Anti-mud polycarboxylate water reducer as well as preparation method and application thereof

A technology of polycarboxylic acid and water-reducing agent, applied in the field of building admixtures, can solve the problems of affecting the use effect of water-reducing agent and concrete strength, inconvenient use of natural zeolite powder and water-reducing agent, and expensive vinyl cationic monomers, etc. , to achieve the effect of increasing water reduction effect, good binding force and effective coating

Active Publication Date: 2019-04-12
詹烨
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The powder and sand materials used in the concrete production process will contain a certain amount of soil and various inorganic salts, such as sulfate, sulfite, etc., these soil and inorganic salts will be adsorbed to the surface of the cement, and polycarboxylic acid Adsorption produces competition, which seriously affects the use effect of water reducing agent and concrete strength
CN101798197A uses compounding method to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] (1) Preparation of hydroxy silicone oil modified polyether: in a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 50 parts of the chemical structure of HO-Si(CH 3 ) 2 O{Si(CH 3 ) 2 O} 3.2 Si(CH 3 ) 2 -OH hydroxy silicone oil, 100 parts of 3-methyl-3-butene-1-polyoxyethylene ether and 1 part of KRA-1, stir, and pass in nitrogen, raise the temperature to 100°C, and react at a constant temperature for 2 hours. After the reaction, it is cooled to 60° C. and discharged to obtain hydroxy silicone oil modified polyether 1.

[0032] (2) Preparation of esterified monomer: in a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 100 parts of polyethylene glycol-200, 200 parts of 4,4-stilbene dicarboxylic acid, 6 parts of p-toluenesulfonic acid, 1 part of hydroquinone and 0.5 part of hydroquinone were stirred, and nitrogen was passed through, the temperature was raised to 90°C, and t...

Example Embodiment

[0034] Example 2

[0035] (1) Preparation of hydroxy silicone oil modified polyether: In a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 40 parts of the chemical structure of HO-Si(CH 3 ) 2 O{Si(CH 3 ) 2 O} 20.5 Si(CH 3 ) 2 -OH hydroxy silicone oil, 100 parts of allyl polyoxyethylene ether and 2 parts of KRA-2, stir, blow in nitrogen, raise the temperature to 110°C, and react at a constant temperature for 3 hours. After the reaction, it is cooled to 60°C and discharged to obtain hydroxy silicone oil modified polyether 2.

[0036] (2) Preparation of esterified monomer: In a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 100 parts of polyethylene glycol-400, 180 parts of 4,4-stilbene dicarboxylic acid, 8 parts of p-toluenesulfonic acid, 1.5 parts of hydroquinone and 0.75 parts of hydroquinone were stirred, and nitrogen was passed through, the temperature was raised to 80° C., and the reaction...

Example Embodiment

[0038] Example 3

[0039] (1) Preparation of hydroxy silicone oil modified polyether: In a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 30 parts of the chemical structure of HO-Si(CH 3 ) 2 O{Si(CH 3 ) 2 O} 6.8 Si(CH 3 ) 2 -OH hydroxy silicone oil, 100 parts of 2-methylallyl polyoxyethylene ether and 0.5 parts of platinum supported on a supported catalyst on a silica solid carrier, stirring, and blowing in nitrogen, the temperature is raised to 100°C , Constant temperature reaction for 2h. After the reaction, it was cooled to 60°C and discharged to obtain hydroxy silicone oil modified polyether 3.

[0040] (2) Preparation of esterified monomer: in a container equipped with a thermometer, agitator, nitrogen gas pipe and reflux condenser, add 100 parts of polyethylene glycol-600, 220 parts of 4,4-stilbene dicarboxylic acid, 10 parts of p-toluenesulfonic acid, 2 parts of hydroquinone and 1 part of hydroquinone were subjected to esterific...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of building additives, and relates to an anti-mud polycarboxylate water reducer as well as a preparation method and application thereof. A synthetic product of an unsaturated polyether monomer and hydroxyl silicone oil is used for preparing a polycarboxylate water reducer, a siloxane structure is introduced into the end of the branched chain of the polycarboxylate water reducer molecule, the siloxane structure enables the polycarboxylate water reducer to have stronger resistance to clay, and the steric hindrance effect of the branched chains of themolecule is enhanced; secondly, an esterification product of polyethylene glycol and 4,4-stilbene dicarboxylic acid is introduced, the structure of the benzene ring enables the the branched chains ofthe molecule of the polycarboxylate water reducer to have a steric hindrance effect, and by slow condensation hydrolysis under an alkaline condition, the anti-mud and dispersing retention performancesof the obtained polycarboxylate water reducer are good.

Description

technical field [0001] The invention belongs to the technical field of building admixtures, and in particular relates to a mud-resistant polycarboxylate water reducer, a preparation method and an application. Background technique [0002] The polycarboxylate superplasticizer is more sensitive to the clay content of the aggregate, mainly manifested in a severe decrease in the water reducing and dispersing ability of the polycarboxylate superplasticizer, poor slump retention effect, and a decrease in the strength of hardened concrete. In the case of high aggregate mud content, simply increasing the amount of polycarboxylate-based superplasticizers cannot solve the problems of water-reducing rate and slump retention. An important reason for scale promotion. [0003] The powder and sand materials used in the concrete production process will contain a certain amount of soil and various inorganic salts, such as sulfate, sulfite, etc., these soil and inorganic salts will be adsorb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/16C08F283/12C08F220/06C08F222/02C08G77/46C08G63/676C08G63/91C04B103/30
CPCC04B24/165C04B2103/302C08F283/124C08G63/676C08G63/918C08G77/46C08F220/06C08F222/02
Inventor 詹烨
Owner 詹烨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap