A kind of resin material for dental filling and preparation method thereof

A resin material and tooth filling technology, which is applied in the field of tooth restoration, can solve the problems of caries, not easy to shrink in volume, easy to wear and so on, and achieve the effects of not easy volume, good sterilization effect, and wide sterilization range.

Active Publication Date: 2022-07-05
XIAN MEDICAL UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The method of treating dental caries is mainly to use filling materials for filling, that is, firstly remove the damaged caries, use tools to make a certain shape, fill the filling materials and restore the shape of tooth defects. Currently, silver amalgam and composite resin are commonly used. , due to the toxicity of mercury in amalgam, the commonly used dental filling materials are resin materials. Compared with amalgam filling materials, resin has excellent biocompatibility, mechanical, aesthetic and other properties, and has become a popular choice for various dental tissues. The main way of damage, but because the dental resin is easy to be worn out during use, the caries symptoms will appear again in the caries repair position, so it is necessary to develop a new type of resin material with a long service life and a volume that is not easy to shrink.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A preparation method of a resin material for dental filling of the present invention is implemented according to the following specific steps:

[0030] Step 1. Weigh respectively calcium hydroxyphosphate 20~30%, polymethyl acrylate 10~15%, triethyl citrate 5~10%, diethyl dodecyl phosphonate 5~10% by weight , calcium alginate 10~15%, antibacterial agent 2~8%, antioxidant 5~10%, stabilizer 1~3%, double distilled water 20~25%, the sum of the mass percentages of the above components is 100% .

[0031] Step 2, add calcium hydroxyphosphate, polymethyl acrylate, triethyl citrate, diethyl dodecyl phosphonate and calcium alginate weighed in step 1 into the planetary high-energy ball mill tank, and at 550 ~ The mixture was obtained by ball milling at a speed of 650 rmp for 1 to 2 hours, and then ultrasonically oscillated for 0.5 to 1 hour.

[0032] Step 3. Add the antibacterial agent, stabilizer and antioxidant weighed in step 1 to the mixture obtained in step 2, mix and stir e...

Embodiment 1

[0039] A preparation method of resin for dental filling of the present invention is specifically implemented according to the following steps:

[0040] Step 1. Weigh calcium hydroxyphosphate 24%, polymethyl acrylate 10%, triethyl citrate 10%, diethyl dodecyl phosphonate 5%, calcium alginate 11%, nanometer 3% of silver powder, 3% of total alkaloids powder of Sophora flavescens, 8% of o-cresol, 1% of p-methoxyphenol, 25% of double distilled water, the sum of the mass percentages of the above components is 100%.

[0041] Step 2. Add calcium hydroxyphosphate, polymethyl acrylate, triethyl citrate, diethyl dodecyl phosphonate, calcium alginate and double distilled water weighed in step 1 into the planetary high-energy ball mill. , ball-milled at a speed of 550rmp for 1h, and then sonicated for 0.5h to obtain a mixture.

[0042] Step 3. To the mixture obtained in step 2, add nano-silver powder, total alkali matrine, o-cresol and p-methoxyphenol weighed in step 1, mix and stir evenl...

Embodiment 2

[0044] A preparation method of resin for dental filling of the present invention is specifically implemented according to the following steps:

[0045] Step 1. Weigh calcium hydroxyphosphate 20%, polymethyl acrylate 15%, triethyl citrate 5%, diethyl dodecyl phosphonate 5%, calcium alginate 15%, nanometer Silver powder 2%, Sophora flavescens total alkali powder 6%, o-cresol 10%, p-methoxyphenol 2%, double distilled water 20%, the sum of the mass percentages of the above components is 100%.

[0046] Step 2. Add the calcium hydroxyphosphate, polymethyl acrylate, triethyl citrate, diethyl dodecyl phosphonate and calcium alginate weighed in step 1 into the planetary high-energy ball mill, at a temperature of 650 rpm. The mixture was ball-milled for 1.5 h at a high speed, and then sonicated for 1 h to obtain a mixture.

[0047] Step 3. Add the antibacterial agent, stabilizer and antioxidant weighed in step 1 to the mixture obtained in step 2, mix and stir evenly at 65°C, and stir f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a resin material for tooth filling, which is composed of the following components according to mass percentage: calcium hydroxyphosphate 20-30%, polymethyl acrylate 10-15%, triethyl citrate 5-10%, dodecyl Diethyl alkyl phosphonate 5-10%, calcium alginate 10-15%, antibacterial agent 2-8%, antioxidant 5-10%, stabilizer 1-3%, double distilled water 20-25%, The sum of the mass percentages of the above components is 100%. The invention also specifically discloses the preparation method of the above-mentioned resin material for dental filling; the resin material for dental filling prepared by the invention has good compressive strength and hardness, does not contain heavy metals, is environmentally friendly, and the preparation method is simple and convenient, easy to use promotion.

Description

technical field [0001] The invention belongs to the field of tooth restoration, and in particular relates to a resin material for tooth filling, and also relates to a preparation method of the above-mentioned resin material for tooth filling. Background technique [0002] Teeth are very important organs of human beings. Dental caries, also known as cavities or tooth decay, is a bacterial disease. If the treatment is carried out, the crown will eventually be completely destroyed and disappear, and you will not be able to chew. [0003] The method of treating dental caries mainly uses filling materials for filling, that is, first remove the damaged caries, use tools to make a certain shape, fill the filling materials and restore the shape of the tooth defect. At present, amalgam and composite resin are often used. , Due to the toxicity of mercury in amalgam, the commonly used dental filling materials are resin materials. Compared with amalgam filling materials, resin has exc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K6/887A61K6/898A61K6/838A61K6/69A61K6/70A61K6/60
Inventor 张耀超左艳萍张琳梅崔晓明
Owner XIAN MEDICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com