A kind of cemented carbide coating completely soluble in water medium and its preparation method and application

A technology of complete dissolution of cemented carbide, applied in metal material coating process, coating, earthwork drilling and mining, etc., can solve the problems of affecting tool use effect, affecting demand, insoluble and so on, so as to reduce construction risk and improve construction Efficiency, small size effect

Active Publication Date: 2021-12-31
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the slips partially dissolve in the well, the inlaid ceramic and hard alloy block will loosen, which will affect the use effect of the tool; while the ceramic and hard alloy block are insoluble and not easy to flow back, which also affects the actual demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cemented carbide coating completely soluble in water medium and its preparation method and application
  • A kind of cemented carbide coating completely soluble in water medium and its preparation method and application
  • A kind of cemented carbide coating completely soluble in water medium and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a cemented carbide coating that is completely soluble in an aqueous medium and is composed of a soluble aluminum alloy and a nickel-based alloy, wherein the volume ratio of the soluble aluminum alloy and the nickel-based alloy is 1:9. The soluble aluminum alloy components and the mass percentage of each component are: 3% Mg, 1% Cu, 1.3% Ga, 0.2% In, and the balance is Al. The soluble aluminum alloy is at 95°C and the concentration is 3wt.%. The dissolution rate in KCl solution is 15mg / cm 2 hr; the nickel-based alloy is Ni60, and the particle size is 250 mesh.

[0038] Concrete preparation steps are as follows:

[0039] (1) Process the above-mentioned soluble aluminum alloy block into small chips, and use a ball mill (the volume ratio of balls and soluble aluminum alloy chips is 1:1) to grind the chips into small chips at 300 rpm / min for 6 hours. Powder, the size of which is screened out is 200 mesh powder to obtain soluble aluminum alloy powde...

Embodiment 2

[0047] This embodiment provides a cemented carbide coating that is completely soluble in an aqueous medium and is composed of a soluble magnesium alloy and an iron-based alloy, wherein the volume ratio of the soluble magnesium alloy and the iron-based alloy is 1:11.5. The soluble magnesium alloy components and the mass percentage content of each component are: 8% Al, 1.5% Zn, 0.5% Ni, and the balance is Mg. The soluble magnesium alloy is dissolved in a 3wt.% KCl solution at 95°C The rate is 25mg / cm 2 hr; iron-based alloy is Fe60, particle size 200 mesh.

[0048] Concrete preparation steps are as follows:

[0049] (1) Process the above-mentioned soluble magnesium alloy block into small chips, and use a ball mill (the volume ratio of balls and soluble magnesium alloy chips to be 1:2) to grind the chips into small chips at a speed of 300 rpm for 6 hours. Powder, the size of which is screened out is 200 mesh powder to obtain soluble magnesium alloy powder;

[0050] (2) Mix the ...

Embodiment 3

[0054] This embodiment provides a cemented carbide coating that is completely soluble in an aqueous medium and is composed of a soluble aluminum alloy and a nickel-based alloy, wherein the volume ratio of the soluble aluminum alloy and the nickel-based alloy is 1:6. The soluble aluminum alloy components and the mass percentage of each component are: 3% Mg, 1% Cu, 1.3% Ga, 0.2% In, and the balance is Al. The soluble aluminum alloy is at 95°C and the concentration is 3wt.%. The dissolution rate in KCl solution is 25mg / cm 2 hr; nickel-based alloy is Ni60, particle size 300 mesh.

[0055] Concrete preparation steps are as follows:

[0056] (1) Process the above-mentioned soluble aluminum alloy block into small chips, and use a ball mill (the volume ratio of balls and soluble aluminum alloy chips is 1:1.5) to grind the chips into small chips at 300 rpm / min for 6 hours. Powder, the size of which is screened out is 200 mesh powder to obtain soluble aluminum alloy powder;

[0057] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cemented carbide coating completely soluble in water medium, a preparation method and application thereof. The cemented carbide coating is composed of soluble alloy powder and cemented carbide powder, with moderate dissolution speed and high hardness. It is prepared as follows: uniformly mix cemented carbide powder and soluble alloy powder, and then spray it on the workpiece by plasma spraying, flame spraying or supersonic spraying process to obtain a cemented carbide coating, which is well combined with the substrate. The cemented carbide coating can be applied to the protection of the surface of tools or parts used in the fracturing reconstruction of oil and gas fields. After the construction, the cemented carbide coating can be completely dissolved, eliminating the need for subsequent grinding and milling processes, which is beneficial to flowback and improves construction efficiency.

Description

technical field [0001] The invention belongs to the field of hard alloy coating preparation and oil and gas field development, and in particular relates to a hard alloy coating which can be completely dissolved in water medium and its preparation method and application. Background technique [0002] A large number of oil and gas resources are distributed in shale, and these resources are distributed in formations of different depths. Due to the characteristics of low permeability, it is difficult to exploit them. For low-permeability oil and gas resources, oil companies often use horizontal well multi-stage hydraulic fracturing technology to increase single well productivity. In fracturing construction, it is necessary to use isolation tools (bridge plugs and fracturing balls) to seal off the construction string, and then use high-pressure fracturing fluid to fracture the shale formation to facilitate oil and gas transportation. [0003] Currently, most commonly used isolat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/06C23C4/134C23C4/129C22C21/06C22C23/02E21B43/26
CPCC23C4/06C23C4/134C23C4/129C22C21/06C22C23/02E21B43/26
Inventor 刘军汪伟李文戈赵胜兰王大江方梦莉王晓婉陈德敏
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com