A microwave heat conversion material, carrier and preparation method thereof

A heat conversion and microwave technology, applied in the combustion method, lighting and heating equipment, combustion type and other directions, can solve the problems of difficult structural molding, cumbersome processing links and high cost, and achieve the effects of easy operation, light weight and low cost

Active Publication Date: 2021-06-01
义乌韦陀环保科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, ferrite or rare metal nickel / cobalt is generally used in the market as microwave heat energy conversion materials. The disadvantages are: the structure is too difficult to form, the cost is too high, and the processing process is extremely cumbersome and many other problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A microwave heat conversion material, carrier and preparation method thereof
  • A microwave heat conversion material, carrier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A microwave heat conversion material is made of the following materials in weight ratio: 60% of graphite powder, 12% of ferrite powder, 20% of glass fiber, 5% of cold-setting pellet binder and 3% of activated carbon binder.

Embodiment 2

[0030] A microwave heat conversion material is made of the following materials in weight ratio: 55% of graphite powder, 15% of ferrite powder, 25% of glass fiber, 6.25% of cold-setting pellet binder and 3.75% of activated carbon binder.

Embodiment 3

[0032] A microwave heat conversion material is made of the following materials in weight ratio: 65% of graphite powder, 10% of ferrite powder, 15% of glass fiber, 3.75% of metallurgical pellet binder and 2.25% of active carbon binder.

[0033] The preparation method of the microwave heat conversion material in the above-mentioned embodiment 1-embodiment 3, such as figure 1 As shown, it includes the following steps: take graphite powder, ferrite powder, glass fiber and binder in proportion, blend and stir evenly, and burn it at a high temperature of 1200-1350 degrees to form a semi-liquid, and the semi-liquid is processed by calendering equipment for multi-stage Roll forming, cooling 10-30 degrees, forming a flexible plate, that is.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of microwave heat conversion, and specifically relates to a microwave heat conversion material, a carrier and a preparation method thereof. The microwave heat conversion material is made of materials with the following weight ratio: graphite powder 55-65%, ferrite powder 10‑15%, glass fiber 15‑25% and binder 5‑10%. The structure of the present invention is convenient and simple to form, light in weight, has good insulation, acid and alkali resistance, pressure resistance and peeling properties, stable physical and chemical properties, high temperature and heat resistance, strong heat insulation, and high temperature resistance up to 1350 degrees Celsius Compared with the existing heat conversion materials, the wave-absorbing heat energy conversion can increase the heat energy conversion efficiency by 30%, and can be used in microwave waste gas combustion equipment efficiently and at high speed. Compared with the previous RTO burner, the energy saving can reach more than 50% and will not produce Consumables, the preparation process is simple, easy to operate, easy to shape, and low cost.

Description

technical field [0001] The invention belongs to the technical field of microwave heat conversion, and in particular relates to a microwave heat conversion material, a carrier and a preparation method thereof. Background technique [0002] Microwave absorbing material, also known as radar absorbing material or radar stealth material, is a material that can absorb microwave and electromagnetic energy with less reflection and scattering. The basic principle of microwave absorption is to convert microwave energy into energy of other forms of motion through a certain physical mechanism, and convert it into heat energy through the dissipation of the motion. Microwave absorbing materials should have good microwave absorbing properties, that is, microwave absorptivity higher than the required threshold and a wide absorption frequency band. In addition, the microwave absorbing material should also have a small thickness and areal density. [0003] Microwave absorbing materials are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H05K9/00F23G7/06
CPCF23G7/06H05K9/0081
Inventor 张永锋张朝锋游遨林子杰张堃
Owner 义乌韦陀环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap