Transparent electrode and organic electroluminescent device including same
A transparent electrode, content technology, applied in the direction of electric solid devices, electrical components, semiconductor devices, etc., can solve problems such as commercialization obstacles, and achieve the effect of improving light efficiency and improving life.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0095] Example 1
[0096] The 1.0mg median diameter D 50 600nm TiO 2 The particles were dissolved in 10 mL of 1-methoxy-2-propanol, thereby obtaining a white paste-like dispersion. And the dispersion was doped in 5mL 0.4mg / ml sodium alginate aqueous solution, and then it was coated on the cleaned glass substrate by spin coating method, and dried into a film with a thickness of 15μm at room temperature. Where multiple coatings make TiO 2 The particles are located on top of the sodium alginate.
[0097] 1mL of 1mg / ml silver nanowires (60-120nm in diameter and 10-20μm in length, purchased from Nanjing Xianfeng Nanomaterials Technology Co., Ltd.) in ethanol were coated on sodium alginate by spin coating. Dried into a film with a thickness of 200nm at room temperature;
[0098] Stick a clean and flat glass cover sheet on the prepared silver nanowire film, exhaust the air between the glass cover sheet and the silver nanowires, and apply a pressure of 12 MPa on the glass cover sheet to co...
Example Embodiment
[0101] Example 2-6
[0102] The transparent electrode was prepared in the same method as in Example 1, except that 1 mL of the dispersion of silver nanowires in ethanol was coated on the sodium alginate at the concentration shown in Examples 2-6 in Table 3.
Example Embodiment
[0103] Example 7
[0104] A transparent electrode was prepared in the same manner as in Example 5, except that 1.0 mg TiO 2 The particles are doped with 5mg aliphatic epoxy resin UVR-6128 (epoxy equivalent of 190-210g / mol, purchased from Xinjing Chemical Co., Ltd.) instead of sodium alginate.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap