Preparation method of corrosion-resistant chemical barrel material

A corrosion-resistant and chemical technology, which is applied in the field of preparation of corrosion-resistant chemical barrel materials, can solve problems such as being unable to withstand high-temperature erosion, and achieve the effects of maintaining stable chemical properties, improving corrosion resistance, and wear-resistant relative density

Inactive Publication Date: 2020-01-17
安徽天路新材料股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The corrosion resistance of the currently used chemical barrels has been improved to a certain extent, but they still cannot withstand the high temperature and the erosion caused by the movement process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A method for preparing a corrosion-resistant chemical barrel material, comprising the following steps:

[0014] S1: Preparation of nano-ceramic materials: Weigh 8.5 grams of silicon nitride and 4.0 grams of graphite powder, mix and grind them for 20 minutes, place them in a beaker, add 20 milliliters of titanium dioxide hydrogel into the beaker, disperse them ultrasonically for 10 minutes, and then add them to the dispersion Add 50 ml of ethylene glycol aqueous solution to the mixture, mix at high speed for 30 minutes at 1000 rpm, let it stand in an oven at 70°C for 4 hours, and then send it into a muffle furnace for calcination for 3 hours at a calcination temperature of 800°C, and cool with the furnace To normal temperature, it can be ground into powder; wherein, the mass concentration of titanium dioxide in the titanium dioxide hydrogel is 28%, and the mass concentration of the ethylene glycol aqueous solution is 60%. The nano-ceramic material prepared by the inventi...

Embodiment 2

[0018] A method for preparing a corrosion-resistant chemical barrel material, comprising the following steps:

[0019] S1: Preparation of nano-ceramic materials: 8.8 grams of silicon nitride and 4.2 grams of graphite powder were mixed and ground for 25 minutes in turn, placed in a beaker, 22 milliliters of titanium dioxide hydrogel was added to the beaker, ultrasonically dispersed for 12 minutes, and then added to the dispersion Add 55 ml of ethylene glycol aqueous solution, mix at 1100 rpm for 35 minutes at high speed, let it stand in an oven at 75°C for 5 hours, then put it into a muffle furnace for calcination for 3.5 hours, the calcination temperature is 850°C, and cool with the furnace To normal temperature, it can be ground into powder; wherein, the mass concentration of titanium dioxide in the titanium dioxide hydrogel is 29%, and the mass concentration of the ethylene glycol aqueous solution is 62%. The nano-ceramic material prepared by the invention has phase transiti...

Embodiment 3

[0023] A method for preparing a corrosion-resistant chemical barrel material, comprising the following steps:

[0024]S1: Preparation of nano-ceramic materials: Weigh 9.0 grams of silicon nitride and 4.5 grams of graphite powder, mix and grind for 30 minutes, put them in a beaker, add 24 milliliters of titanium dioxide hydrogel into the beaker, ultrasonically disperse for 15 minutes, and then add Add 60 ml of ethylene glycol aqueous solution to the mixture, mix at 1200 rpm for 40 minutes at high speed, let it stand in an oven at 80°C for 6 hours, then send it to a muffle furnace for calcination for 4 hours at a temperature of 900°C, and cool with the furnace To normal temperature, it can be ground into powder; wherein, the mass concentration of titanium dioxide in the titanium dioxide hydrogel is 30%, and the mass concentration of the ethylene glycol aqueous solution is 65%. The nano-ceramic material prepared by the invention has phase transition toughness, particle size betwe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of new material processing, and discloses a preparation method of a corrosion-resistant chemical barrel material. According to the preparation method, nanometer ceramic material modified polypropylene composite plastic is used for preparing a chemical barrel material master batch; chemical reaction between a corrosive medium and the surface of the chemical barrel material is prevented; a interface structure is protected; excellent performances of corrosion resistance, wear resistance, low relative density and the like are realized; the preparationmethod can be used for plastic enhancement, and the effect of promoting plasticization can also be achieved; after being treated and added into the polypropylene blended plastic, the corrosion-resistant chemical barrel material has an excellent reinforcing effect, the material microstructure can greatly improve the corrosion resistance, mechanical properties and aging resistance of blended materials, the corrosion-resistant chemical barrel material can be well dispersed in the blended materials, and the chemical properties are basically kept stable after immersion in corrosive liquid for a long time.

Description

technical field [0001] The invention belongs to the technical field of new material processing, and in particular relates to a preparation method of a corrosion-resistant chemical barrel material. Background technique [0002] Most of the chemical barrels are made of plastic, generally called plastic chemical barrels and plastic chemical barrels. They are developed and blow-molded using scientific formulas. Fading, non-deformation and other aspects meet the packaging index, which is an ideal choice for long-distance transportation of chemical product packaging materials. [0003] With the development of industrialization, the demand for chemical barrels is getting higher and higher. The requirements for chemical barrels are not limited to basic performance. While ensuring beauty, elegance, and convenience, the most important thing is the safety during packaging, transportation, and use. Often, the barrels store highly irritating and corrosive chemicals, so corrosion resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L67/02C08K9/04C08K9/02C08K3/34
CPCC08K2201/011C08L23/12C08L67/02C08K9/04C08K9/02C08K3/34
Inventor 独少培
Owner 安徽天路新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com