Interior wall paint with magnetic functions, and preparation method thereof

An interior wall paint and functional technology, applied in the field of paint, can solve the problems of poor use effect of magnetic paint, poor magnetic powder dispersion, single paint function, etc., and achieve the effect of reducing load, volatile viscosity, and increasing safety factors.

Inactive Publication Date: 2019-06-25
BNSA NEW MATERIAL SHANGHAI CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] But the technical defect that the above-mentioned patent application technology exists is: (1) the magnetic powder in the magnetic paint is used as a dispersant with water, so that its dispersibility needs to be improved. The power is large, and there is almost no magnetic power in some positions, which directly leads to poor use of magnetic coatings; (2) The above-mentioned coatings overemphasize the magnetic function of the coating, and do not consider its basic properties such as heat insulation, weight loss, and flame retardancy. , it seems that the function of the coating is too single.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Preparation of nano-Fe 3 o 4 Dispersion liquid: 5 parts of nano-Fe 3 o 4 Mix with 40 parts of OS-10, and ultrasonically vibrate for 15 minutes at room temperature to make nano-Fe 3 o 4 Uniformly distributed in the solvent to obtain nano-Fe 3 o 4 Dispersions;

[0029] (2) Matrix pre-curing: place 40 parts of epoxy resin in the air, vibrate with an ultrasonic machine to remove air bubbles, and let it stand for 1 hour for pre-curing;

[0030] (3) Wet paint preparation: the prepared nano-Fe 3 o 4 Dispersion liquid, pre-cured epoxy resin, flame retardant 3 parts Al(OH) 3 Stir fully with 3 parts of mica powder under normal pressure for 30 minutes to obtain a wet coating;

[0031] (4) Curing of wet paint: apply the wet paint to the inner wall, then at t=25°C, Under certain conditions, the interior wall paint with magnetic function can be obtained by curing.

Embodiment 2

[0033] (1) Preparation of nano-Fe 3 o 4 Dispersion liquid: 8 parts of nano-Fe 3 o 4 Mix with 15 parts of OS-20, and ultrasonically vibrate for 20 minutes at room temperature to make nano-Fe 3 o 4 Uniformly distributed in the solvent to obtain nano-Fe 3 o 4 Dispersions;

[0034] (2) Matrix pre-curing: Mix 45 parts of silicone resin with the corresponding curing agent, vibrate with an ultrasonic machine to remove air bubbles, and let it stand for 1.5 hours for pre-curing;

[0035] (3) Wet paint preparation: the nano-Fe 3 o 4 The dispersion, the pre-cured silicone resin, 4 parts of melamine and 5 parts of graphite powder were fully stirred under vacuum for 60 minutes to obtain a wet coating;

[0036] (4) Curing of wet paint: apply the wet paint to the inner wall, and then at t=60°C, Under certain conditions, the interior wall paint with magnetic function can be obtained by curing.

Embodiment 3

[0038] (1) Preparation of nano-Fe 3 o 4 Dispersion liquid: 10 parts of nano-Fe 3 o 4 Mix with 20 parts of OS-20, and ultrasonically shake for 30 minutes at room temperature to make nano-Fe 3 o 4 Uniformly distributed in the solvent to obtain nano-Fe 3 o 4 Dispersions;

[0039] (2) Matrix pre-curing: Mix 50 parts of silicone resin with the corresponding curing agent, vibrate with an ultrasonic machine to remove air bubbles, and let it stand for 2 hours for pre-curing;

[0040](3) Wet paint preparation: the nano-Fe 3 o 4 The dispersion, the pre-cured silicone resin, 6 parts of dicyandiamide and 6 parts of talcum powder were fully stirred under vacuum for 120 minutes to obtain a wet coating;

[0041] (4) Curing of wet paint: apply the wet paint to the inner wall, and then at t=80°C, Under certain conditions, the interior wall paint with magnetic function can be obtained by curing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an interior wall paint with magnetic functions, and a preparation method thereof. The interior wall paint with magnetic functions comprises following components, by weight, 40to 50 parts of a matrix, 20 to 40 parts of a solvent, 1 to 10 parts of a weight reducing body, 3 to 6 parts of a flame retardant, 3 to 6 parts of a lubricant, and 5 to 10 parts of nanometer Fe3O4. Itis prepared through four steps including preparation of a nanometer Fe3O4 dispersion, matrix pre-curing, wet coating preparation, and wet coating curing. Compared with the prior art, the advantages are that: the interior wall paint possesses strong magnetic force; the lubricant capable of improving touch feel is adopted, so that excellent comfortability is achieved; the interior wall paint possesses thermal insulation function, is non-toxic, is safe, is friendly to the environment, and is a novel functional coating with both the advantages of magnetic coating and common coating; and no pollution is caused.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to an interior wall coating with magnetic function and a preparation method thereof. Background technique [0002] Magnetodynamic function refers to the collective name of biomagnetic function, negative ion generation function, far-infrared ray emission function, and antibacterial function; as we all know, magnetism is electricity, electricity is magnetism, and the two are inseparable; as far as electricity is concerned, it contains electromagnetic waves, and electromagnetic waves It also contains visible light and invisible light. Therefore, magnetic power contains the energy of magnetism, electricity, light and heat. [0003] Studies have found that reasonable magnetic stimulation can improve and improve the body's ability to resist and treat diseases. As a natural physical energy, magnetism may maintain the "magnetic balance" between the human body and the environment through its effects...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D183/04C09D5/23C09D5/18C09D7/61C09D7/20C09D7/65
Inventor 娄冬冬袁仁杰侯进全
Owner BNSA NEW MATERIAL SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com