Wear-resistance and heat-resistance functional ceramic pot and preparing technology thereof

A technology of functional ceramics and ceramic pots, which is applied in the production of ceramic materials, clay products, and other household utensils, etc. It can solve the problems of ceramic pot damage, glaze layer thinning, cracking, etc., to increase stability, increase density, improve The effect of stickiness

Inactive Publication Date: 2019-04-12
FUJIAN HUAXIA VAJRA TECH CO LTD
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, when the ceramic pot is used to cook the ingredients, the ingredients will continue to roll in different degrees in the soup, which will cause slight friction on the ceramic pot. Over time, the excessive friction of the ceramic pot will cause it to produce The thinning, cracking or even falling off of the glaze layer will cause damage to the ceramic pot. Therefore, it is necessary to provide a functional ceramic pot with wear resistance and heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistance and heat-resistance functional ceramic pot and preparing technology thereof
  • Wear-resistance and heat-resistance functional ceramic pot and preparing technology thereof
  • Wear-resistance and heat-resistance functional ceramic pot and preparing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment provides a wear-resistant and heat-resistant functional ceramic pot, including a green body and a glaze layer applied on the green body. The green body is made of the following raw materials in parts by weight: 35 parts of kaolin, 35 parts of waste ceramics, 25 parts of zircon powder, 10 parts of sepiolite powder, 20 parts of activated alumina with a particle size of 200 microns, and 8 parts of silica gel powder; the glaze layer is made of the following raw materials in parts by weight: 10 parts of kaolin, 10 parts of mica powder , 6 parts of silicon dioxide with a particle size of 3 microns, 10 parts of silica gel powder, 5 parts of zircon powder, 8 parts of bone meal, 8 parts of carbon fiber powder, and 3 parts of iron oxide red pigment.

[0027] This embodiment also provides a preparation process for this kind of wear-resistant and heat-resistant functional ceramic pot, including the following steps:

[0028] (1), take each raw material respectively a...

Embodiment 2

[0036] This embodiment provides a wear-resistant and heat-resistant functional ceramic pot, including a green body and a glaze layer applied on the green body. The green body is made of the following raw materials in parts by weight: 40 parts of kaolin, 37 parts of waste ceramics, 27 parts of zircon powder, 10 parts of sepiolite powder, 22 parts of activated alumina with a particle size of 300 microns, and 10 parts of silica gel powder; the glaze layer is made of the following raw materials in parts by weight: 15 parts of kaolin, 12 parts of mica powder , 8 parts of silicon dioxide with a particle size of 5 microns, 10 parts of silica gel powder, 7 parts of zircon powder, 8 parts of bone meal, 10 parts of carbon fiber powder, and 7 parts of wrapped red pigment for glaze.

[0037] This embodiment also provides a preparation process for this kind of wear-resistant and heat-resistant functional ceramic pot, including the following steps:

[0038] (1), take each raw material respe...

Embodiment 3

[0046] This embodiment provides a wear-resistant and heat-resistant functional ceramic pot, including a green body and a glaze layer applied on the green body. The green body is made of the following raw materials in parts by weight: 45 parts of kaolin, 40 parts of waste ceramics, 30 parts of zircon powder, 12 parts of sepiolite powder, 25 parts of activated alumina, and 10 parts of silica gel powder; the glaze layer is made of the following raw materials in parts by weight: 17 parts of kaolin, 12 parts of mica powder, and a particle size of 1 micron 10 parts of silicon dioxide, 12 parts of silica gel powder, 7 parts of zircon powder, 10 parts of bone meal, 10 parts of carbon fiber powder, and 9 parts of white ceramic pigment.

[0047] This embodiment also provides a preparation process for this kind of wear-resistant and heat-resistant functional ceramic pot, including the following steps:

[0048] (1), take each raw material respectively according to parts by weight, for sub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a wear-resistance and heat-resistance functional ceramic pot. The wear-resistance and heat-resistance functional ceramic pot comprises a blank and an enamel layer applied to theblank; the blank is prepared from, by weight, 35-50 parts of kaolin, 35-50 parts of waste ceramic, 25-35 parts of zircon powder, 10-15 parts of sepiolite powder, 20-30 parts of activated aluminum oxide and 8-12 parts of silica gel powder; the enamel layer is prepared from, by weight, 10-20 parts of kaolin, 10-15 parts of mica powder, 6-12 parts of silicon dioxide, 10-15 parts of silica gel powder, 5-10 parts of zircon powder, 8-14 parts of bone meal, 8-12 parts of carbon fiber powder and 3-15 parts of pigment. The ceramic pot is smooth and bright in appearance, quick in heat conduction, goodin thermal insulation, resistant to wear and corrosion, and free of toxicity or pollution.

Description

technical field [0001] The invention belongs to the technical field of daily-use ceramic products, and in particular relates to a wear-resistant and heat-resistant functional ceramic pot and a preparation process thereof. Background technique [0002] When using a ceramic pot to make soup, it can ensure a constant temperature environment in the pot, which can lock the nutrients in the ingredients and prevent them from being lost, thereby ensuring the umami taste of the soup. Therefore, using a ceramic pot to make soup, especially soup medicine, can To a large extent, its deliciousness is guaranteed and its nutrition is maintained. Because the ceramic fort is mainly used to cook the ingredients for a long time, it needs to have high thermal stability, so as to ensure that it can withstand high temperature and not crack during the continuous heating process. It also needs to have high thermal insulation performance, so that The heat is accumulated in the pot for a long time, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/132C03C8/00C04B41/86
CPCC03C8/00C04B33/131C04B33/1324C04B41/009C04B41/5022C04B41/86C04B2235/3217C04B2235/3418C04B2235/3427C04B2235/96C04B41/4539Y02P40/60
Inventor 林贵基
Owner FUJIAN HUAXIA VAJRA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com