Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A treatment method, rubber wood technology, applied in wood treatment, impregnated wood, wood treatment details, etc., can solve the problems of decay, long cycle, mildew, etc., and achieve the effect of reducing energy consumption
Inactive Publication Date: 2020-02-21
INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, due to the high content of starch, sugar and protein in rubber wood, rubber wood is prone to blue stain, mold, moth and decay.
At present, the modification of rubber wood is mainly drug treatment. Water-soluble chemicals ar
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] (1) Put the wood to be modified in a dipping tank, heat it to 60°C, vacuumize it to -0.1MPa, and keep it for 20-30min.
[0026] (2) When the temperature of the impregnation tank is lowered to about 25°C under vacuum, the impregnation liquid is injected, and the impregnation liquid completely submerges the wood.
[0027] (3) Pressurize to 1.2MPa, keep it for 5-6 hours, and discharge the impregnation solution.
[0028] (4) Open the impregnation tank, take out the wood and put it into the drying kiln, dry it in stages, dry at 60°C until the moisture content is <30%, dry at 70°C until the moisture content is <20%, dry at 80°C until the moisture content is <15%, 100 °C and dry until the moisture content is less than 10%.
Embodiment 2
[0030] (1) Place the wood to be modified in a dipping tank, heat to 80°C, vacuumize to -0.1MPa, and keep for 20-30min.
[0031] (2) When the temperature of the impregnation tank is lowered to about 20°C under vacuum, the impregnation liquid is injected, and the impregnation liquid completely submerges the wood.
[0032] (3) Pressurize to 1.2MPa, keep it for 5-6 hours, and discharge the impregnation solution.
[0033] (4) Open the impregnation tank, take out the wood and put it into the drying kiln, dry it in stages, dry at 60°C until the moisture content is <30%, dry at 70°C until the moisture content is <20%, dry at 80°C until the moisture content is <15%, 100 °C and dry until the moisture content is less than 10%.
Embodiment 3
[0035] (1) Place the wood to be modified in a dipping tank, heat to 120°C, vacuumize to -0.1MPa, and keep for 20-30min.
[0036] (2) When the temperature of the dipping tank is lowered to 25°C in a vacuum state, inject the dipping liquid, and the dipping liquid will completely submerge the wood.
[0037] (3) Pressurize to 1.2MPa, keep it for 5-6 hours, and discharge the impregnation solution.
[0038] (4) Open the impregnation tank, take out the wood and put it into the drying kiln, dry it in stages, dry at 60°C until the moisture content is <30%, dry at 70°C until the moisture content is <20%, dry at 80°C until the moisture content is <15%, 100 °C and dry until the moisture content is less than 10%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Formaldehyde emission
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a treatment method of impregnated rubber wood, which comprises the following steps: putting wood to be modified into an impregnation tank, and vacuumizing at a heating state; cooling to 25 DEG C, injecting an impregnation liquid, pressurizing and maintaining the pressure for 5-6 hours, and discharging the impregnation liquid; and opening the impregnation tank, taking out the wood, putting the wood into a drying kiln, carrying out staged drying treatment, drying at 60 DEG C until the moisture content is less than 30%, drying at 70 DEG C until the moisture content is lessthan 20%, drying at 80 DEG C until the moisture content is less than 15%, and drying at 100 DEG C until the moisture content is less than 10% to obtain the impregnated rubber wood. According to the invention, the rubber wood wet plates can be directly processed; the problems of high energy consumption and high cost due to the fact that dry plates are needed for processing and treatment in conventional rubber wood processing are solved; according to the method, vacuumizing is carried out at heating state, air in the wood can be partially or completely exhausted, then cooling is conducted, theremaining air in the wood is compressed to generate a vacuum state, chemicals enter the wood by means of the pressure difference during pressurization, the impregnation effect is improved, the formaldehyde content of the impregnation liquid is low, and the method is environmentally friendly.
Description
technical field [0001] The invention relates to the technical field of wood processing and production, in particular to a treatment method for impregnated rubber wood and the impregnated rubber wood prepared by the treatment method. Background technique [0002] Rubber trees (Hevea brasiliensis) are widely planted in southern my country and Southeast Asia. The effective rubber production period of rubber trees is about 30 years. More than 10 million cubic meters of rubber wood. Rubberwood is a diffuse-porous wood, easy to process and beautiful in texture. It is currently widely used to make wood products such as furniture, glulam finger-joint boards, toys, etc. It is an important commercial forest plantation material. However, due to the high content of starch, sugar and protein in rubber wood, rubber wood is prone to blue stain, mold, moth and decay. At present, the modification of rubber wood is mainly drug treatment. Water-soluble chemicals are immersed in rubber wood th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): B27K3/08B27K3/10B27K3/52B27K5/04
CPCB27K3/0207B27K3/08B27K3/10B27K3/52B27K5/04
Inventor 柴宇博平立娟孙柏玲刘君良吕文华倪林胡极航王小青
Owner INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY