Fiber spinning solution
A technology of spinning solution and fiber, which is applied in the fields of fiber chemical characteristics, cellulose/protein conjugated rayon, rayon manufacturing, etc. It can solve the problems of not being able to achieve lightness and warmth, and achieve good antibacterial and antibacterial effects, elasticity Good, long-lasting effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A fiber spinning solution, consisting of the following raw materials in parts by weight: 10 parts of bamboo charcoal fiber, 14 parts of viscose fiber, 16 parts of polyester fiber, 10 parts of nano-ceramic powder, and 10 parts by mass of sodium hydroxide solution 30 parts and 40 parts of 15% urea solution in parts by mass.
[0025] Dissolve the bamboo charcoal fiber, viscose fiber and polyester fiber of the above-mentioned parts by weight in the mixed solution of sodium hydroxide and urea at -13°C, and then add the nano-ceramic powder of the above-mentioned parts by weight to it after fully mixing, and continue to stir Mix evenly, prepare the above-mentioned fiber spinning solution, and finally use the wet spinning method to spin into fiber filaments. The fiber filaments prepared from the fiber spinning solution have good antibacterial and antibacterial effects, and at the same time have strong warmth retention properties.
[0026] Wherein, the nano-ceramic powder is at...
Embodiment 2
[0028] A fiber spinning solution, consisting of the following raw materials in parts by weight: 20 parts of bamboo charcoal fiber, 18 parts of viscose fiber, 20 parts of polyester fiber, 12 parts of nano-ceramic powder, and 10 parts by mass of sodium hydroxide solution 50 parts and 60 parts of 15% urea solution in parts by mass.
[0029] Dissolve the bamboo charcoal fiber, viscose fiber and polyester fiber of the above-mentioned parts by weight in the mixed solution of sodium hydroxide and urea at -11°C, after fully mixing, add the nano-ceramic powder of the above-mentioned parts by weight to it, and continue to stir Mix evenly, prepare the above-mentioned fiber spinning solution, and finally use the wet spinning method to spin into fiber filaments. The fiber filaments prepared from the fiber spinning solution have good antibacterial and antibacterial effects, and at the same time have strong warmth retention properties.
[0030] Wherein, the nano-ceramic powder is at least o...
Embodiment 3
[0032] A fiber spinning solution, consisting of the following raw materials in parts by weight: 15 parts of bamboo charcoal fiber, 16 parts of viscose fiber, 18 parts of polyester fiber, 11 parts of nano-ceramic powder, and 10 parts by mass of sodium hydroxide solution 40 parts and 50 parts of 15% urea solution in parts by mass.
[0033] Dissolve the bamboo charcoal fiber, viscose fiber and polyester fiber of the above-mentioned parts by weight in the mixed solution of sodium hydroxide and urea at -12°C, after fully mixing, add the nano-ceramic powder of the above-mentioned parts by weight to it, and continue to stir Mix evenly, prepare the above-mentioned fiber spinning solution, and finally use the wet spinning method to spin into fiber filaments. The fiber filaments prepared from the fiber spinning solution have good antibacterial and antibacterial effects, and at the same time have strong warmth retention properties.
[0034] Wherein, the nano-ceramic powder is at least o...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |