Preparation method of polyether-ether-ketone (PEEK) composite material artificial joint

A technology of artificial joints and composite materials, applied in the fields of medical science, tissue regeneration, prosthesis, etc., can solve the problems of worn fibers, fractures, fractures, etc., and achieve the effect of good biocompatibility and wear resistance

Inactive Publication Date: 2019-04-26
永康市仁合五金制品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention: Abrasion and fiber breakage will still occur in the existing composite artificial joint materials under complex physiological conditions and stressed states, and there is even a possibility of breakage, and the particles produced by wear can also cause local tissue inflammation To respond to the problem, a preparation method of PEEK composite artificial joint is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] In terms of parts by weight, weigh 100 parts of PEEK powder with a particle size of 150 microns, 5 parts of copper powder with a particle size of 10 microns, 1 part of antioxidant 136 and 0.1 part of white carbon black, mix them evenly and place them in a box-type resistor In the furnace, heat treatment at 280-310°C for 3-5 hours, after natural cooling, use a ball mill to mill for 20-25 minutes to obtain component A;

[0018] Dry the untreated CF in a vacuum oven at 100-130°C for 20-24 hours, then cool to obtain component B;

[0019] In terms of parts by weight, weigh 100 parts of component A and 30 parts of component B respectively, mix them uniformly and place them in a ball mill for 10-15 minutes to make component C;

[0020] When the heat press machine is heated up to 200°C, put component C into the knee joint mold of the heat press machine for preheating, pressurize to 6MPa when heated to 250°C, release the pressure to preheat for 2 minutes when heated to 280°C, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a polyether-ether-ketone (PEEK) composite material artificial joint, belonging to the technical field of medical materials. In order to solve the problems that the existing composite artificial joint materials are still worn and subjected to fiber breakage under the complicated physiological conditions and stress states and even have the possibilityof breakage, and the particles generated by abrasion also cause the inflammatory reaction of local tissues, the invention provides a preparation method of the PEEK composite material artificial joint. The artificial joint manufactured by using the technical scheme provided by the invention has the advantages of being good in biocompatibility and wear resistance, and the like.

Description

technical field [0001] The invention relates to a preparation method of a PEEK composite material artificial joint, belonging to the technical field of medical materials. Background technique [0002] Artificial joints are implantable prostheses made of artificial materials to replace damaged or diseased joints in order to treat fractures, joint deformities, joint ankylosis and various destructive bone and joint diseases. Artificial joint replacement is an effective method to treat advanced osteoarthritis, eliminate joint pain and improve function. Together with fracture internal fixation surgery, it is hailed as a great breakthrough in the field of orthopedics in the 20th century. It enables these diseased joints to be corrected and restored. Normal function helps improve the quality of life of some rheumatoid arthritis and osteoarthritis patients whose joints are severely damaged. [0003] Medical practice has shown that the performance of artificial joint materials and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/44A61L27/08A61L27/04A61L27/50
CPCA61L27/047A61L27/08A61L27/443A61L27/50A61L2430/24C08L61/16