A low-chromium corrosion-resistant high-strength polycrystalline superalloy and its preparation method

A high-temperature alloy and corrosion-resistant technology, which is applied in the field of low-chromium corrosion-resistant high-strength polycrystalline superalloy and its preparation, can solve problems such as impact and alloy structure instability, and achieve excellent oxidation resistance, excellent strength and corrosion resistance The effect of excellent tissue stability

Active Publication Date: 2020-08-18
CHINA HUANENG GRP CO LTD +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of Al element will also cause problems such as instability of the alloy structure, especially the higher content of Al element has a significant impact on the solidification and forming structure of the alloy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-chromium corrosion-resistant high-strength polycrystalline superalloy and its preparation method
  • A low-chromium corrosion-resistant high-strength polycrystalline superalloy and its preparation method
  • A low-chromium corrosion-resistant high-strength polycrystalline superalloy and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]The heat-resistant steel material of this embodiment includes by mass percentage: Cr: 17%, Co: 20%, Ti: 1.5%, Al: 4.0%, W: 7.0%, Si: 0.5%, Mn: 0.5%, Nb: 1.0%, C: 0.04%, the balance being Ni;

[0037] The preparation method of the present embodiment comprises the following steps:

[0038] 1) Raw material preparation: The ingredients include by mass percentage: Cr: 17%, Co: 20%, Ti: 1.5%, Al: 4.0%, W: 7.0%, Si: 0.5%, Mn: 0.5%, Nb: 1.0 %, C: 0.04%, the balance is Ni;

[0039] 2) Melting step: place the ceramic crucible and prepared raw materials in a vacuum melting furnace at the same time, and use a vacuum induction furnace at a vacuum degree not higher than 1.0×10 -4 Under MPa, the prepared alloy is smelted into alloy mother liquor, and when the alloy mother liquor is solidified, an electric arc is used to preheat the ceramic crucible at low power. After the alloy is completely solidified into an ingot, it is moved to a preheated ceramic crucible to prevent the alloy i...

Embodiment 2

[0045] The heat-resistant steel material of this embodiment includes by mass percentage: Cr: 17%, Co: 20%, Ti: 1.0%, Al: 4.0%, W: 8.5%, Si: 0.5%, Mn: 0.5%, Nb: 1.5%, C: 0.04%, the balance being Ni;

[0046] The preparation method of the present embodiment comprises the following steps:

[0047] 1) Raw material preparation: The ingredients include by mass percentage: Cr: 17%, Co: 20%, Ti: 1.0%, Al: 4.0%, W: 8.5%, Si: 0.5%, Mn: 0.5%, Nb: 1.5% %, C: 0.04%, the balance is Ni;

[0048] 2) Melting step: place the ceramic crucible and prepared raw materials in a vacuum melting furnace at the same time, and use a vacuum induction furnace at a vacuum degree not higher than 1.0×10 -4 Under MPa, the prepared alloy is smelted into alloy mother liquor, and when the alloy mother liquor is solidified, an electric arc is used to preheat the ceramic crucible at low power. After the alloy is completely solidified into an ingot, it is moved to a preheated ceramic crucible to prevent the alloy...

Embodiment 3

[0073] 1) Alloy preparation: Alloy components meet the following range requirements by mass percentage: Cr: 15%, Co: 15%, Ti: 0.5%, Al: 3.5%, W: 5%, Si: ≤0.5%, Mn: ≤0.5 %, Nb: 0.5%, C: 0.03%, the balance is Ni;

[0074] 2) Smelting: Melt the prepared alloy into alloy mother liquor, then use electroslag remelting process to refine, cool, after the alloy mother liquor is solidified into ingot and before the ingot temperature reaches 900°C, control the cooling rate not to exceed 15°C / min , after the ingot temperature reaches 900°C, it is cooled to room temperature at a cooling rate exceeding 10°C / min;

[0075] 3) Homogenization treatment: take out the ingot, then heat the ingot to 1030°C for half an hour, then heat it in a heat treatment furnace at 1170°C for 23 hours, and finally cool to room temperature to obtain a superalloy ingot;

[0076] 4) Hot rolling: the ingot is rolled, the total deformation is 50%, the deformation of each pass is controlled at 15%, and the deformation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A low-chromium corrosion-resistant high-strength polycrystalline superalloy and a preparation method thereof, the alloy components meet the following requirements in terms of mass percentage: Cr: 15-18%, Co: 15-20%, Ti: 0.5-1.5%, Al: 3.5 ~4.5%, W: 5~8.5%, Si: ≤0.5%, Mn: ≤0.5%, Nb: 0.5~1.5%, C: 0.03~0.08%, the balance is Ni; homogenization treatment after smelting, hot rolling , final heat treatment. The room temperature and 850°C tensile yield strength of the alloy of the present invention are respectively higher than 850MPa and 550MPa, and the alloy is subjected to 850°C high-temperature flue gas environment (N 2 ‑15% CO 2 ‑3.5% O 2 ‑0.1% SO 2 ) After 500 hours of corrosion, the weight change is less than 0.2mg / cm 2 . In addition, the alloy exhibits excellent structural stability during thermal exposure at 850 °C.

Description

technical field [0001] The invention belongs to the field of high-temperature alloy materials, and in particular relates to a low-chromium corrosion-resistant high-strength polycrystalline superalloy and a preparation method thereof. Background technique [0002] As my country's electricity demand continues to increase, energy shortages and environmental pollution problems have become increasingly prominent, and the need to develop high-efficiency, energy-saving, and environmentally friendly power generation methods has become increasingly urgent. Thermal power generation has been the most important power generation technology in my country for a long time, and improving the steam parameters of the unit is considered to be the most effective way to solve the above problems. A lot of practice in the past has shown that the service performance of key component materials is the most important factor restricting the improvement of steam parameters of boiler units. Service perfo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05C22C1/02C22F1/10
CPCC22C19/056C22C1/023C22F1/10
Inventor 严靖博谷月峰袁勇杨征张醒兴
Owner CHINA HUANENG GRP CO LTD