Galvanized sheet treating agent
A treatment agent and technology for galvanized sheet, applied in the field of galvanized sheet treatment agent, can solve the problems that the anti-rust performance cannot be achieved, affected, and not considered various influencing factors, and achieve the effect of excellent anti-rust performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment Construction
[0027] The metal surface treatment agent of the present invention will be specifically described below through specific examples, but the scope of the present invention is not limited thereto.
[0028] The composition of the galvanized sheet treating agent of the present invention is as follows, wherein the percentages shown are by weight.
[0029]
[0030]
[0031] Cleaning and coating:
[0032] A 6 cm x 4 cm zinc plated steel plate test piece was cleaned in "Great Quick Degreaser" at 60°C for 5 minutes. Then rinse with clear water for 2 minutes, dry with hot air at 70°C, soak in the metal surface treatment solution of the present invention for 2 minutes, take it out and dry with hot air, apply high-based acrylic polyester primer, paint film thickness: 10 μm, acrylic topcoat paint Film thickness: 5 μm.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap