A composite ceramic membrane and photocatalytic technology, applied in chemical instruments and methods, membrane technology, semipermeable membrane separation, etc., can solve the problems of high turbidity, shortened membrane service life, high COD, etc., and achieve the effect of improving membrane separation efficiency

Inactive Publication Date: 2019-11-22
SHENZHEN PANGU ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to the high COD and high turbidity of landfill leachate, when membrane separation technology is used to treat landfill leachate, problems such ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of photocatalytic composite ceramic membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0020] In this embodiment of the present invention, it should be noted that the terms "center", "upper", "lower", "left", "right", "vertical", "horizontal", "inner", "outer" etc. The indicated orientation or positional relationship is based on the position or positional relationship shown in the drawings, and is only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying that the referred device or element must have a specific orientation, and must have a specific orientation. construction and operation are therefore not to be con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention is applicable to the technical field of ceramic membrane preparation, and provides a preparation method of a photocatalytic composite ceramic membrane. The method comprises the followingsteps: mixing ethylenediamine, boric acid, thiourea and tetrabutyl titanate sol to prepare a composite precursor; dropwise adding absolute ethyl alcohol and glacial acetic acid into the obtained composite precursor, uniformly mixing and stirring, and carrying out wet ball milling to obtain faint yellow titanium dioxide transparent sol; adding a liquid glass solution into the titanium dioxide transparent sol for dipping, wherein the dipping time is 30-50 minutes; coating a flat plate support body with the the impregnated titanium dioxide sol; placing the coated flat plate supporting body in aroom temperature environment with the humidity smaller than 40% to be stored for 12-24 h; taking out the flat plate support body, roasting in a muffle furnace by taking nitrogen as a protective gas, heating to 500 DEG C at a speed of 2-5 DEG C/min, and keeping the constant temperature for 2-8 hours; and taking out the flat plate support body from the muffle furnace, and naturally cooling to room temperature to obtain the photocatalytic composite ceramic membrane.

Description

technical field [0001] The invention belongs to the technical field of ceramic film preparation, and in particular relates to a preparation method of a photocatalytic composite ceramic film. Background technique [0002] Inorganic ceramic ultrafiltration membranes are sintered from ceramic raw materials, so compared with organic membranes, they have better high temperature resistance, chemical corrosion resistance, higher mechanical strength, stronger oxidation resistance and easy cleaning. . With the continuous reduction of costs, inorganic ceramic membranes have been gradually promoted and used in water treatment applications, and partially replaced organic membranes in some drinking water and urban sewage treatment plants at home and abroad. The use of ceramic membranes in the treatment of landfill leachate can give full play to the advantages of chemical corrosion resistance and easy cleaning. [0003] However, due to the high COD and high turbidity of landfill leachat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D71/02B01D69/12B01D67/00C02F1/32C02F101/30C02F103/06
CPCB01D67/0039B01D69/12B01D71/025C02F1/32C02F2101/30C02F2103/06C02F2303/04
Inventor 徐剑晖何頔赵建树周鸿波徐飞郭彧王光照刘国均谢旺
Owner SHENZHEN PANGU ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap