High-performance environment-friendly adhesive and preparation method thereof

An adhesive and environment-friendly technology, applied in the direction of adhesives, polymer adhesive additives, ester copolymer adhesives, etc., can solve problems affecting the bonding effect, bubbling, poor stability, etc., and achieve a firm bonding effect Effect

Inactive Publication Date: 2020-01-17
YASUSA CHEM CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In some components, PC materials often require pressure-sensitive tape to fix or fix other materials or devices on the material; because PC materials are not stable in high-temperature and high-humidity environments, they are easy to hydrolyze and release carbon dioxide and water vapor. The tape is pasted on the surface of the PC material, and bubbles are prone to occur under high temperature and high humidity conditions, which will affect the bonding effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: A kind of high-performance environment-friendly adhesive, this adhesive is acrylic adhesive, by mass ratio, is made up of following components: MMA 5 parts, BA 90 parts, AA 4 parts and crosslinking agent 2 parts; Wherein , the acrylate adhesive is an acrylic polymer, which is a polymer mainly composed of monomers containing at least one acrylate group in one molecule, and the weight average molecular weight (a) of the acrylic polymer is 60×10 4 .

[0026] The adhesive also includes a tackifying resin, the softening point of the tackifying resin is higher than 85°C, about 10 to 40 parts by weight relative to 100 parts by weight of the acrylic polymer, the tackifying resin is rosin phenol or terpene phenols; the tackifying resin is Arakawa Trade name "TAMANOL 803L" (terpene phenol resin, softening point about 145° C. to 160° C., hydroxyl value 1 mgKOH / g to 20 mgKOH / g) manufactured by Chemical Industry Co., Ltd.

[0027] The adhesive also includes 200-220 p...

Embodiment 2

[0041] A high-performance environment-friendly adhesive, the adhesive is an acrylic adhesive, which consists of the following components according to the mass ratio: 7 parts of MMA, 88 parts of BA, 3 parts of AA and 2 parts of cross-linking agent; among them, the acrylic The adhesive is an acrylic polymer, which is a polymer formed mainly from a monomer containing at least one acrylate group in one molecule. The weight average molecular weight (a) of the acrylic polymer is 50×10 4 .

[0042] The adhesive also includes a tackifying resin, the softening point of the tackifying resin is higher than 85°C, about 10 to 40 parts by weight relative to 100 parts by weight of the acrylic polymer, the tackifying resin is rosin phenol or terpene phenols; the tackifying resin is Arakawa Trade name "TAMANOL 803L" (terpene phenol resin, softening point about 145° C. to 160° C., hydroxyl value 1 mgKOH / g to 20 mgKOH / g) manufactured by Chemical Industry Co., Ltd.

[0043] The adhesive also inc...

Embodiment 3

[0056] A high-performance environment-friendly adhesive, the adhesive is an acrylic adhesive, which consists of the following components according to the mass ratio: 2 parts of MMA, 92 parts of BA, 6 parts of AA and 2 parts of cross-linking agent; among them, the acrylic The adhesive is an acrylic polymer, which is a polymer formed mainly from a monomer containing at least one acrylate group in one molecule. The weight average molecular weight (a) of the acrylic polymer is 50×10 4 .

[0057] The adhesive also includes a tackifying resin, the softening point of the tackifying resin is higher than 85°C, about 10 to 40 parts by weight relative to 100 parts by weight of the acrylic polymer, the tackifying resin is rosin phenol or terpene phenols; the tackifying resin is Arakawa Trade name "TAMANOL 803L" (terpene phenol resin, softening point about 145° C. to 160° C., hydroxyl value 1 mgKOH / g to 20 mgKOH / g) manufactured by Chemical Industry Co., Ltd.

[0058] The adhesive also inc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-performance environment-friendly adhesive which is an acrylate adhesive and consists of the following components in parts by mass: 1-8 parts of MMA (methl methacrylate), 5-93 parts of BA (butyl acrylate), 2-6 parts of AA (acrylic acid) and 1-5 parts of a crosslinking agent, wherein the acrylate adhesive is an acrylate polymer which is a polymer formed by a monomer with at least one acrylate group in one molecule as a main constitution monomer; and the weight average molecular weight (a) of the acrylate polymer is 30-80*10<4>. According to the high-performance environment-friendly adhesive provided by the invention, stirring is implemented while nitrogen is introduced into the solution of the acrylate polymer. By adopting the mode, oxygen in a polymerizationsystem can be removed, technical defects that carbon dioxide and moisture can be easily released through hydrolysis as a conventional PC material is poor in stability in a high temperature and high humidity environment can be solved, a prepared pressure sensitive adhesive tape is pasted to the surface of a PC material, a bubble phenomenon is barely caused under a high temperature and high humiditycondition, and a solid bonding effect can be maintained for a long time.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a high-performance environment-friendly adhesive and a preparation method thereof. Background technique [0002] Adhesive, also known as adhesive, referred to as glue (bonding agent, adhesive), is a non-metallic medium material that makes an object closely connected with another object. The adhesive only occupies a very thin layer of volume between the two adherend surfaces, but after the adhesive is used to complete the bonding construction, the obtained adhesive joints can meet various requirements of actual needs in terms of mechanical properties and physical and chemical properties. It can effectively bond materials together. [0003] PC is a thermoplastic engineering plastic with excellent comprehensive properties, which has high impact strength, transparency, rigidity, flame resistance, excellent electrical insulation and heat resistance. It has high dimensional stabili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/08C09J11/08C08F220/18C08F220/14C08F220/06C09J7/38
CPCC08F220/18C09J11/08C09J133/12C09J2467/006C09J7/385C09J2301/122C09J2301/302C08L93/04C08L45/00
Inventor 张才香胡其根陶杰王燕
Owner YASUSA CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com