Method for preparing ionic pressure array sensor based on 3D printing

An array sensor and 3D printing technology, applied in the field of 3D printing, can solve the problems of difficult preparation of array sensors, complex process, promotion and utilization of unfavorable materials, etc., and achieve the effect of good continuity, high precision, and not easy to flow

Active Publication Date: 2019-06-14
XI AN JIAOTONG UNIV
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current method of preparing ionic polymers for the preparation of sensors adopts the casting film process, so the prepared structure is relatively simple, which is not conducive to the promotion and utilization of the material. Melting 3D printing ionic polymer precursor materials are used to prepare ionic polymers For sensor devices, this printing method needs to hydrolyze the polymerized side chain SO2 groups of the printed Nafion precursors into SO3 groups. Microstructured Array Sensors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ionic pressure array sensor based on 3D printing
  • Method for preparing ionic pressure array sensor based on 3D printing
  • Method for preparing ionic pressure array sensor based on 3D printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] 1) Solution configuration;

[0049] It is 40% that the Nafion solution 40ml and 10ml of Nafion solution 40ml and 10ml of Nafion solution (DMAC) mixed with a graduated cylinder are mixed with magnetic stirring and heated and concentrated to Nafion;

[0050] 2) Planix gel configuration;

[0051] Weigh 4g of F-127 white powder, dissolve it in 6g of water, use a planetary mixer to stir evenly into a transparent gel, use a print head for preliminary inspection, the gel can be extruded into a uniform filament;

[0052] 3) Composite printing process;

[0053] S301, first load the ion polymer ink and F127 gel into the direct-writing printer with double nozzles, and adjust the extrusion air pressure for printing the ion polymer ink and F127 respectively, so that the nozzles can evenly discharge filaments;

[0054] S302, run the G code of the array model, the printer parameters are set to a layer thickness of 0.25mm, a scanning speed of 35mm / s, and an extrusion pressure of 0.3M...

Embodiment 2

[0060] 1) Solution configuration;

[0061] The dimethylformamide (DMF) mixing of 20ml and 10ml of Nafion solution 20ml and 10ml by graduated cylinder to measure mass fraction is 60% to the concentration of Nafion heated by magnetic stirring

[0062] 2) Planix gel configuration;

[0063] Weigh 3g of F-127 white powder, dissolve it in 7g of water, use a planetary mixer to stir evenly into a transparent gel, use a print head for preliminary inspection, the gel can be extruded into a uniform filament;

[0064] 3) Composite printing process;

[0065] S301, first load the ion polymer ink and F127 gel into the direct-writing printer with double nozzles, and adjust the extrusion air pressure for printing the ion polymer ink and F127 respectively, so that the nozzles can evenly discharge filaments;

[0066] S302, run the G code of the array model, the printer parameters are set to a layer thickness of 0.165mm, a scanning speed of 5mm / s, and an extrusion pressure of 0.02MPa to first p...

Embodiment 3

[0072] 1) Solution configuration;

[0073] Use a graduated cylinder to measure 10ml of Nafion solution with a mass fraction of 5% and mix it with 10ml of ethylene glycol (DMF), stir and concentrate with magnetic stirring until the concentration of Nafion is 50%.

[0074] 2) Planix gel configuration;

[0075] Weigh 3g of F-127 white powder, dissolve it in 7g of water, use a planetary mixer to stir evenly into a transparent gel, use a print head for preliminary inspection, the gel can be extruded into a uniform filament;

[0076] 3) Composite printing process;

[0077] S301, first load the ion polymer ink and F127 gel into the direct-writing printer with double nozzles, and adjust the extrusion air pressure for printing the ion polymer ink and F127 respectively, so that the nozzles can evenly discharge filaments;

[0078] S302, run the G code of the array model, the printer parameters are set to a layer thickness of 0.2mm, a scanning speed of 15mm / s, and an extrusion pressure ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an ionic pressure array sensor based on 3D printing. An ionic polymer solution Nafion and high-boiling-point solvent are used as ion sensing raw materials, pluronic F 127 is used as a printing supporting layer raw material, and the ionic pressure array sensor can be prepared through 3D composite printing. According to the method, the printing Nafion solution and printing supporting gel F-127 are combined, the problems occurring in array structure manufacturing with the pure printing Nafion solution are solved, the method is suitable for manufacturing different types of Nafion polymer microstructure arrays and therefore great utilization potentiality is achieved in the fields of artificial skin, flexible sensing and the like.

Description

technical field [0001] The invention belongs to the technical field of 3D printing, and in particular relates to a method for preparing an ion-type pressure array sensor based on 3D printing. Background technique [0002] Ionic electroactive polymer (iEAP) material is a typical flexible smart material with sensing-driving bidirectional function, usually in the sandwich composite membrane structure of electrode-ionic polymer-electrode, and ionic polymer usually adopts Nafion solution or Nafion membrane, the polymer contains mobile ions and water molecules. Under the action of external force, the iEAP material bends, and the elastic stress gradient generated inside makes the mobile cations migrate to the outside of the bend, thereby forming a space charge gradient distribution and forming a potential difference between the two electrodes. Compared with traditional piezoelectric polymer materials, it has outstanding advantages such as light weight, low mechanical impedance and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C64/118B33Y10/00B33Y70/00B33Y80/00
Inventor 陈花玲罗斌樊鹏徐雪杰
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com