1,6-hexanediol modified unsaturated polyester and preparation method thereof

A hexanediol and unsaturated technology, which is applied in the field of 1,6-hexanediol modified unsaturated polyester and its preparation, can solve the problems of poor crack resistance, impact resistance, poor crack resistance and fatigue resistance, and surface cracking. Sticking and other problems, to achieve the effect of improving crack resistance, improving air-drying performance, and preventing contact area

Inactive Publication Date: 2019-06-25
HUIZHOU CHANGRUNFA PAINT +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional unsaturated polyester has excellent process performance, such as wide processing temperature, light color, etc. The cured unsaturated polyester has good comprehensive properties, good corrosion resistance, electrical properties and good heat resistance, etc. The raw materials used are from a wide range of sources, and the price is cheaper than epoxy resin, but there are also shortcomings, such as large shrinkage during curing, high brittleness of the cured product, and the brittleness of the product makes the impact resistance, cracking resistance and fatigue resistance of the product poor. The surface of the film is soft and has a large contact area with oxygen in the air, resulting in a sticky and rough surface
[0003] In the existing unsaturated polyester resins, small molecular diols are often used, such as ethylene glycol, diethylene glycol, glycerol, etc. Due to the short molecular chain, the resin has poor flexibility and poor crack resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of 1,6-hexanediol modified unsaturated polyester, in weight percent:

[0016] Neopentyl Glycol 8%,

[0017] Maleic anhydride 30.5%,

[0018] Antioxidant 0.06%,

[0019] Distilled water 6.3%,

[0020] Dicyclopentadiene 27.9%,

[0021] 1,6-Hexanediol 12.2%,

[0022] 98% Pentaerythritol 2.5%,

[0023] Methylhydroquinone 0.02%,

[0024] Toluene 1.8%,

[0025] Styrene 9.5%,

[0026] Dimethyl carbonate 1.22.

[0027] A 1,6-hexanediol modified unsaturated polyester provided in this example has a finished viscosity of 6000±1000mPa.s / 25°C, a solid content of 85%±1.5, an acid value of 20-30mgKOH / g, and gelatinization Time: 10-18min. Color: ≤2# (Fe-Co).

Embodiment 2

[0029] A kind of 1,6-hexanediol modified unsaturated polyester, in weight percent:

[0030] Neopentyl Glycol 6%,

[0031] Maleic anhydride 31.5%,

[0032] Antioxidant 0.06%,

[0033] Distilled water 7.3%,

[0034] Dicyclopentadiene 27.9%,

[0035] 1,6-Hexanediol 12.2%,

[0036] 98% Pentaerythritol 2.5%,

[0037] Methylhydroquinone 0.02%,

[0038] Toluene 1.8%,

[0039] Styrene 9.5%,

[0040] Dimethyl carbonate 1.22.

[0041] A 1,6-hexanediol modified unsaturated polyester provided in this example has a finished viscosity of 6000±1000mPa.s / 25°C, a solid content of 86%±1.5, an acid value of 20-30mgKOH / g, and gelatinization Time: 10-19min. Color: ≤2# (Fe-Co).

Embodiment 3

[0043] A kind of 1,6-hexanediol modified unsaturated polyester, in weight percent:

[0044] Neopentyl Glycol 7%,

[0045] Maleic anhydride 30.5%,

[0046] Antioxidant 0.06%,

[0047] Distilled water 7.3%,

[0048] Dicyclopentadiene 27.9%,

[0049] 1,6-Hexanediol 12.2%,

[0050] 98% Pentaerythritol 2.5%,

[0051] Methylhydroquinone 0.02%,

[0052] Toluene 1.8%,

[0053] Styrene 9.5%,

[0054] Dimethyl carbonate 1.22.

[0055] A 1,6-hexanediol modified unsaturated polyester provided in this example has a finished viscosity of 6000±1000mPa.s / 25°C, a solid content of 85%±1.5, an acid value of 20-30mgKOH / g, and gelatinization Time: 10-19min. Color: ≤2# (Fe-Co).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of chemical industry, and particularly discloses a 1,6-hexanediol modified unsaturated polyester and a preparation method thereof, wherein the 1,6-hexanediol modified unsaturated polyester comprises, by weight, 6-10% of neopentyl glycol, 28-32% of maleic anhydride, 0.05-0.1% of an antioxidant, 4-8% of distilled water, 25-30% of an air drying agent, 10-15% of 1,6-hexanediol, 2-4% of 98% pentaerythritol, 0.01-0.03% of methylhydroquinone, 1-2% of toluene, 8-12% of a diluent, and 1-2% of dimethyl carbonate. According to the present invention, with theapplication of the the unsaturated polyester synthesized by using the long molecular chain of 1,6-hexanediol and the allyl ether-containing double bond in dicyclopentadiene in wood lacquers, the flexibility, the leveling property and the cracking resistance of the resin are improved, the softness and the sticking of the surface of the paint film are improved, the air drying performance is improved, the time for the next process of coating is saved so as to improve the production efficiency, and the needs of customers in the market are met.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a 1,6-hexanediol modified unsaturated polyester and a preparation method thereof. Background technique [0002] Traditional unsaturated polyester has excellent process performance, such as wide processing temperature, light color, etc. The cured unsaturated polyester has good comprehensive properties, good corrosion resistance, electrical properties and good heat resistance, etc. The raw materials used are from a wide range of sources, and the price is cheaper than epoxy resin, but there are also shortcomings, such as large shrinkage during curing, high brittleness of the cured product, and the brittleness of the product makes the impact resistance, cracking resistance and fatigue resistance of the product poor. The surface of the film is soft and has a large contact area with oxygen in the air, resulting in a sticky and rough surface. [0003] In the existing unsatura...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/01C08F212/08C08G63/52C08G63/78C09D151/08
Inventor 湛光练世斌戴超
Owner HUIZHOU CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com