Polyimide oriented film preparation method

A technology of polyimide and polyimide polymer is applied in the field of preparation of polyimide alignment films, which can solve the problems of high requirements for the preparation of alignment films, affecting the display effect of display screens, etc., and achieves reduction of process difficulty and low cost. , the effect of simple operation

Inactive Publication Date: 2019-12-27
合肥中聚和成电子材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing a polyimide alignment film in order to solve the problem that the alignment liquid on the electrode is dissolved with a dissolving agent, which will affect the display effect of the display screen, in order to solve the problem of high requirements for the preparation of the existing alignment film.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1, a kind of polyimide alignment film preparation method, comprises the following steps:

[0027] Step 1: Spread the polyimide polymer solution evenly on the glass substrate;

[0028] Step 2: Immediately irradiate the polyimide polymer solution on the substrate with a linearly polarized laser for polymerization;

[0029] Step 3: Perform pre-curing treatment on the polyimide polymer solution applied on the substrate, and the pre-curing temperature is 80-100°C;

[0030] Step 4: Curing the polyimide polymer solution on the pre-cured substrate at a curing temperature of 180-200°C.

[0031] The polyimide polymer solution is formed by mixing siloxane compound, ethanol, and glutarimide, and the method for mixing the polyimide solution includes the following steps: mixing glutarimide with Mix the ethanol to dissolve the glutarimide; mix the siloxane compound with the ethanol solution in which the glutarimide is dissolved to make a polyimide polymer solution.

Embodiment 2

[0032] Embodiment 2, a kind of polyimide alignment film preparation method, comprises the following steps:

[0033] Step 1: Spread the polyimide polymer solution evenly on the glass substrate;

[0034] Step 2: Immediately irradiate the polyimide polymer solution on the substrate with a linearly polarized laser for polymerization;

[0035] Step 3: Perform pre-curing treatment on the polyimide polymer solution applied on the substrate, and the pre-curing temperature is 80-100°C;

[0036] Step 4: Curing the polyimide polymer solution on the pre-cured substrate at a curing temperature of 180-200°C;

[0037] Step 5: Take off the cured and formed alignment film, check it, and complete the preparation.

[0038] The polyimide polymer solution is formed by mixing siloxane compound, ethanol, and glutarimide, and the method for mixing the polyimide solution includes the following steps: mixing glutarimide with Ethanol is mixed to dissolve glutarimide; the siloxane compound is mixed wi...

Embodiment 3

[0039] Embodiment three, a kind of polyimide alignment film preparation method, comprises the following steps:

[0040] Step 1: Spread the polyimide polymer solution evenly on the glass substrate;

[0041] Step 2: Immediately irradiate the polyimide polymer solution on the substrate with a linearly polarized laser for polymerization;

[0042] Step 3: Perform pre-curing treatment on the polyimide polymer solution applied on the substrate, and the pre-curing temperature is 80-100°C;

[0043] Step 4: Curing the polyimide polymer solution on the pre-cured substrate at a curing temperature of 180-200°C.

[0044] The polyimide polymer solution is formed by mixing siloxane compound, ethanol, and glutarimide, and the method for mixing the polyimide solution includes the following steps: mixing glutarimide with Mix the ethanol to dissolve the glutarimide; mix the siloxane compound with the ethanol solution in which the glutarimide is dissolved to make a polyimide polymer solution.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyimide oriented film preparation method. The method comprises the steps that a polyimide polymer solution is uniformly smeared on a glass substrate; a linearly polarized laser is used to irradiate the polyimide polymer solution on the substrate for polymerization; the polyimide polymer solution smeared on the substrate is subjected to precuring treatment, wherein the precuring temperature is 80-100 DEG C; the polyimide polymer solution on the substrate after precuring treatment is subjected to curing treatment, wherein the curing temperature is 180-200 DEG C; and an oriented film, which is cured and formed, is taken off and checked to complete preparation. The polyimide polymer solution contains a siloxane compound, ethyl alcohol and glutarimide, all of which are mixed. According to the method, the linearly polarized laser is used for irradiation and polymerization immediately after the polyimide polymer is smeared on the glass substrate, so that siloxane compound molecules are connected to a polyimide molecular chain, and control over a pre-tilt angle of liquid crystals of a display screen can be realized just by controlling the content of the siloxanecompound molecules in the polymer.

Description

technical field [0001] The invention belongs to the technical field of preparation of alignment films, in particular to a preparation method of polyimide alignment films. Background technique [0002] In the past, liquid crystal displays using the STN display mode have the problems of small viewing angle, color loss of the picture when viewed from a larger side angle, and poor contrast and color performance. In order to solve this problem, people have developed a wide viewing angle technology. ADS, that is, advanced ultra-dimensional field switching technology, forms a multi-dimensional electric field through the electric field generated by the edge of the slit electrode in the same plane and the electric field generated between the slit electrode layer and the plate electrode layer, so that the gap between the slit electrodes and the electrodes in the liquid crystal cell All aligned liquid crystal molecules directly above can be rotated, thereby improving the working effic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02F1/1337
CPCG02F1/133723G02F1/133788
Inventor 梁小朝连杰姚浩川黄德新
Owner 合肥中聚和成电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap