Preparation method of antibacterial medical non-woven fabric

A technology of non-woven fabrics and polymers, applied in the direction of melt spinning, non-woven fabrics, textiles and papermaking, etc., can solve the problems of poor antibacterial ability, unsuitable for ordinary community hospitals and rural health centers, and high cost, and achieve improvement Antimicrobial ability, enhanced toughness and strength, low cost effect

Inactive Publication Date: 2019-03-29
桐城市鸿江包装有限公司
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The expansion of the application field of non-woven fabrics, non-woven fabrics are widely used in the medical field, but although the current non-woven fabric wall coverings are relatively strong, they generally have poor antibacterial ability or high cost, so they are not suitable for ordinary community hospitals. or used by rural health centers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antibacterial medical non-woven fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] S1: The fine fiber polymer includes low-melting chemical fiber, carpenter fiber and wood pulp, low-melting chemical fiber: wood pulp fiber: carpenter = 5:3:1, the mixture of fine fiber polymer and binder fiber is made by a large screw High-temperature melt extrusion, the heating temperature is 260 ° C, to obtain polymer A in a molten state;

[0018] S2: Spinning polymer A through an extruder at a pressure of 4.8 MPa, stretching the filaments through a stretcher to form a fiber drawing B, and guiding it into the soaking liquid for 4 hours, and then guiding it to air-laid On the machine, the components of the soaking solution are as follows: 30 parts of astragalus extract, 20 parts of acrylate, 0.01 part of triclosan, and 30 parts of ethylene glycol;

[0019] S3: When the three-layer fiber drawing material B is stacked on the web forming machine, guide the laminate to the hot rolling mill for hot rolling. During hot rolling, the surface of the fiber drawing material is ev...

Embodiment 2

[0022] S1: The fine fiber polymer includes low-melting chemical fiber, carpenter fiber and wood pulp, low-melting chemical fiber: wood pulp fiber: carpenter = 5:3:1, the mixture of fine fiber polymer and binder fiber is made by a large screw High-temperature melt extrusion, the heating temperature is 280°C, to obtain polymer A in a molten state;

[0023] S2: Spinning polymer A through an extruder at a pressure of 5.3MPa, stretching the filaments through a stretcher to form a fiber drawing B, and guiding it into the soaking liquid for 8 hours of soaking, and then guiding it to air-laid On the machine, the components of the soaking solution are as follows: 40 parts of astragalus extract, 40 parts of acrylate, 0.02 part of triclosan, and 40 parts of ethylene glycol;

[0024] S3: When the four-layer fiber drawing material B is stacked on the web forming machine, guide the laminated material to the hot rolling mill for hot rolling. During hot rolling, the surface of the fiber drawi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an antibacterial medical non-woven fabric, comprising the following steps: S1, melt-extruding a mixture of a fine fiber polymer and binder fibers by a large screw at a high temperature of 260-280 DEG C to obtain a molten polymer A; S2, spinning the polymer A by an extruder under the pressure of 4.8-5.3 MPa, stretching the spun fibers by a stretcher to form a fiber stretching material B, guiding to a soaking solution for soaking for 4-8 h, and then guiding to a lapper; and S3, when three or four layers of fiber stretching material B are laminatedon the lapper, guiding a laminate to a hot rolling mill for hot rolling at 160-180 DEG C under 4 MPa, uniformly spraying resin powder to the surface of the fiber stretching material during hot rollingto obtain a non-woven fabric, and winding the non-woven fabric. On the basis of ensuring toughness, the non-woven fabric has excellent antibacterial ability and low cost, and is particularly suitablefor small hospitals.

Description

technical field [0001] The invention relates to the field of non-woven fabric preparation, in particular to a preparation method of antibacterial medical non-woven fabric. Background technique [0002] Non-woven fabric is a kind of non-woven fabric, which directly uses polymer chips, short fibers or filaments to form fibers through airflow or machinery, and then undergoes hydroentanglement, needle punching, or hot rolling reinforcement, and finally finishes finishing Formed non-woven fabric. A new type of fiber product with soft, breathable and planar structure. The advantage is that it does not produce lint, is strong, durable, and silky soft. It is also a kind of reinforcing material, and it also has a cotton feel. Compared with cotton fabrics, non-woven fabrics Cloth bags are easy to form and inexpensive to make. [0003] The expansion of the application field of non-woven fabrics, non-woven fabrics are widely used in the medical field, but although the current non-wove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/732D04H1/587D04H1/541D04H1/542D01D5/098
CPCD01D5/098D04H1/541D04H1/542D04H1/587D04H1/732D10B2401/13D10B2509/00
Inventor 李涛程文斌朱扬刘先银
Owner 桐城市鸿江包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More