High-strength and tough heat-resistant mg-gd alloy suitable for low-pressure casting and its preparation method

A low-pressure casting, mg-gd technology, applied in the field of high-strength, toughness, heat-resistant Mg-Gd alloy and its preparation, can solve the problems of inability to achieve the performance of cast aluminum alloy, insufficient heat resistance, etc., and achieve the effects of high efficiency and simple process

Active Publication Date: 2021-09-28
SHANGHAI JIAOTONG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the industrial problem that the existing cast magnesium alloy cannot reach the performance of cast aluminum alloys such as A380 due to insufficient strength, toughness and heat resistance, which results in its application being greatly limited, the invention provides a high-strength toughness suitable for low-pressure casting. A heat-resistant Mg-Gd alloy and a preparation method thereof. After the alloy is heat-treated by low-pressure casting, the room temperature tensile strength of the alloy is more than 280 MPa, and the elongation rate is more than 16%; rate of 16% or more

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and tough heat-resistant mg-gd alloy suitable for low-pressure casting and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The percentage by weight of a high-strength, tough, heat-resistant Mg-Gd alloy suitable for low-pressure casting related to the present embodiment is: according to the theoretical ratio, 4.0% Gd, 1.2% Zn, 1.2% Al, 0.3% Mn, 0.05% Ti, 0.03% B, the balance is Mg and other unavoidable impurities.

[0042]Its preparation method is: (1) according to the above-mentioned Mg-Gd alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgGd30 and MgMn10 master alloy layer and dry and preheat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) after melting the industrial pure magnesium ingot accounting for 25% of the crucible height into a molten pool at 680°C, Pass in the protective gas argon, and add the remaining magnesium ingots; (3) After the magnesium ingots are ...

Embodiment 2

[0045] The percentage by weight of a high-strength and tough heat-resistant Mg-Gd alloy suitable for low-pressure casting related to this embodiment is: according to the theoretical ratio, 8.0% Gd, 4.8% Zn, 0.8% Al, 0.1% Mn, 0.08% Ti, The balance is Mg and other unavoidable impurities.

[0046] Its preparation method is: (1) according to the above-mentioned Mg-Gd alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgGd30 and MgMn10 master alloy layer and dry and preheat to 180°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) After melting the industrial pure magnesium ingot accounting for 20% of the crucible height into a molten pool at 685°C, Introduce SF containing 0.2% volume fraction 6 and CO 2 (3) After the magnesium ingots are completely melted, heat up to...

Embodiment 3

[0049] The percentage by weight of a high-strength and tough heat-resistant Mg-Gd alloy suitable for low-pressure casting related to this embodiment is: according to the theoretical ratio, 7.0% Gd, 3.0% Zn, 0.5% Al, 0.2% Mn, 0.01% Ti, 0.01% B, the balance is Mg and other unavoidable impurities.

[0050] Its preparation method is: (1) according to the above-mentioned Mg-Gd alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgGd30 and MgMn10 master alloy layer and dry and preheat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) After melting the industrial pure magnesium ingot accounting for 20% of the crucible height into a molten pool at 675°C, Pass through the protective gas argon, and add the remaining magnesium ingots; (3) After the magnesium ingots are...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength, toughness and heat-resistant Mg-Gd alloy suitable for low-pressure casting and a preparation method thereof. The chemical composition of the alloy is as follows: 4.0-8.0% Gd, 1.2-4.8% Zn, 0.5-1.2% Al, 0.1-0.3% Mn, 0.01-0.08% M, the balance being Mg and other unavoidable impurities, wherein M is Ti and at least one element in B. After low-pressure casting, secondary solution treatment and artificial aging heat treatment, the high-strength, toughness and heat-resistant Mg-Gd alloy suitable for low-pressure casting of the present invention has a tensile strength of more than 280 MPa at room temperature and an elongation of more than 16%; The tensile strength is above 190MPa, and the elongation is above 16%, meeting the high-end demand for lightweight development in aerospace, military, automotive and other industries.

Description

technical field [0001] The invention belongs to the field of industrial magnesium alloy and its manufacture, and in particular relates to a high-strength and tough heat-resistant Mg-Gd alloy suitable for low-pressure casting and a preparation method thereof. Background technique [0002] As the lightest engineering metal material (the density of magnesium is 2 / 3 of aluminum and 1 / 4 of steel), its specific strength is obviously higher than that of aluminum alloy and steel. Higher than engineering plastics, it also has a series of advantages such as good castability, good machinability, good thermal conductivity, damping, strong electromagnetic shielding ability and easy recycling. Wide application prospects. Magnesium alloy has become an ideal material to replace aluminum alloy, steel and engineering plastics to achieve lightweight, among which aluminum alloy has the greatest substitution potential. Cast aluminum alloy has the necessary strength, toughness and thermal stabi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/06C22C1/03C22C1/06B22D18/04C22F1/06
Inventor 叶兵刘子利孔向阳
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap