Mesoporous titania-silica oxide composite material, preparation method therefor and application of mesoporous titania-silica oxide composite material

A technology of mesoporous titanium oxide and composite materials, applied in catalyst activation/preparation, chemical instruments and methods, separation methods, etc., can solve the problems of small specific surface area, low photocatalytic activity, and high electron-hole binding ability

Pending Publication Date: 2019-04-12
CHONGQING TECH & BUSINESS UNIV
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a mesoporous titanium oxide-silicon oxide composite material and its preparation method and application, to solv

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mesoporous titania-silica oxide composite material, preparation method therefor and application of mesoporous titania-silica oxide composite material
  • Mesoporous titania-silica oxide composite material, preparation method therefor and application of mesoporous titania-silica oxide composite material
  • Mesoporous titania-silica oxide composite material, preparation method therefor and application of mesoporous titania-silica oxide composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A mesoporous titanium oxide-silicon oxide composite material with a pore diameter of 9.2-10.6nm and a specific surface area of ​​257-356m 2 / g, the volume ratio of the anatase phase in the titanium oxide species to the total titanium oxide species is 93.2-99.5%.

[0036] The invention discloses a method for preparing the above-mentioned mesoporous titanium oxide-silicon oxide composite material, which specifically includes the following steps:

[0037] (1) Add 5.1g of P123 into 180ml of 1.0M HCl, stir and dissolve at room temperature, and after equilibrating at 35°C for 30min, add 0.06g of NH 4 F;

[0038] (2) After pre-mixing 30 g of n-nonane, 8 g of ethyl orthosilicate, and 12 g of n-butyl titanate, they were added to the reaction solution obtained in step (2), and then hydrolyzed at 35° C. for 24 hours;

[0039] (3) Transfer the reaction solution obtained in step (2) to a hydrothermal kettle for hydrothermal treatment at 120° C. for 24 hours;

[0040] (4) Filter t...

Embodiment 2-5 and comparative example 6-7

[0049] The calcination temperature of Examples 1-5 is controlled, and the calcination temperature and catalytic effect of each embodiment are shown in Table 1 below.

[0050] Table 1

[0051]

[0052] in conclusion:

[0053] (1) from figure 1 From the transmission electron microscope (TEM) image of the composite material obtained in Example 1 shown in , it can be found that titanium oxide particles in the material obtained in Example 1 are uniformly dispersed in silicon oxide. The size of titanium oxide particles is relatively uniform, about 5nm×10nm;

[0054] (2) It can be drawn from Examples 1-3 that the present invention synthesizes a kind of mesoporous titanium oxide- Silicon oxide composite material. The pore diameter of these materials is 9.2-10.6nm, which is a typical mesoporous material; the specific surface area is 257-356m 2 / g, significantly exceeding the specific surface area of ​​pure titanium oxide material.

[0055] (3) from figure 2 As shown in the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of inorganic compounds and particularly discloses a mesoporous titania-silica oxide composite material. The mesoporous titania-silica oxide composite material has the pore size of 9.2nm to 10.6nm and the specific surface area of 350m<2>/g to 460m<2>/g, and an anatase crystal phase in titania species accounts for 93.2% to 99.5% the total titania species.The invention further discloses a preparation method for the mesoporous titania-silica oxide composite material and an application of the mesoporous titania-silica oxide composite material in catalysis of NO removal under visible light with the wavelength greater than 420nm. The mesoporous titania-silica oxide composite material has relatively high photocatalytic activity.

Description

technical field [0001] The application of the present invention belongs to the technical field of inorganic compounds, and specifically discloses a mesoporous titanium oxide-silicon oxide composite material and its preparation method and application. Background technique [0002] Titanium oxide material is a semiconductor photocatalytic material that has been widely valued. It has the advantages of non-toxicity, low price, and good oxidation resistance. It is widely used in the photocatalytic elimination of pollutants in gases and water. However, pure titanium oxide materials have a relatively high electron-hole combining ability, which is detrimental to the photocatalytic activity. In addition, the specific surface area of ​​pure titanium oxide materials is relatively small, generally only up to 10-50m 2 / g, limiting the improvement of its catalytic performance. The 100-200m can be achieved by making titanium oxide into nanotubes and other special morphology materials or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J21/14B01J37/00B01D53/86B01D53/56B01J35/00
CPCB01D53/8628B01J21/14B01J35/004B01J37/00
Inventor 张海东申渝陈佳熊昆唐源桃
Owner CHONGQING TECH & BUSINESS UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap