Optical fiber for incubator and preparation method of optical fiber

An incubator and optical fiber technology, applied in clad optical fiber, multi-layer core/clad optical fiber, rayon manufacturing, etc., can solve the defects of elasticity and bending stiffness, yarn tension increase, yarn elongation, etc. problems, achieve good bending and wear resistance, improve oil resistance and solvent resistance, good fatigue strength and folding resistance

Active Publication Date: 2015-12-09
临清三和纺织集团有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the high modulus fiber is used in the field of knitting loops, due to its defects in elasticity and bending stiffness, the yarn will be elongated during the knitting process, the internal tension of the yarn will increase, and when the knitting needle The hook diameter is very small, and the needle hook can easily cut off the fibers with poor folding resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] Correspondingly, the present invention also provides a method for preparing an optical fiber for an incubator, comprising the following steps: polymethylmethacrylate, polyaryletherketone, polyamide resin, SEBS, polyoxymethylene, TPU, methacryl Oxysilane, bisbenzoylphenyl phosphine oxide and 2,4-dihydroxybenzophenone are mixed and granulated by a single-screw extruder to obtain the inner core layer material. The temperature of the single-screw extruder is 130 -190°C, the speed of the pelletizer is 5.0HZ, the feeding speed is 6.0HZ, and the head pressure is 10MPa; polycarbonate, polysulfone, aramid fiber, 2-fluoromethyl acrylate, trifluoromethacrylate Ethyl ester, vinyltriethoxysilane, methacryloxypropyltrimethoxysilane, aroylphosphine oxide, α-hydroxyalkylphenone and nano-silica are mixed through a single-screw extruder Carry out granulation to obtain the material of the outer core layer, the temperature of the single-screw extruder is 160-200°C, the rotational speed of ...

Embodiment 1

[0042] 30 parts by mass of polymethylmethacrylate, 20 parts by mass of polyaryletherketone, 30 parts by mass of polyamide resin, 5 parts by mass of SEBS, 5 parts by mass of TPU, 20 parts by mass of polyoxymethylene, 8 parts by mass of Methacryloxysilane, 1 part by mass of bisbenzoylphenylphosphine oxide, and 1 part by mass of 2,4-dihydroxybenzophenone.

[0043] The material of the inner core layer is granulated by a single-screw extruder, and the granulation process conditions are as follows:

[0044] Extruder temperature: 180°C, pelletizer speed: 5.0HZ, feeding speed: 6.0HZ, head pressure: 10MPa.

Embodiment 2

[0046] 40 parts by mass of polymethylmethacrylate, 15 parts by mass of polyaryletherketone, 25 parts by mass of polyamide resin, 4 parts by mass of SEBS, 4 parts by mass of TPU, 25 parts by mass of polyoxymethylene, 8 parts by mass of Methacryloxysilane, 2 parts by mass of bisbenzoylphenylphosphine oxide, and 2 parts by mass of 2,4-dihydroxybenzophenone.

[0047] The material of the inner core layer is granulated by a single-screw extruder, and the granulation process conditions are as follows:

[0048] Extruder temperature: 170°C, pelletizer speed: 5.0HZ, feeding speed: 6.0HZ, head pressure: 10MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
refractive indexaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to view more

Abstract

The invention provides an optical fiber for an incubator and a preparation method of the optical fiber. Polyformaldehyde has excellent mechanical property, and has more excellent bending resistance, fatigue resistance, self-lubricating property, dimensional stability, creep resistance and heat aging resistance after being subjected to toughening modification by polyaryletherketone; TPU (Thermoplastic Polyurethane Elastomer) has extremely-high adhesiveness so as to favorably improve oil resistance and solvent resistance of materials; an outer core layer takes fluoroacrylate as a main base material and trifluoroethyl methacrylate as an auxiliary material, so that a refractive index is guaranteed, and good bending and wear resistance is obtained; methacryloxypropyltrimethoxysilane is taken as a compatilizer of the whole system; nanosilicon dioxide is grafted with polycarbonate, polysulfone, aramid fibers and the like by a coupling action, and is uniformly distributed on the whole outer core layer. Experimental results show that the optical fiber for the incubator, which is prepared by the preparation method disclosed by the invention, has good fatigue resistance and bending resistance.

Description

technical field [0001] The invention relates to the field of textile technology, in particular to an optical fiber for an incubator and a preparation method thereof. Background technique [0002] For various reasons, when the baby comes out of the mother's womb, the jaundice value will be abnormal. This is a disease characterized by jaundice on the skin, mucous membrane and sclera caused by abnormal bilirubin metabolism. Diseases can be divided into physiological and pathological. Physiological jaundice appears 2-3 days after birth, peaks at 4-6 days, subsides at 7-10 days, and lasts longer in premature infants. Except for a slight loss of appetite, there are no other clinical symptoms. If jaundice appears 24 hours after birth and persists in 2-3 weeks, or even continues to deepen and aggravate or reappears after disappearing, or jaundice begins to appear within one to several weeks after birth, it is all pathological jaundice. [0003] Most physiological jaundice does not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/10D01F8/16D01F8/12D01F8/14D01F1/10B29B9/06B29C47/92G02B6/036B29C48/92
Inventor 冷建军张芳
Owner 临清三和纺织集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap