Anti-ultraviolet paint and preparation method thereof

An anti-ultraviolet and coating technology, applied in the field of coatings, can solve the problems of UV resistance and achieve strong resistance

Inactive Publication Date: 2019-06-18
FOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies of the above-mentioned prior art, the object of the present invention is to provide an anti-ultraviolet coating and a preparation method thereof, aiming at solving the problem that the existing coating is not resistant to ultraviolet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The anti-ultraviolet coating of the present invention consists of the following components in parts by weight:

[0053] 15 parts of styrene-acrylic emulsion;

[0054] 25 parts of polyvinyl alcohol;

[0055] Attapulgite 15 parts;

[0056] Potassium silicate 15 parts;

[0057] Neoprene latex 7 parts;

[0058] 7 parts water glass;

[0059] 60 parts of water;

[0060] 3 parts of thickener;

[0061] Potassium stearate 3 parts.

[0062] The preparation method of the anti-ultraviolet coating of the present invention is: when preparing, take styrene-acrylic emulsion, polyvinyl alcohol, attapulgite, potassium water glass and add in water and stir for 30 minutes, increase the temperature to 80 ° C, then add neoprene latex, water glass, The thickener and potassium stearate were stirred for 30 minutes and cooled to room temperature.

Embodiment 2

[0064] The anti-ultraviolet coating of the present invention consists of the following components in parts by weight:

[0065] 15 parts of styrene-acrylic emulsion;

[0066] 25 parts of polyvinyl alcohol;

[0067] Attapulgite 15 parts;

[0068] Potassium silicate 15 parts;

[0069] Neoprene latex 7 parts;

[0070] 7 parts water glass;

[0071] 60 parts of water;

[0072] 3 parts of thickener;

[0073] Potassium stearate 3 parts.

[0074] The preparation method of the anti-ultraviolet coating of the present invention is: when preparing, take styrene-acrylic emulsion, polyvinyl alcohol, attapulgite, potassium water glass and add in water and stir for 30 minutes, increase the temperature to 80 ° C, then add neoprene latex, water glass, The thickener and potassium stearate were stirred for 30 minutes and cooled to room temperature.

[0075] Through performance tests, the coating for building exterior walls prepared by the invention complies with relevant national standards...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-ultraviolet paint and a preparation method thereof. The anti-ultraviolet paint is prepared from the following components in parts by weight: 10-15 parts of a styrene-acrylic emulsion, 25-35 parts of polyvinyl alcohol, 15-25 parts of attapulgite, 10-15 parts of potassium water glass, 7-9 parts of chloroprene latex, 7-9 parts of water glass, 40-60 parts of water, 3-5parts of a thickener and 3-5 parts of potassium stearate. The anti-ultraviolet paint provided by the invention has extremely strong resistance to ultraviolet rays and cannot discolor or crack under the long-term irradiation of sunlight. Moreover, the paint provided by the invention also has a quick-drying effect and is capable of rapidly solidifying under a low temperature condition. Therefore, the paint provided by the invention is superior to similar paint on the market.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an anti-ultraviolet coating and a preparation method thereof. Background technique [0002] At present, building exterior wall coatings are exposed to sunlight for a long time, and will change color and peel when damaged by ultraviolet rays, which will affect the appearance of building exterior walls. [0003] Therefore, the prior art still needs to be improved and developed. Contents of the invention [0004] In view of the above deficiencies in the prior art, the object of the present invention is to provide an anti-ultraviolet coating and a preparation method thereof, aiming at solving the problem that the existing coatings are not resistant to ultraviolet. [0005] Technical scheme of the present invention is as follows: [0006] A kind of anti-ultraviolet paint, wherein, by weight parts, be made up of following components: [0007] 10-15 copies of styrene-acrylic emulsion; [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/04C09D125/14C09D111/02
Inventor 陈强
Owner FOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD