A cross-linked, adhesive technology, applied in the directions of adhesive additives, adhesives, non-polymer adhesive additives, etc., can solve the problems of insufficient cohesive strength, substandard pendulum impact performance, etc. The effect of good die-cutting performance and excellent aging performance

Active Publication Date: 2019-05-24
新纶电子材料(常州)有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main PE foam manufacturers are Japanese suppliers, such as Waseda, Inoue, Sekisui, etc. The PE foam produced by these Japanese suppliers basically has good bal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cross-linked rubber adhesive, high-bonding-strength shock absorbing and silencing tape applying rubber adhesive and preparation method of rubber adhesive and tape
  • Cross-linked rubber adhesive, high-bonding-strength shock absorbing and silencing tape applying rubber adhesive and preparation method of rubber adhesive and tape
  • Cross-linked rubber adhesive, high-bonding-strength shock absorbing and silencing tape applying rubber adhesive and preparation method of rubber adhesive and tape

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]Prepare shock-absorbing and sound-absorbing type high-bond strength adhesive composition: put 434g of 120# solvent oil into a 1000ml light-shielding reaction bottle, then start the stirring device at a speed of 200rpm, and put in 80g of polymerized terpene resin A and polymerized terpene resin in turn while stirring. Vinyl resin B 33g, difunctional monomer HDDA 3.37g, photoinitiator 184 0.13g, light stabilizer Tinuvin144 0.13g, composite antioxidant 1010 and 168 respectively 0.36g and 0.3g, stir for 15min until it dissolves, and then put in Dispersant BYK-111 0.405g and hollow glass microspheres im30K 6.75g, after stirring for 10 minutes, put in 120g of star-shaped SIS, stir for 8 hours to completely dissolve and mix evenly, stop stirring, let it stand for more than 30 minutes to defoam naturally, and the reduced Shock-absorbing type high bond strength adhesive composition;

[0036] Coating process of shock-absorbing and sound-absorbing high-bond strength adhesive: On th...

Embodiment 2

[0038] Prepare shock-absorbing and noise-absorbing type high-bonding strength adhesive composition: put 440g of 120# solvent oil into a 1000ml light-shielding reaction bottle, then start the stirring device, and the rotation speed is 200rpm, and put in 100g of polymerized terpene resin A and polymerized terpene resin in turn while stirring. Vinyl resin B 20g, difunctional monomer HDDA 8g, photoinitiator 184 0.4g, light stabilizer Tinuvin144 0.3g, composite antioxidant 1010 and 168 respectively 0.6g and 0.4g, stir for 15min until it dissolves, then put into the dispersion Agent BYK-111 0.405g and hollow glass microspheres im30K 6.75g, after stirring for 10 minutes, put in 100g of star-shaped SIS, stir for 8 hours to completely dissolve and mix evenly, stop stirring, let it stand for more than 30 minutes to defoam naturally, and you can get shock absorption Sound-absorbing high-bond strength adhesive composition;

[0039] Coating process of shock-absorbing and sound-absorbing hi...

Embodiment 3

[0041] Prepare the shock-absorbing and sound-absorbing type high-bond strength adhesive composition: put 444g of 120# solvent oil into a 1000ml light-shielding reaction bottle, then start the stirring device at a speed of 200rpm, and put in 120g of polymerized terpene resin A and polymerized terpene resin in sequence while stirring. Vinyl resin B 6.7g, difunctional monomer HDDA 10g, photoinitiator 184 0.7g, light stabilizer UV-328 0.7g, composite antioxidant 1010 and 168 respectively 0.96g and 0.4g, stir for 15min until it dissolves, Then add 0.405g of dispersant BYK-111 and 6.75g of hollow glass microspheres K15, stir for 10 minutes, and finally put in 80g of star-shaped SIS, stir for 8 hours to completely dissolve and mix evenly, stop stirring, and let it stand for more than 30 minutes to defoam naturally. Obtain a shock-absorbing and sound-absorbing type high-bond strength adhesive composition;

[0042] Coating process of shock-absorbing and sound-absorbing high-bond streng...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cross-linked rubber adhesive. The cross-linked rubber adhesive is prepared from, by mass, 12-18% of star type SIS, 12-18% of polyterpene A, 1-5% of polyterpene B, 0.05-0.15%of a polyfunctional group monomer, 0.6-1.4% of hollow glass microspheres, 0.01-0.1% of a dispersing agent, 0.02-0.05% of a photoinitiator, 0.02-0.1% of a light stabilizer, 0.1-0.2% of an antioxidant and 50-70% of a solvent. The cross-linked rubber adhesive and high-bonding-strength shock absorbing and silencing tape applying the rubber adhesive have the advantages of water prevention, shock absorption, sound attenuation, high bonding strength, excellent aging performance and good subsequent die cutting processing performance, and can be used as double-sided adhesive tape in the fields of someautomobiles and electronics well.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to a cross-linked rubber adhesive, a high bonding strength shock-absorbing and sound-absorbing adhesive tape using the adhesive and a preparation method thereof. Background technique [0002] With the rapid development of industrial products, ranging from spacecraft, automobiles, to notebook computers, mobile phones, etc., more and more occasions require adhesives or adhesive tapes to provide bonding functions, especially for high bonding strength, durable The requirements for high and low temperature performance, waterproof performance, shock absorption and sound insulation performance are getting higher and higher. High and low temperature resistance mainly refers to ensuring that the adherend does not fall off and has a certain bonding strength under high or low temperature environments. Waterproof performance mainly refers to preventing water from penetrating from ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J4/06C09J4/02C09J11/04C09J11/06C09J7/10C09J7/30
Inventor 夏有贵王恒龙冲倪惠峰顾叶梅
Owner 新纶电子材料(常州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap