A glycerin and slurry technology, applied in the directions of non-polymer adhesive additives, adhesive additives, non-polymer organic compound adhesives, etc., can solve the problems of poor processability, poor viscosity, screen blockage, etc. Low cost, wide application range, excellent conductivity and adhesion effects

Inactive Publication Date: 2019-06-25
CHANGZHOU HEDA OIL PUMP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing slurry mainly uses resin as the binder. During the preparation process, the physical properties of the metal and the resin are very different. After the formulation is made, many problems often arise, such as poor processability, screen blockage, and difficulty in cleaning. Elimination and replacement, difficulty in slurry flow, or poor conductivity and poor viscosity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] This glycerin slurry is made from the raw materials of following parts by weight:

[0011] 20-30 parts of metal powder, 1.5-4.5 parts of glycerin, 35-40 parts of isoamyl acetate, 4-5 parts of hydroxyalkyl acrylate, and 20-25 parts of adhesive.

[0012] 20 parts of metal powder, 1.5 parts of glycerin, 35 parts of isoamyl acetate, 4 parts of hydroxyalkyl acrylate, and 20 parts of adhesive.

[0013] 30 parts of metal powder, 4.5 parts of glycerin, 40 parts of isoamyl acetate, 5 parts of hydroxyalkyl acrylate, and 25 parts of adhesive.

[0014] 25 parts of metal powder, 3 parts of glycerin, 38 parts of isoamyl acetate, 4.5 parts of hydroxyalkyl acrylate, and 22 parts of adhesive.

[0015] The beneficial effects of the invention are: the raw materials of the glycerin slurry are common and easy to obtain, and the cost is low, and the finally prepared slurry has excellent electrical conductivity and adhesion, and has a wide range of applications.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of slurries, particularly to a glycerin slurry, which is prepared from the following raw materials by weight: 20-30 parts of metal powder, 1.5-4.5parts of glycerin, 35-40 parts of isoamyl acetate, 4-5 parts of hydroxyalkyl acrylate, and 20-25 parts of a binder. According to the present invention, the raw materials are common and easily-available, the cost is low, and the finally prepared slurry has advantages of excellent electrical conductivity, excellent adhesion, good flowability and wide application range.

Description

technical field [0001] The invention relates to a slurry, in particular to a glycerin slurry. Background technique [0002] The existing slurry mainly uses resin as the binder. During the preparation process, the physical properties of the metal and the resin are very different. After the formulation is made, many problems often arise, such as poor processability, screen blockage, and difficulty in cleaning. Elimination and replacement, difficulty in slurry flow, or poor conductivity and poor viscosity. Contents of the invention [0003] The present invention aims to solve the above-mentioned defects and provides a glycerin slurry. [0004] In order to overcome the defective that exists in the background technology, the technical scheme that the present invention solves its technical problem adopts is: this glycerin slurry is made by the raw material of following weight part: [0005] 20-30 parts of metal powder, 1.5-4.5 parts of glycerin, 35-40 parts of isoamyl acetate,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J9/02C09J11/04C09J11/06
Inventor 居振平
Owner CHANGZHOU HEDA OIL PUMP