Spraying-free scratch-resistant polypropylene composite material used for car exterior trimming parts and preparation method of composite material

A composite material and polypropylene technology, applied in the field of polymers, can solve the problems of environmental protection, sustainable development, high content of harmful organic volatiles, and affecting the health of operators, so as to improve the molding surface effect and ensure the size , low cost effect

Inactive Publication Date: 2014-09-17
ORINKO NEW MATERIAL CO LTD
View PDF2 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the spraying process requires the use of a large amount of paint, organic solvents, etc., which not only consumes a lot of manpower and material resources; more importantly, the paint has a high content of toxic and harmful organic volatiles, which seriously affects the health of operators and pollutes the air environment. Requirements for environmental protection and sustainable...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The modified PP composite material in this example is composed of the following raw materials in parts by weight:

[0039] PP: 40.1 parts of copolymerized polypropylene

[0040] Homopolypropylene 37 parts

[0041] HDPE 5 parts

[0042] Filler: talcum powder 15 parts

[0043] Antioxidant: Antioxidant 1010 0.2 parts

[0044] Anti-scratch agent: Dow Corning MB50_001 1.0 parts

[0045] Lubricant: PE wax 0.5 parts

[0046] Light stabilizer: 3808PP5 0.2 parts

[0047] Aluminum powder of metallic color powder 1.0 parts

[0048] Concrete preparation method comprises the following steps:

[0049] (1) Take various raw materials respectively by formula ratio;

[0050] (2) Add the measured PP resin, filler, anti-scratch agent, antioxidant, lubricant, light stabilizer and metallic toner into the high-speed mixer and mix at high speed for 2-10 minutes;

[0051] (3) Put the mixed materials into a parallel twin-screw extruder to melt, extrude and granulate to obtain a modi...

Embodiment 2

[0053] The modified PP composite material in this example is composed of the following raw materials in parts by weight:

[0054] PP: 72.8 parts of copolymerized polypropylene

[0055] HDPE 7 parts

[0056] Toughening agent: ethylene-octene copolymer 10 parts

[0057] Filling agent: calcium carbonate 15 parts

[0058] Antioxidant: Antioxidant DSTP 0.2 parts

[0059] Antioxidant 1010 0.2 parts

[0060] Anti-scratch agent: Dow Corning MB50_001 2.0 parts

[0061] Lubricant: PE wax 0.3 parts

[0062] CaSt 0.3 parts

[0063] Light stabilizer: V703 0.3 parts

[0064] Metallic color powder: aluminum powder 1.0 parts

[0065] Copper zinc powder 1.0 parts

[0066] Concrete preparation method comprises the following steps:

[0067] (1) Take various raw materials respectively by formula ratio;

[0068] (2) Add the measured PP resin, toughener, filler, anti-scratch agent, antioxidant, lubricant, light stabilizer and metallic toner together into a high-speed mixer for 2 minutes ...

Embodiment 3

[0073] The modified PP composite material in this example is composed of the following raw materials in parts by weight:

[0074] PP: Homopolypropylene 51.3 parts

[0075] HDPE resin 7 parts

[0076] Toughening agent: ethylene-octene copolymer 10 parts

[0077] Propylene-alpha olefin copolymer 4 parts

[0078] Filler: Whiskers 12 parts

[0079] Barium sulfate 10 parts

[0080] Antioxidant: Antioxidant DSTP 0.4 parts

[0081] Anti-scratch agent: Dow Corning MB50_001 1.0 parts

[0082] BASF SR100 2.0 parts

[0083] Lubricant: EBS 0.5 parts

[0084] Light stabilizer: V68 0.3 parts

[0085] Metal color powder: stainless steel powder 2.5 parts

[0086] Concrete preparation method comprises the following steps:

[0087] (1) Take various raw materials respectively by formula ratio;

[0088] (2) Add the measured PP resin, toughening agent, filler, anti-scratch agent, antioxidant, lubricant, light stabilizer and metallic toner together into a high-speed mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a spraying-free scratch-resistant polypropylene composite material used for car exterior trimming parts and a preparation method of the composite material. The spraying-free scratch-resistant polypropylene composite material is prepared from the following components in parts by weight: 39.6-77.1 parts of polypropylene, 5.0-8.0 parts of high-density polyethylene, 0-15 parts of flexibilizer, 15-25 parts of filler, 0.2-1 part of antioxidant, 1.0-5.0 parts of scratch resistant agent, 0.5-1 part of lubricant, 0.2-0.4 part of light stabilizer, 1.0-5.0 parts of metal toner. According to the spraying-free scratch-resistant polypropylene composite material disclosed by the invention, the metal toner and the scratch resistant agent are adopted, so that the polypropylene composite material has metallic luster effect and scratch resistance, has spraying-free effect and further has scratch resistance at the same time, and therefore, application field of the polypropylene is expanded, and the spraying-free scratch-resistant polypropylene composite material is especially applicable to using on the field of car exterior trimming parts.

Description

technical field [0001] The invention relates to the technical field of polymers, in particular to a non-spraying and scratch-resistant polypropylene composite material for automobile exterior trims and a preparation method thereof. [0002] Background technique [0003] Polypropylene (PP) has become one of the fastest-growing varieties of plastic production due to its simple synthesis method, abundant raw material sources, low price, and good physical and mechanical properties and processing properties. Its output ranks first among the five general-purpose plastics. Three, and has a large number of applications in the automotive field. [0004] Polypropylene (PP) is widely used in the automotive industry due to its excellent heat resistance, good bending fatigue resistance, and low price. However, PP has low impact toughness, poor creep resistance, large molding shrinkage, and poor dimensional stability; polypropylene composite materials are generally not resistant to scra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/14C08L23/06C08K3/08B29B9/06
CPCC08L23/14B29B9/06B29C48/92B29C2948/92514B29C2948/9258B29C2948/92704C08K2201/014C08L23/12C08L2205/025C08L2205/03C08L2205/035C08L2207/062C08L23/06C08K13/02C08K2003/0812C08K3/34C08L23/0815C08K2003/265C08K13/04C08K7/02C08K3/08C08L23/16C08K2003/0893C08L53/025C08K2003/085
Inventor 林经萍张奎贾小彬周素蓉李荣群
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap