Preparation method for rubber sheet material glue

A glue and board technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of rubber sheet corrosion, low bonding strength, low heat resistance, etc. High bonding strength and high heat resistance

Inactive Publication Date: 2019-03-29
贵州恒力源林业科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the existing rubber sheet is green and environmentally friendly, non-toxic and harmless, waterproof and non-slip, the rubber sheet becomes astringent when exposed to water, can be waterproof and non-slip, and is light in weight. It can be installed immediately with glue, and the wear-resistant layer on the surface can withstand a lot of trampling , long life, impact resistance, elasticity, good sound absorption, comfortable feet, acid and alkali resistance, corrosion resistance, can withstand harsh environmental tests, good insulation and flame retardancy, non-flammable, non-combustible, no deformation when exposed to water, can effectively inhibit Harmful bacteria growth and other advantages, so the rubber sheet is widely used now, but when the rubber sheet is connected with glue, the glue is prone to aging, easy to corrode the rubber sheet, and easy to delaminate, low bonding strength, heat resistance low, little elasticity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1 of the present invention: a rubber sheet glue, the glue is made of the raw materials with the following weight composition ratio; the raw materials are: 25 parts of polymer resin, 35 parts of bonding resin, 4 parts of styrene, 2 parts of silicone rubber 20 parts of strengthening agent, 0.05 parts of sodium styrene sulfonate, 20 parts of black glue, 7 parts of anti-aging agent, 4 parts of softening oil, 3 parts of formic acid, and 35 parts of rubber solvent.

[0016] The processing method of this glue comprises the following steps:

[0017] A, in the reaction kettle, add 20% rubber solvent, black glue and softening oil successively, then heat the reaction kettle, the heating temperature is 90 degrees Celsius, and keep it warm for 1 hour to obtain product a;

[0018] B. In another reaction kettle, add the remaining rubber solvent, polymer resin, bonding resin, styrene, silicone rubber, reinforcing agent, softening oil, and then heat the reaction kettle for 1 ...

Embodiment 2

[0020] Embodiment 2 of the present invention: a rubber sheet glue, which is made of the following raw materials by weight and composition ratio; the raw materials are: 20 parts of polymer resin, 30 parts of bonding resin, 4 parts of styrene, and 2 parts of silicone rubber 15 parts of strengthening agent, 0.02 parts of sodium styrene sulfonate, 25 parts of black glue, 6 parts of anti-aging agent, 3 parts of softening oil, 3 parts of formic acid, and 40 parts of rubber solvent.

[0021] The processing method of this glue comprises the following steps:

[0022] A, in the reaction kettle, add 25% rubber solvent, black glue and softening oil successively, then heat the reaction kettle, the heating temperature is 95 degrees Celsius, and keep warm for 1.5 hours to obtain the a product;

[0023] B. In another reaction kettle, add the remaining rubber solvent, polymer resin, bonding resin, styrene, silicone rubber, reinforcing agent, softening oil, and then heat the reaction kettle for...

Embodiment 3

[0025] Embodiment 3 of the present invention: a rubber sheet glue, which is made of the following raw materials by weight and composition ratio; the raw materials are: 30 parts of polymer resin, 40 parts of bonding resin, 4 parts of styrene, and 3 parts of silicone rubber 20 parts, strengthening agent 20 parts, 0.07 parts of sodium styrene sulfonate, 30 parts of black glue, 8 parts of anti-aging agent, 4 parts of softening oil, 4 parts of formic acid, 30 parts of rubber solvent.

[0026] The processing method of this glue comprises the following steps:

[0027] A, in the reaction kettle, add 30% rubber solvent, black glue and softening oil successively, then heat the reaction kettle, the heating temperature is 100 degrees Celsius, and keep warm for 1 hour to obtain product a;

[0028] B. In another reaction kettle, add the remaining rubber solvent, polymer resin, bonding resin, styrene, silicone rubber, reinforcing agent, softening oil, and then heat the reaction kettle for 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for a rubber sheet material glue. The glue is prepared from the following raw materials, by weight component ratio: 20-30 parts of polymer resin, 30-40 parts of adhesive resin, 3-5 parts of styrene, 2-3 parts of silicone rubber, 15-20 parts of a reinforcing agent, 0.02-0.1 part of sodium p-styrenesulfonate, 20-30 parts of black glue, 6-10 parts of an anti-aging agent, 2-5 parts of softening oil, 1-4 parts of formic acid, and 30-40 parts of a rubber solvent. The glue is the glue specially used for rubber sheets; and the glue has beneficial effects ofbeing not easy to age and layer, small in rubber sheet corrosion, high in bonding intensity and heat resistance, and large in elasticity.

Description

technical field [0001] The invention relates to a preparation method of glue, in particular to a preparation method of rubber plate glue. Background technique [0002] At present, the existing rubber sheet is green and environmentally friendly, non-toxic and harmless, waterproof and non-slip, the rubber sheet becomes astringent when exposed to water, can be waterproof and non-slip, and is light in weight. It can be installed immediately with glue, and the wear-resistant layer on the surface can withstand a lot of trampling , long life, impact resistance, elasticity, good sound absorption, comfortable feet, acid and alkali resistance, corrosion resistance, can withstand harsh environmental tests, good insulation and flame retardancy, non-flammable, non-combustible, no deformation when exposed to water, can effectively inhibit Harmful bacteria growth and other advantages, so the rubber sheet is widely used now, but when the rubber sheet is connected with glue, the glue is pron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J201/00C09J11/06C09J11/08
CPCC09J201/00C08L2201/08C08L2205/035C09J11/06C09J11/08C08L101/00C08L83/04C08K5/42
Inventor 林建
Owner 贵州恒力源林业科技有限公司