High-strength-and-ductility heat resistance pressure casting Mg-Y alloy and preparing method thereof

A hot die-casting and toughness-resistant technology is applied in the field of high-strength, toughness, heat-resistant die-casting Mg-Y alloy and its preparation. Small, enhance the effect of room temperature mechanical properties and high temperature performance

Active Publication Date: 2019-06-11
SHANGHAI JIAO TONG UNIV
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In order to solve the industrial problem that the existing die-casting magnesium alloy cannot reach the performance of die-casting aluminum alloys such as A380 due to insufficient strength, toughness and heat resistance, resulting in its application being greatly limited, the present invention provides a high-strength, toughness and heat-resistant die-casting Mg alloy. - Y alloy and its preparation method for pressure casting. After the alloy is pressure cast, the room temperature tensile strength of the die-cast alloy reaches 315MPa, the high temperature tensile strength of 200°C reaches 210MPa, and the room temperature elongation reaches 12.0%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength-and-ductility heat resistance pressure casting Mg-Y alloy and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The weight percent of a kind of high-strength and toughness heat-resistant die-casting Mg-Y alloy is: by theoretical ratio, 2.5% Y, 1.0% Zn, 0.5% Al, 0.3% Mn, 0.01% Ti, 0.01% B, the balance is Mg and other unavoidable impurities.

[0038] Its preparation method is:

[0039] (1) According to the above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the amount of required raw materials; industrially pure magnesium ingots, industrially pure zinc, industrially pure aluminum ingots, and MgY25 and MgMn10 master alloys are all removed from the oxide layer and pre-dried Heat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy;

[0040] (2) After melting the commercially pure magnesium ingots accounting for 25% of the height of the crucible into a molten pool at 680 ° C, the protective gas argon is introduced, and the remaining magnesium ingots are added;

[0041] (3) After the magnesi...

Embodiment 2

[0046] The weight percent of a high-strength and tough heat-resistant die-casting Mg-Y alloy is: according to the theoretical ratio, 5.0% Y, 4.0% Zn, 1.2% Al, 0.1% Mn, 0.08% Ti, and the balance is Mg and other unavoidable Impurities.

[0047] Its preparation method is:

[0048] (1) According to the above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the amount of required raw materials; remove the oxide layer and pre-dry the industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgY30 and MgMn10 master alloy Heat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy;

[0049] (2) After melting the commercially pure magnesium ingot accounting for 25% of the height of the crucible into a molten pool at 680 ° C, pass through a protective gas containing 0.2% volume fraction of SF 6 and CO 2 The mixed gas, add the remaining magnesium ingot;

[0050] (3...

Embodiment 3

[0055] The weight percentage of a kind of high-strength and toughness heat-resistant die-casting Mg-Y alloy is: by theoretical ratio, 3.0%Y, 2.0%Zn, 1.0%Al, 0.2%Mn, 0.05%Ti, 0.03%B, the balance is Mg and other unavoidable impurities.

[0056] Its preparation method is: (1) according to above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgY30 and MgMn10 master alloy Layer and dry and preheat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy;

[0057] (2) After melting the commercially pure magnesium ingots accounting for 25% of the height of the crucible into a molten pool at 680 ° C, the protective gas argon is introduced, and the remaining magnesium ingots are added;

[0058] (3) After the magnesium ingots are completely melted, raise the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-strength-and-ductility heat resistance pressure casting Mg-Y alloy and a pressure casting preparing method thereof. The alloy comprises, by mass percent, 2.5 to 5.0% of Y, 1.0 to 4.0% of Zn, 0.5 to 1.2% of Al, 0.1 to 0.3% of Mn, 0.01 to 0.08% of M and the balance Mg and inevitable impurities, and M is at least one element of Ti and B. Through pressure casting of the high-strength-and-ductility heat resistance pressure casting Mg-Y alloy, the room temperature tensile strength of the pressure-casting-state alloy reaches 315 MPa, the 200-DEG C high-temperature tensile strength reaches 210 MPa, the room temperature elongation reaches 12.0%, use is achieved without aging and solid-solution heat treatment, and the high-end needs of aerospace, automotive, telecommunications and other industries for lightweight development can be met.

Description

technical field [0001] The invention relates to a high-strength and toughness heat-resistant die-casting Mg-Y alloy and a preparation method thereof, belonging to the field of industrial magnesium alloys and their manufacture. Background technique [0002] As the lightest engineering metal material (the density of magnesium is 2 / 3 of aluminum and 1 / 4 of steel), its specific strength is obviously higher than that of aluminum alloy and steel. Higher than engineering plastics, it also has a series of advantages such as good castability, good machinability, good thermal conductivity, damping, strong electromagnetic shielding ability and easy recycling. Wide application prospects. Magnesium alloy has become an ideal material to replace aluminum alloy, steel and engineering plastics to achieve lightweight, among which aluminum alloy has the greatest substitution potential. [0003] Die casting is a casting method in which liquid or semi-solid metal is filled into the die-casting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/06C22C1/03C22C1/06
Inventor 叶兵刘子利丁文江蒋海燕
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap