Preparation process of high-temperature-resistant and impact-resistant acrylonitrile butadiene styrene (ABS) particles

A preparation process and impact resistance technology, applied in the field of plastics, can solve the problems of lack of high temperature resistance, insufficient application force, low ductility and lack of impact resistance, etc., to achieve high toughness, good impact resistance, and good heat resistance The effect of high temperature resistance

Inactive Publication Date: 2019-03-12
广东正品智慧科技股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the plastic industry is widely used in all walks of life. For the common plastic ABS on the market, most of them lack good high temperature and high heat resistance, low ductility and no impact resistance. They can only be used as conventional engineering plastics. For special projects such as electronics Insufficient engineering application capabilities such as electrical appliances and aerospace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The following preferred examples illustrate the implementation of the present invention.

[0016] A high-temperature-resistant and impact-resistant granular ABS preparation process, characterized in that it comprises the following raw materials in parts by weight: 50-70 parts of ABS resin, 5-15 parts of SBS thermoplastic elastomer, 30-40 parts of PPS, 2 parts of foaming agent, 10 parts of anti-shock powder, 1 part of dispersant, 10 parts of toughening agent and 20 parts of coupling agent, described coupling agent comprises the mixture of polylactic acid, acrylonitrile-butadiene-styrene and acrylic oligomer , described toughening agent comprises the mixture of methyl methacrylate-butadiene and styrene terpolymer (MBS), and described styrene terpolymer (MBS) is made of 42 parts of styrene-butadiene latex (according to dry weight), 28 parts of styrene, and 30 parts of methyl methacrylate are polymerized in water, and the impact-resistant powder includes a mixture of modifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-temperature-resistant and impact-resistant acrylonitrile butadiene styrene (ABS) particles, which are prepared from the following raw materials in parts by weight: 50-70 parts of ABS resin, 5-15 parts of styrene-butadiene-styrene block copolymer (SBS) thermoplastic elastomer, 30-40 parts of polyphenylene sulfide (PPS), 2 parts of a foaming agent, 10 parts of impact-resistant powder, 1 part of a dispersing agent, 10 parts of a toughening agent and 20 parts of a coupling agent, wherein the coupling agent is prepared from a mixture of polylactic acid, acrylonitrile-butadiene-styrene and acrylic oligomers, the toughening agent is prepared from a mixture of methyl methacrylate-butadiene and styrene terpolymer (MBS), the MBS is prepared by polymerizing 42 parts (by dry mass) of styrene-butadiene latex, 28 parts of styrene and 30 parts methyl methacrylate in water, and the impact-resistant powder is prepared from a mixture of modified thermoplastic polyurethane (TPU) and polymethyl methacrylate (PMMA). The ABS particles produced by the process are obviously superior to the special engineering plastics commonly available on the market, and have very good impactresistance and high toughness while having good heat resistance and high temperature resistance, thus being suitable for a wider range of characteristics.

Description

technical field [0001] The invention relates to the field of plastics, in particular to a process for preparing high-temperature-resistant and impact-resistant granule ABS. Background technique [0002] At present, the plastic industry is widely used in all walks of life. For the common plastic ABS on the market, most of them lack good high temperature and high heat resistance, low ductility and no impact resistance. They can only be used as conventional engineering plastics. For special projects such as electronics The application of electrical appliances, aerospace and other engineering applications is insufficient. Contents of the invention [0003] The object of the present invention is to provide a high-temperature-resistant and impact-resistant particle ABS preparation process to solve the problems raised in the above-mentioned background technology. [0004] To achieve the above object, the present invention provides the following technical solutions: [0005] A p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L53/02C08L81/02C08L51/04C08K13/02C08K5/09C08K3/04C08J9/10
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/103C08J2203/04C08J2355/02C08J2451/04C08J2453/02C08J2481/02
Inventor 陈建国
Owner 广东正品智慧科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products