Preparation method of gradually-changed elastic waistband for paper diapers with unidirectional moisture-conducting function
A technology of one-way moisture guide and elastic waist, which is applied in the field of baby hygiene products, can solve the problems of poor air permeability, easy to be stuffy and sweaty, etc., and achieve the effect of gradual elastic thin thickness and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] Example 1
[0038] A method for preparing a gradual elastic waistline for diapers with a one-way wetness function, the specific steps are:
[0039] The first step: add the hydrophobic agent amino silicone oil to the solvent N,N-dimethylformamide, stir evenly, and then add polyurethane to obtain a hydrophobic polyurethane spinning with an amino silicone oil mass fraction of 2% and a polyurethane mass fraction of 10%. Silk dope: Use an electrostatic spinning device to spin the hydrophobic polyurethane spinning dope to prepare a hydrophobic fiber membrane with an average pore diameter of 3.0μm. The spinning temperature is 26.5°C, the relative humidity is 65%, and the voltage is 40kV. The distance is 20cm, the perfusion speed of the spinning solution is 3ml / h, and the diameter of the fiber obtained is 800nm. During the spinning process, adjust the sliding table distance step by step (40cm, 35cm, 30cm, 25cm, 20cm, 15cm, 10cm, 5cm, 0cm) to prepare a fiber membrane with a thicknes...
Example Embodiment
[0043] Example 2
[0044] A method for preparing a gradual elastic waistline for diapers with a one-way wetness function, the specific steps are:
[0045] The first step: add the hydrophobizing agent hexadecyltrimethoxysilane to the solvent N,N-dimethylformamide, stir evenly, and then add polyurethane to obtain the cetyltrimethoxysilane with a mass fraction of 3% , A hydrophobic polyurethane spinning dope with a polyurethane mass fraction of 10%; using an electrostatic spinning device to spin the hydrophobic polyurethane spinning dope to prepare a hydrophobic fiber membrane with an average pore diameter of 2.2μm, and the spinning temperature is 26.5℃ , The relative humidity is 80%, the voltage is 50kV, the receiving distance is 20cm, the perfusion speed of the spinning solution is 3ml / h, and the fiber diameter is 700nm. During the spinning process, the sliding table distance (40cm, 35cm, 30cm, 25cm, 20cm, 15cm, 10cm, 5cm, 0cm) to prepare a fiber membrane with a thickness gradient,...
Example Embodiment
[0049] Example 3
[0050] A method for preparing a gradual elastic waistline for diapers with a one-way wetness function, the specific steps are:
[0051] The first step: add the hydrophobic agent polydimethylsiloxane to the solvent N,N-dimethylformamide, stir evenly, and then add polyurethane to obtain a polydimethylsiloxane mass fraction of 3%, polyurethane The hydrophobic polyurethane spinning dope with a mass fraction of 15%; the hydrophobic polyurethane spinning dope is spun by an electrospinning device to prepare a hydrophobic fiber membrane with an average pore diameter of 2.5μm. The spinning temperature is 26.5℃. The humidity is 85%, the voltage is 50kV, the receiving distance is 20cm, the perfusion speed of the spinning solution is 3ml / h, and the resulting fiber diameter is 850nm. During the spinning process, the distance of the sliding table is adjusted step by step (30cm, 25cm, 20cm, 15cm, 10cm, 5cm, 0cm) to prepare a fiber membrane with a thickness gradient, the thickn...
PUM
Property | Measurement | Unit |
---|---|---|
Average pore size | aaaaa | aaaaa |
Average pore size | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap