Production method for high-strength cement

A high-strength cement and production method technology, applied in the field of cement, can solve the problems of metal components susceptible to electrochemical corrosion, limited cement adhesion and strength, and insufficient connection of building products, so as to increase cement adsorption and increase strength , the effect of stable connection

Inactive Publication Date: 2019-03-29
TONGLING SHANGFENG CEMENT CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the cement produced by them has limited adhesion and strength, and during long-term use, metal components such as steel bars in cement products are susceptible to electrochemical corrosion, which will reduce the service life of cement products. In some specific buildings In the place of use, when the cement is not bonded enough, the connection between the building products will not be strong enough, and it will easily fall off the wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The invention provides a technical solution: a high-strength cement comprising the following components by weight:

[0024] 20 parts of sand, 16 parts of coal gangue, 55 parts of desulfurized gypsum, 1.2 parts of ferrous ion compound, 6 parts of modified aramid fiber-carbon fiber, 3 parts of metal wire, 1.2 parts of defoamer, 15 parts of deionized water, and 2 parts of reinforcing agent 3.5 parts and 3.5 parts of adhesive.

[0025] A method for producing high-strength cement, comprising the steps of:

[0026] S1: Take raw materials, weigh all the required raw materials, take them according to the predetermined ratio, and store them;

[0027] S2: Make A mixture, dehydrate the desulfurized gypsum to generate hemihydrate gypsum, crush and grind the coal gangue to a fineness of 0.25 mm, then add sand, coal gangue powder, ferrous ion compound, hemihydrate gypsum and deionized water and stir Mix and stir in the container, the stirring time is 30-45min, add the defoamer duri...

Embodiment 2

[0034] The invention provides a technical solution: a high-strength cement comprising the following components by weight:

[0035] 20 parts of sand, 16 parts of coal gangue, 55 parts of desulfurized gypsum, 1.2 parts of ferrous ion compound, 7.5 parts of modified aramid-carbon fiber, 3 parts of metal wire, 1.2 parts of defoamer, 15 parts of deionized water, and 2 parts of reinforcing agent 3.5 parts and 3.5 parts of adhesive.

[0036] A method for producing high-strength cement, comprising the steps of:

[0037] S1: Take raw materials, weigh all the required raw materials, take them according to the predetermined ratio, and store them;

[0038] S2: Make A mixture, dehydrate the desulfurized gypsum to generate hemihydrate gypsum, crush and grind the coal gangue to a fineness of 0.25 mm, then add sand, coal gangue powder, ferrous ion compound, hemihydrate gypsum and deionized water and stir Mix and stir in the container, the stirring time is 30-45min, add the defoamer during t...

Embodiment 3

[0045] The invention provides a technical solution: a high-strength cement comprising the following components by weight:

[0046] 20 parts of sand, 16 parts of coal gangue, 55 parts of desulfurized gypsum, 1.2 parts of ferrous ion compound, 6 parts of modified aramid fiber-carbon fiber, 3 parts of metal wire, 1.2 parts of defoamer, 15 parts of deionized water, and 2 parts of reinforcing agent 4.5 parts and 4.5 parts of adhesive.

[0047] A method for producing high-strength cement, comprising the steps of:

[0048] S1: Take raw materials, weigh all the required raw materials, take them according to the predetermined ratio, and store them;

[0049] S2: Make A mixture, dehydrate the desulfurized gypsum to generate hemihydrate gypsum, crush and grind the coal gangue to a fineness of 0.25 mm, then add sand, coal gangue powder, ferrous ion compound, hemihydrate gypsum and deionized water and stir Mix and stir in the container, the stirring time is 30-45min, add the defoamer duri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method for high-strength cement, and belongs to the field of cement. The high-strength cement is prepared from the following components in parts by weight: 20-30 parts of sandy soil, 15-30 parts of coal gangue, 50-65 parts of flue gas desulfurization gypsum, 1-3 parts of ferrous ionic compounds, 5-10 parts of modified aramid fiber-carbon fiber, 2-5 parts of metal wires, 1-3 parts of a defoaming agent, 10-25 parts of deionized water, 1-4.5 parts of a reinforcing agent and 3-6 parts of an adhesive. The production method has the advantages of being more scientific and reasonable, the strength of a cement finished product can be well improved, the phenomenon that steel bars is subjected to electrochemical corrosion can be well avoided, the service life of the cement product is effectively prolonged, the adhesive force of the cement finished product is effectively improved, the adsorbability of the cement can be well improved, and the connection among building products is more stable.

Description

technical field [0001] The invention relates to the field of cement, in particular to a production method of high-strength cement. Background technique [0002] Cement is a powdery hydraulic inorganic gelling material. Add water and stir to form a slurry, which can be hardened in air or better in water, and can firmly bond sand, stone and other materials together. The mixture of early lime and volcanic ash is very similar to modern lime pozzolanic cement. It glues concrete made of gravel. After hardening, it not only has high strength, but also can resist the erosion of fresh water or salt water. For a long time, as an important cementitious material, it has been widely used in civil engineering, water conservancy, national defense and other projects. There are many existing methods for producing cement. [0003] However, the cement produced by them has limited adhesion and strength, and during long-term use, metal components such as steel bars in cement products are susce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/24C04B7/38C04B7/44C04B7/48
CPCC04B7/24C04B7/38C04B7/44C04B7/48Y02P40/10
Inventor 叶挺钢徐瞒张茂鹍王东
Owner TONGLING SHANGFENG CEMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap