Polyacid-based copper complex based on 2-picolinic acid and preparation method and application of complex
A picolinic acid, copper complex technology, applied in copper organic compounds, organic compounds/hydrides/coordination complex catalysts, chemical instruments and methods, etc., can solve the problems of reducing the dimension of the result, increasing the dimension of the target product, etc. The effect of improving the cleaning ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0042] [Cu(2-PA) of the one-dimensional chain structure 2 ]·2H 2 O was prepared as follows:
[0043] 0.24gCu(NO 3 ) 2 ·3H 2 O, 0.12g of 2-PA, 0.12g of PMo 12 and 10 g of H 2 0 mixed, evaporated and refluxed at 100°C for 6 hours with a condenser tube, obtained a blue transparent solution after cooling, left to volatilize after filtering, and obtained a blue transparent cuboid crystal, which is the [Cu( 2-PA) 2 ]·2H 2 O, hereinafter referred to as compound 1.
Embodiment 2
[0045] [(CH of the zero-dimensional supramolecular structure 3 ) 4 N][Cu(2-PA) 2 (SiW 12 o 40 ) 2 ] is prepared as follows:
[0046] 0.24g of Cu(NO 3 ) 2 ·3H 2 O, 0.12g of 2-PA, 0.2g of SiW 12 and 10 g of H 2 0 mixed with HNO 3 The solution was adjusted to a pH of 3.5, and added to a 15mL polytetrafluoroethylene-lined high-pressure stainless steel reactor, sealed and placed in an oven at 160°C for 3 days to obtain light blue cubic crystals, namely [(CH 3 ) 4 N][Cu(2-PA) 2 (SiW 12 o 40 ) 2 ], hereinafter referred to as compound 2.
Embodiment 3
[0048] [Cu of the homochiral two-dimensional network structure 6 (2-PA) 9 (PMo 12 o 40 )(NO 3 )]·H 2 O was prepared as follows:
[0049] 0.24g of Cu(NO 3 ) 2 ·3H 2 O, 0.12g of 2-PA, 0.1g of Mo 7 o 24 and 0.35 g of H 3 PO 4 , adding 10 g of H 2 0 mixed with HNO 3 The pH of the solution was adjusted to 0.5, and it was added to a 15mL polytetrafluoroethylene-lined high-pressure stainless steel reactor. After sealing, the reactor was placed in an oven at 160°C for 3 days, and a large number of green polygonal crystals were obtained, which was the pure [Cu 6 (2-PA) 9 (PMo 12 o 40 )(NO 3 )]·H 2 O, hereinafter referred to as compound 3.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com