps:

[0034] S1: Weigh the raw materials according to the proportion, add water to the ball mill for grinding, and pass through the sieve after grinding to obtain the glaze slurry;

[0035] S2: immerse the green body in the glaze slurry by hand;

[0036] S3: Put the green body into the kiln for firing, heat at a rate of 300°C / h for 3 hours in an oxidizing atmosphere, reach 900°C, keep it for 3 hours, then control the heating rate to 55°C / h, reach 1020°C, keep it for 2 hours Control the heating rate to 110°C / h, heat to 1240°C in a reducing atmosphere, keep it for 0.5h, and then cool it naturally.

[0037] The mass ratio of raw materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to celeste blue glaze and a preparation method thereof. The celeste blue glaze is prepared from, by mass, 48-51 parts of melilite, 14-16 parts of drug, 14-16 parts of calcite, 11-13 parts of quartz, 5-8 parts of talc and 0.4-0.6 part of bone ash; the preparation method for the celeste blue glaze comprises the following steps that S1, the raw materials are weighed according tothe matching ratio, water is added into a ball grinder for grinding the raw materials, after grinding, the ground raw materials are sieved by a sieve, and glaze paste is obtained; S2, blank bodies are manually soaked in the glaze paste; S3, the blank bodies are placed in a kiln for firing and heated for 3 h at the 300 DEG C / h speed under an oxidizing atmosphere to 900 DEG C, after the temperatureis kept for 3 h, the heating speed is controlled to be 55 DEG C / h, the temperature reaches 1020 DEG C, after the temperature is kept for 2 h, the heating speed is controlled to be 110 DEG C / h, undera reducing atmosphere, the blank bodies are heated to 1240 DEG C, after the temperature is kept for 0.5 h, the blank bodies are cooled naturally, and the celeste blue glaze is obtained; by adopting the formula and the preparation method, the fired jun porcelain glaze color is bright and smooth, and the glaze is bright, high in artistic value, wear-resisting, solid and durable; the optical propertyof the melilite is sage green, yellow and brownness, and a thin melilite piece is colorless.

Description

technical field [0001] The invention belongs to the technical field of ceramic glazes, and in particular relates to a sky blue glaze and a preparation method thereof. Background technique [0002] Jun porcelain began in the Tang Dynasty and flourished in the Song Dynasty. It is one of the five famous porcelains in ancient China. The opalescent state of Jun glaze and the phenomenon of kiln transformation are two appearance characteristics that constitute the artistic beauty of Jun porcelain. The opalescence state refers to the beautiful azure semi-opacity state of Jun kiln glaze like green agate or opal, which not only makes Jun glaze produce a series of blue from light to dark, but also endows it with a subtle luster and elegant Texture, reducing the coquettish floating light caused by glaze vitrification. The phenomenon of kiln change means that Jun glaze melts and flows at high temperature, and the opacity and coloring colors undergo complex interlacing changes, making t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86C03C8/00
CPCC03C8/00C03C2204/04C04B41/5022C04B41/86C04B41/4535C04B41/0072
Inventor 李雪亚
Owner 禹州市神后镇永春瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com