Preparation method of high shock strength optical resin monomer

An optical resin and high impact resistance technology, which is applied in the field of preparation of high impact strength optical resin monomers, can solve the problems of difficulty in achieving unity of refractive index and impact resistance, and achieve the effect of excellent impact resistance and high impact strength

Inactive Publication Date: 2019-08-30
江苏可奥熙光学材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the preparation technology of optical resin monomers for the production of medium and high refractive index lenses is still not very mature, and it is often difficult to achieve a unified refractive index and impact resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A preparation method of high impact strength optical resin monomer, comprising the steps of:

[0022] (1) In terms of parts by mass, put 100 parts of acetyl triethyl citrate, 28 parts of allyl alcohol and 1.2 parts of calcium hydroxide into the R-01 reactor, heat to 185°C, and recover ethanol and allyl Alcohol, after the reaction is over, the reacted material is transferred to the R-02 reactor for distillation, heated to 85-100°C, and after further recovery of ethanol and allyl alcohol, the temperature continues to rise to 185°C, and the distilled material A is condensed and recovered to be Use; the specific operation process is:

[0023] a) Feeding: in parts by mass, put 100 parts of acetyl triethyl citrate, 28 parts of allyl alcohol and 1.2 parts of calcium hydroxide into the R-01 reactor, heat, and set the temperature of the reactor to 185 ℃;

[0024] b) Reflux: Observe from the sight glass of the R-01 reactor, when a mixture of liquid ethanol and allyl alcohol flo...

Embodiment 2

[0034] A preparation method of high impact strength optical resin monomer, comprising the steps of:

[0035] (1) In parts by mass, put 100 parts of acetyl triethyl citrate, 24 parts of allyl alcohol and 1.2 parts of calcium hydroxide into the R-01 reactor, heat to 185 °C, and recover ethanol and allyl Alcohol, after the reaction is over, the reacted material is transferred to the R-02 reactor for distillation, heated to 85-100°C, and after further recovery of ethanol and allyl alcohol, the temperature continues to rise to 185°C, and the distilled material A is condensed and recovered to be Use; the specific operation process is:

[0036] b) Feeding: In parts by mass, 100 parts of acetyl triethyl citrate, 24 parts of allyl alcohol and 1.2 parts of calcium hydroxide are put into the R-01 reactor, heated, and the temperature of the reactor is set to 185 °C,

[0037] b) Reflux: Observe from the sight glass of the R-01 reactor, when a mixture of liquid ethanol and allyl alcohol f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a high shock strength optical resin monomer, which comprises the following steps of: adding 100 parts by mass of acetyl triethyl citrate, 24-28 parts bymass of allyl alcohol and 1.2-1.8 parts by mass of calcium hydroxide into an R-01 reaction kettle, adding 100 parts by mass of purified material after a reaction is finished, 10-15 parts by mass of 1,4-cyclohexanediol and 0.1-0.15 parts by mass of antimonous oxide into an R-01 reaction kettle, heating to 160 DEG C for reaction, transferring 100 parts by mass of material after the reaction, 5-8 parts by mass of Columbia resin, 5-6 parts by mass of dibutyl maleate, 7-8 parts by mass of dioctyl maleate, 2-3 parts by mass of benzyl alcohol and 12-15 parts of triphenyl phosphite into an R-04 mixing kettle, and performing stirring and mixing for 45-60min to form viscous liquid. A refractive index of a resin lens reach above 1.56 when the monomer is used for producing the resin lens, and at thesame time, the monomer further has higher impact strength.

Description

technical field [0001] The invention relates to a preparation method of a high impact strength optical resin monomer. Background technique [0002] Compared with inorganic glass lenses, optical resin lenses have become more and more popular among consumers due to their own advantages, such as light weight, good toughness, and low price. [0003] Generally, in the lens industry, the refractive index is above 1.60 as the high refractive index, the refractive index is 1.56 as the medium refractive index, and the refractive index is below 1.56 as the low refractive index; [0004] At present, the preparation technology of optical resin monomers for the production of medium and high refractive index lenses is still not very mature, and it is often difficult to achieve uniform refractive index and impact resistance. Contents of the invention [0005] Object of the invention: The object of the invention is to provide a method for preparing a high-impact-strength optical resin mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L29/10C08K5/00C08K5/11C08K5/05C08K5/526
CPCC08K5/00C08K5/05C08K5/11C08K5/526C08L29/10
Inventor 钱军戴双汉
Owner 江苏可奥熙光学材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com