Method for preparing high-stability automobile rubber tube rubber

A high-stability technology for automobile rubber hoses, which is applied in the field of preparation of high-stability automobile rubber hoses, can solve various problems such as unsatisfactory properties, and achieve the effects of increased strength, reasonable collocation, and simple process

Inactive Publication Date: 2019-07-12
马天时
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the quality of the rubber hose, the existing technology has carried out processing and improvement on it. For example, the application number is: CN201610681208.3 discloses a kind of rubber hose for automobiles, the main component of which is chlorinated polyethylene rubber. It has improved the strength and high temperature resistance of rubber, but with the continuous improvement of production requirements, the various properties of this material can no longer be satisfied, and further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of high-stability automobile hose rubber, comprising the steps of:

[0024] (a) Put the polytetrafluoroethylene micropowder into the acid solution for soaking and cleaning for 4 minutes, take it out and rinse it with deionized water until it is neutral, and finally put it in a drying box and dry it to a constant weight for later use;

[0025] (b) Put the PTFE micropowder treated in step (a) into the irradiation box for electron beam irradiation treatment, and take it out after 5 minutes for later use;

[0026] (c) Immerse the polytetrafluoroethylene micropowder treated in step (b) into the modification solution A, then perform magnetic stirring, and filter out the polytetrafluoroethylene micropowder after 35 minutes;

[0027] (d) Mix EPDM rubber, PTFE micropowder treated in step (c), benzoyl peroxide, sodium hexametaphosphate, and sulfur in a weight ratio of 20:4:0.1:0.5:0.1 , and then after high-speed blending, kneading treatment, and extrusion, t...

Embodiment 2

[0039] A preparation method of high-stability automobile hose rubber, comprising the steps of:

[0040] (a) Put the polytetrafluoroethylene micropowder into the acid solution to soak and clean for 5 minutes, take it out and rinse it with deionized water until it is neutral, and finally put it in a drying oven to dry to constant weight before use;

[0041] (b) Put the PTFE micropowder treated in step (a) into the irradiation box for electron beam irradiation treatment, and take it out after 6 minutes for later use;

[0042] (c) Immerse the polytetrafluoroethylene micropowder treated in step (b) into the modification solution A, then perform magnetic stirring, and filter out the polytetrafluoroethylene micropowder after 37 minutes;

[0043] (d) Mix EPDM rubber, PTFE micropowder treated in step (c), benzoyl peroxide, sodium hexametaphosphate, and sulfur in a weight ratio of 23:5:0.15:0.8:0.16 , and then after high-speed blending, kneading treatment, and extrusion, the mixture B is...

Embodiment 3

[0055] A preparation method of high-stability automobile hose rubber, comprising the steps of:

[0056] (a) Put the polytetrafluoroethylene micropowder into the acid solution to soak and clean it for 6 minutes, take it out and rinse it with deionized water until it is neutral, and finally put it in a drying box and dry it to a constant weight for later use;

[0057] (b) Put the PTFE micropowder treated in step (a) into the irradiation box for electron beam irradiation treatment, and take it out after 7 minutes for later use;

[0058] (c) Immerse the polytetrafluoroethylene micropowder treated in step (b) into the modification solution A, then perform magnetic stirring, and filter out the polytetrafluoroethylene micropowder after 40 minutes;

[0059] (d) Mix EPDM rubber, PTFE micropowder treated in step (c), benzoyl peroxide, sodium hexametaphosphate, and sulfur in a weight ratio of 25:6:0.2:1:0.2 , and then after high-speed blending, kneading treatment, and extrusion, the mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing high-stability automobile rubber tube rubber. The method comprises the following steps: (a) cleaning polytetrafluoroethylene micropowder; (b) carrying out electron beam radiation treatment; (c) soaking with a modification liquid A; (d) preparing a mixed material B; (e) weighing raw materials; and (f) preparing a finished product. The preparation method disclosed by the invention is relatively simple in process, the steps are reasonably matched, properties such as strength, temperature resistance, aging resistance and corrosion resistance of the rubber of the automobile rubber tube are remarkably improved, the stability of the rubber is improved, the service life of the rubber is prolonged, and the rubber has great market competitiveness and production benefits.

Description

technical field [0001] The invention belongs to the technical field of automobile rubber processing, and in particular relates to a preparation method of high-stability automobile rubber hose. Background technique [0002] At present, the rapid and vigorous development of the automobile industry has brought unprecedented development opportunities to the rubber industry supporting the automobile industry. According to the "2015-2020 China Automobile Manufacturing Market Assessment and Investment Prospect Forecast Report" released by China Industry Information Network, it shows that in June 2015, the number of automobiles in my country has exceeded 163 million, second only to the 220 million in the United States. vehicles, becoming the second in the world. China has become a big country of automobile consumption. Correspondingly, the engine manufacturing technology is relatively backward, which is one of the main factors hindering the development of the domestic automobile ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L91/06C08L23/16C08L27/18C08K13/06C08K9/04C08K3/28C08K3/32C08K3/04C08K3/26C08J3/24C08J3/28C08J7/14
CPCC08J3/246C08J3/28C08J7/14C08J2323/28C08J2327/18C08J2423/16C08J2427/18C08J2491/06C08K3/04C08K3/28C08K3/32C08K9/04C08K9/08C08K13/06C08K2003/265C08K2201/011
Inventor 马天时
Owner 马天时
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com