Aqueous-phase preparation method for chiral metal compound nanomaterial mercury sulfide

A technology of metal compounds and nanomaterials, which is applied in the field of aqueous phase preparation of chiral metal compound nanomaterials mercury sulfide, which can solve the problems of mercury sulfide not suitable for the environment, low product purity, single particle size, etc., and achieve uniform appearance , simple operation steps and simple reaction conditions

Inactive Publication Date: 2019-03-08
HENAN NORMAL UNIV
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing nano-scale mercury sulfide often requires heating and reflux operations, and the product ha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous-phase preparation method for chiral metal compound nanomaterial mercury sulfide
  • Aqueous-phase preparation method for chiral metal compound nanomaterial mercury sulfide
  • Aqueous-phase preparation method for chiral metal compound nanomaterial mercury sulfide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] Add 62.3 mg of mercury nitrate containing 0.5 crystal water to 10 mL of deionized water, and then add 2 mL of an alkaline solution of L-cystine with a molar concentration of 0.09 mol / L. The alkaline solution of L-cystine is It is prepared by dissolving 8mL L-cystine in 1.3mL sodium hydroxide aqueous solution with molar concentration of 2mol / L, and then adding 1mL molar concentration of thioacetamide aqueous solution with 0.18mol / L, and stirring in a 38℃ water bath. For 15 hours, centrifuge at 4500 rpm, take out the supernatant, and disperse the centrifuged product in 10 mL of deionized water, and finally prepare the chiral metal compound nano-material mercury sulfide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous-phase preparation method for chiral metal compound nanomaterial mercury sulfide. The aqueous-phase preparation method includes the steps of taking a mercury salt aqueous solution and a sulfide aqueous solution as reaction raw materials, taking sulfur-containing amino acid as a chiral inducer, and reacting the three in a water bath with the temperature of 20-50 DEG C while stirring to obtain the chiral metal compound nanomaterial mercury sulfide having optical isomerism and uniform size; the chiral metal compound nanomaterial mercury sulfide can be re-dispersed in deionized water. The aqueous-phase preparation method has simple reaction conditions, is easy to operate and can be applied to mass production; the final product has high dispersibility in distilled water.

Description

technical field [0001] The invention belongs to the technical field of preparation of functional nanomaterials, and in particular relates to an aqueous phase preparation method of mercury sulfide, a chiral metal compound nanomaterial. Background technique [0002] The precipitation and dissolution of mercury sulfide (HgS) as a basic environmental chemical process plays a key role in the speciation distribution, migration, reactivity and corresponding migration and transformation (including methylation / demethylation) of mercury in environmental media , is also a key process to control mercury toxicity. Therefore, studying the environmental behavior of mercury sulfide is an important way to solve mercury pollution. Since the particle size of mercury sulfide in the environment is mostly on the submicron scale, it is necessary to use submicron mercury sulfide to simulate the reaction and form changes of mercury sulfide in the real environment, but currently only granular mercur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G13/00B82Y30/00
CPCB82Y30/00C01G13/00
Inventor 杨嬅嬿王俊玉王萌杨守宁杨林
Owner HENAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap