A mold for in-mold rapid forming and quenching

A mold and entity technology, applied in the direction of forming tools, quenching devices, manufacturing tools, etc., can solve the problems of mutual influence, affecting the forming performance of sheet metal, and the mutual coupling between forming process and quenching process, and achieve small heat capacity and thin skin Effect

Active Publication Date: 2020-11-03
DALIAN UNIV OF TECH +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the problem that in the hot forming process of existing sheet metal parts, when all the forming dies are in a cold state (hot stamping) or a certain side of the die is in a cold state (cold and hot composite die forming), it is easy to appear a hot state metal plate. Due to the rapid drop in the local temperature of the billet, which affects the formability of the sheet metal, the forming process and the quenching process are coupled, interacted, and cannot be reasonably coordinated. A mold that realizes rapid forming and quenching in the mold is proposed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A mold for in-mold rapid forming and quenching
  • A mold for in-mold rapid forming and quenching
  • A mold for in-mold rapid forming and quenching

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] combine figure 1 And Fig. 2 illustrates, a kind of mold that realizes in-mold rapid prototyping and quenching, (1) forming mold comprises upper mold and lower mold, and lower mold is a traditional overall structure; The thin-walled skin is tightly wrapped on the internal solid core; (3) The shape and size of the outer surface of the thin-walled skin are the same as the shape and size of the part; (4) The surface of the internal solid core is provided with vertical ribs and mutual Connected grooves, thin-walled skins and grooves form specific channels after contact; (5) Medium inlet holes and outlet holes are provided on the internal solid core, and are connected to the channels formed by the skin and grooves.

[0039] The above-mentioned mold for realizing rapid forming and quenching in the mold, its working process is carried out according to the following steps:

[0040] Step 1. According to the material type, complexity, precision requirements, etc. of the metal she...

Embodiment 2

[0048] combine image 3 And Fig. 4 illustrates, another kind of mold that realizes rapid prototyping and quenching in the mold, (1) forming mold comprises upper mold and lower mold, and upper mold and lower mold are all composite structures; (2) upper mold and lower mold are all made of The thin-walled skin and the internal solid mold core are composed, and the thin-walled skin is tightly wrapped on the internal solid mold core; (3) the shape and size of the outer surface of the thin-walled skin are the same as the shape and size of the part; (4) the surface of the internal solid mold core is provided with Ribs and interconnected grooves, the thin-walled skin and the grooves contact to form a specific channel; (5) There are medium inlet holes and outlet holes on the internal solid mold core, which are connected to the channel formed by the skin and grooves. connect.

[0049] The working process of the above-mentioned mold for rapid forming and quenching in the mold is the sam...

Embodiment 3

[0051] Example Three: Combining figure 1 As shown in Fig. 4, a mold for realizing rapid prototyping and quenching in the mold, in step 1, the thin-walled skin in the combined mold adopts a metal sheet with good thermal conductivity, small heat capacity, high strength, and wear resistance, such as a stainless steel plate , high-temperature alloy plate or titanium alloy plate, etc., the thickness of the thin-walled skin is 0.2-0.5mm, and the thin-walled skin is in close contact with the vertical ribs of the internal solid mold core and does not deform during the contact process with the metal slab. Others are the same as the first and second embodiments.

[0052] Due to the thin wall thickness and small heat capacity of the skin, during the forming stage, when the hot metal slab contacts the skin, the temperature of the skin will rise quickly but will not conduct much away from the hot metal slab The heat will not cause the temperature of the hot metal slab to drop rapidly. Ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a die capable of achieving rapid forming and quenching therein. The die includes an upper die, a blank holder and a lower die, where the upper die is composed of an internal solid die core and a thin-walled skin. Grooves in communication with each other are disposed between the internal solid die core and the thin-walled skin. In a forming stage, the grooves are not filled or filled with a heat insulating material such as a gas; and in a quenching stage, a low-temperature medium is introduced into the grooves. The die can be used to achieve rapid forming and quenching of metal materials of different types and thicknesses.

Description

technical field [0001] The invention relates to a mold for forming metal plate parts, in particular to a mold capable of realizing rapid forming and quenching of metal plate parts in the mold. Background technique [0002] For metal sheet parts that can be strengthened by heat treatment (such as 2000 series, 6000 series, 7000 series aluminum alloy sheets, 22MnB5 boron steel sheets), heat treatment strengthening is usually required for the formed parts (for aluminum alloy sheets, solid solution quenching is first performed to form Supersaturated solid solution, and then artificial aging precipitation strengthening; for 22MnB5 boron steel plate, first heating and heat preservation to austenitize, and then rapid cooling and quenching to form martensite). However, since the sheet metal parts need to undergo multiple heating and cooling during the heat treatment process, the shape and size of the parts are easily changed due to uneven thermal expansion and contraction, thermal st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21D37/10B21D37/16C21D1/673
CPCB21D37/10B21D37/16C21D1/673B21D22/208B21D37/01B21D22/022B21D37/02B21D37/08
Inventor 苑世剑何祝斌凡晓波林艳丽王国峰亓昌
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com