Copper-iron alloy material electromagnetic shielding wire and preparation method thereof

Abstract

The invention provides a copper-iron alloy material electromagnetic shielding wire and a preparation method thereof, and belongs to the technical field of electromagnetic shielding wire material. Thecopper-iron alloy material comprises the following chemical components of, in percentage by weight, 5%-20% of Fe, less than or equal to 0.2% of Ni, less than or equal to 0.2% of Mn, less than or equalto 0.1% of Pb and the balance of Cu. The preparation method comprises the following steps of S1, preparing material; S2, smelting, and up leading continuously casting to obtain a phi 10 mm-20 mm copper rod blank; step 3, drawing, and repeatedly carrying out high-temperature annealing during drawing to obtain a phi 1 mm-2 mm copper-iron alloy wire rod; S4, carrying out heat preservation; S5, carrying out multi-pass drawing again to obtain an electromagnetic shielding wire with the diameter of phi 0. 05 mm-0.5 mm; and S6, weaving to obtain a net wire with electromagnetic shielding. According tothe method, the performance, the structure, the material utilization rate, the industrialization and other aspects of the prepared copper-iron alloy shielding wire are further improved, and a new path is provided for the application and the development of the copper-iron alloy shielding wire.

Description

technical field [0001] The invention relates to the technical field, in particular to a copper-iron alloy electromagnetic shielding wire and a manufacturing method thereof. Background technique [0002] Electromagnetic shielding refers to the use of shielding materials to block or attenuate the transmission of electromagnetic energy between the shielded area and the outside world. At present, the commonly used electromagnetic shielding materials include metal electromagnetic shielding materials, conductive polymer electromagnetic shielding materials and other carbon fiber / SiO materials such as CaO. 2 Composite materials, etc., the general preparation methods are: (1) mechanical alloying method; (2) deformation in-situ composite preparation; (3) rapid solidification preparation. Traditional methods are low in efficiency, high in cost, and difficult to achieve continuous production. From the research status and development trend of electromagnetic shielding materials, the fu...

AI Technical Summary

Problems solved by technology

[0007] 1. Raw material preparation adopts general discontinuous casting, which has low production efficiency and low material utilization rate;

[0008] 2. The round rod billet is obtained by hot extrusion process. Due to the uneven deformation of the hot extrusion process, the mechanical properties and metallographic structure of the manufactured profile are poor, and the p